Energy absorption and shock absorption PC/ABS alloy and preparation method thereof

A shock absorption, ABS resin technology, applied in the field of polymer material processing, can solve the problem that PC/ABS alloy energy absorption and shock absorption cannot meet the requirements of use, etc., to increase rigidity, improve energy absorption and surface impact performance, improve The effect of energy absorption and shock absorption

Active Publication Date: 2019-05-17
SHANGHAI KUMHO SUNNY PLASTICS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the energy absorption and shock absorption of PC / ABS alloy is still difficult to meet the requirements of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Energy absorption and shock absorption PC/ABS alloy and preparation method thereof
  • Energy absorption and shock absorption PC/ABS alloy and preparation method thereof
  • Energy absorption and shock absorption PC/ABS alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] This embodiment provides an energy-absorbing and shock-absorbing PC / ABS alloy and a preparation method thereof, the method comprising the following steps:

[0053] (1) Weigh each component by weight: PC: 50, ABS: 30, toughening agent: 15; antioxidant 0.1, lubricant 0.2, IPN resin 3.

[0054] (2) Feed the raw materials ABS resin, PC resin, toughener, antioxidant and lubricant from the feeding port, feed the IPN resin into the seventh zone, and melt and extrude it at 200-280°C. The rotating speed of the extruder is 400rpm, the pressure is 2MPa, and the product is obtained through melt extrusion and granulation.

[0055] (3) The screw diameter of the extruder is 40 mm, and the aspect ratio is 42.

Embodiment 2

[0057] This embodiment provides an energy-absorbing and shock-absorbing PC / ABS alloy and a preparation method thereof, the method comprising the following steps:

[0058] (1) Weigh each component by weight: PC: 60, ABS: 40, toughening agent: 5; antioxidant 0.2, lubricant 0.3, IPN resin 10.

[0059] (2) Feed the raw materials ABS resin, PC resin, toughener, antioxidant and lubricant from the feeding port, feed the IPN resin into the seventh zone, and melt and extrude it at 200-280°C. The rotating speed of the extruder is 400rpm, the pressure is 2MPa, and the product is obtained through melt extrusion and granulation.

[0060] (3) The screw diameter of the extruder is 40 mm, and the aspect ratio is 42.

Embodiment 3

[0062] This embodiment provides an energy-absorbing and shock-absorbing PC / ABS alloy and a preparation method thereof, the method comprising the following steps:

[0063] (1) Weigh each component by weight: PC: 70, ABS: 50, toughening agent: 3; antioxidant 1, lubricant 2, IPN resin 20.

[0064] (2) Feed the raw materials ABS resin, PC resin, toughener, antioxidant and lubricant from the feeding port, feed the IPN resin into the seventh zone, and melt and extrude it at 200-280°C. The rotating speed of the extruder is 400rpm, the pressure is 2MPa, and the product is obtained through melt extrusion and granulation.

[0065] (3) The screw diameter of the extruder is 40 mm, and the aspect ratio is 42.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention provides an energy absorption and shock absorption PC / ABS alloy and a preparation method thereof. The energy absorption and shock absorption PC / ABS alloy is prepared from the following components in parts by weight: 30-50 parts of ABS, 50-70 parts of PC, 3-20 parts of IPN resin, 3-15 parts of a toughening agent, 0.1-1 part of an antioxidant and 0.2-2 parts of a lubricant. The preparation method of the energy absorption and shock absorption PC / ABS alloy comprises the following steps that (a) ABS resin, PC resin, the toughening agent, the antioxidant and the lubricant are added into a high-speed mixer for mixing; (b) the mixture obtained in the step (a) is mainly fed through a double-screw extruder, IPN components are subjected to side-feeding on a seventh zone, blending is carried out, and melting, extruding and granulating are carried out to obtain the energy absorption and shock absorption PC / ABS alloy. Compared with the prior art, the energy absorption and shock absorption PC / ABS alloy is well dispersed in the PC / ABS alloy and is mostly in a PC phase by adding a micro IPN interpenetrating network structure into the alloy through side feeding, so that the rigidity ofthe material is increased without reducing the toughness, and the energy absorption and shock absorption of the alloy are improved.

Description

technical field [0001] The invention relates to the field of polymer material processing, in particular to an energy-absorbing and shock-absorbing PC / ABS alloy and a preparation method thereof. Background technique [0002] Polycarbonate has high toughness, ABS resin can improve processing performance, PC / ABS alloy is a general-purpose alloy, but it is difficult to effectively absorb energy in some safety seats, bumpers, helmets and other scenes that require safety performance, and it is difficult to improve product safety. performance. [0003] Usually super-tough materials deform and absorb some of the energy, but do not provide protection. The high rigidity material can support the protection but cannot block the impact force. In addition, the reinforced PC / ABS alloy will be damaged when it receives external impact, and its toughness will drop sharply. [0004] Disclosed a kind of high-performance PC / ABS alloy material as CN 108219429A, its raw material formula by weig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L33/12C08L9/06C08L51/04
Inventor 王璐李强辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap