Polyester multilayer film and its manufacturing method

A multi-layer film, polyester technology, applied in chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems of lower yield, lower production yield, management and production difficulties, etc., to achieve shrinkage Low rate, excellent coating manufacturability, and the effect of reducing slack

Active Publication Date: 2021-08-13
KOLON IND INC
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] When only the central part is used, the edge part needs to be cut and discarded, so the yield of the product is reduced. When the edge parts are laminated and used, since the physical properties of each edge part are different, it is necessary to measure the orientation angle for lamination, etc. Inspection process, so there are difficulties in management and production, and it also reduces production yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester multilayer film and its manufacturing method
  • Polyester multilayer film and its manufacturing method
  • Polyester multilayer film and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0159] The core layer uses polyethylene terephthalate (PET) with an intrinsic viscosity of 0.65dl / g, and the surface layer uses PET with an intrinsic viscosity of 0.64dl / g and 70ppm of silica particles with an average particle size of 2.5μm. Coextrusion is performed separately to coextrude a three-layer film laminated with skin layer / core layer / skin layer, followed by casting on a cooling roll to produce an unstretched sheet. At this time, the core layer accounts for 80% by weight of the total film weight, and the surface layer accounts for 20% by weight of the total film weight. Sequentially stretched 3 times along the machine direction, 3.4 times along the width direction, and heat-treated at 210 ° C, as shown in Table 1, a total of 3.5% relaxation in the four regions, in the first region, The second region, the third region, and the fourth region were given relaxation rate gradients of 1.2%, 1.0%, 0.9%, and 0.8%, respectively, thereby manufacturing a film with a total thick...

Embodiment 2、3

[0162] As shown in Table 1 below, a film was produced in the same manner as in Example 1 except that the relaxation rate in the width direction was changed.

[0163] The physical properties of the produced films were measured and shown in Tables 2 and 3 below.

Embodiment 4、5

[0165] As shown in Table 1 below, a film was produced in the same manner as in Example 1, except that the intrinsic viscosity of the surface layer material and the relaxation rate in the width direction were changed.

[0166] The physical properties of the produced films were measured and shown in Tables 2 and 3 below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
mean roughnessaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The present invention relates to an optical polyester multilayer film with high transparency and excellent surface properties and its manufacturing method. Specifically, it relates to a wide film with a low shrinkage rate and a full width of 5,000 mm or more. A polyester multilayer film and a method for producing the polyester multilayer film having a smaller difference in shrinkage rate between parts, thereby reducing bending phenomenon and baggy phenomenon occurring in subsequent processing steps.

Description

technical field [0001] The present invention relates to an optical polyester multilayer film with high transparency and excellent surface properties and its manufacturing method. Specifically, it relates to a wide film with a low shrinkage rate and a full width of 5,000 mm or more. A polyester multilayer film and a method for producing the same because the difference in the shrinkage rate of the parts is small, thereby improving the bending phenomenon, and reducing the baggy phenomenon that occurs in subsequent processing steps such as prism coating and diffusion coating. Background technique [0002] Optical films are used as optical components for displays, as optical materials for LCD BLUs, or as optical components for surface protection of various displays such as LCDs, PDPs, and touch panels. [0003] In order to make such an optical film suitable for applications such as touch panels or mobile phones, it is important to improve the quality of the film to exhibit approp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B27/36B32B27/20B32B7/023B32B7/028B29C48/00B29C55/12
CPCB32B7/02B32B27/08B32B27/20B32B27/36B29C55/12B29C48/00B29C48/0018
Inventor 曹铉
Owner KOLON IND INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com