Partition board and preparation method thereof

A technology for partition board and titanium tailings extraction, applied in the field of building materials, can solve the problems of pollution, the land occupation of titanium tailings and the like

Inactive Publication Date: 2019-05-14
攀钢冶金材料有限责任公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the purpose of the present invention is to prepare a partition wall board by using the tailings of titanium extraction, which solves the problems of land occupation and environmental pollution of the tailings of titanium extraction, and has better economic and social benefits

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Partition board and preparation method thereof
  • Partition board and preparation method thereof
  • Partition board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] The mass ratio of raw materials for preparing lightweight partition wall panels in Example 1 of the present invention is: 25wt% of titanium tailings, 47wt% of lightly burned magnesium oxide, 24wt% of industrial magnesium sulfate, 3wt% of fly ash, and 0.4wt% of straw fiber , compound admixture 0.5wt%, foaming agent 0.1wt%; The composition of compound admixture is: 25wt% iron alum, 15wt% sugar calcium, 15wt% calcium chloride, 20wt% silica fume, 5wt% % water reducer, 20wt% sucrose. The preparation method of the compound admixture is as follows: mixing iron alum, sugar calcium, calcium chloride, silica fume, water reducing agent and sucrose according to the above-mentioned mass content ratio.

[0083] The preparation method comprises the following steps:

[0084] 1) Industrial magnesium sulfate was dissolved in water 20 hours in advance, configured into an aqueous magnesium sulfate solution with a Baume degree of 25 ° Be, and the precipitate was filtered to obtain a clear ...

Embodiment 2

[0094] According to the method of Example 1, the light-weight partition board is prepared. The difference from Example 1 is that the mass ratio of the raw materials of the light-weight partition board is: 33wt% of titanium tailings, 41wt% of light-burned magnesium oxide, industrial Magnesium sulfate 20wt%, fly ash 4wt%, straw fiber 0.63wt%, compound admixture 1.3wt%, blowing agent 0.07wt%; The composition of compound admixture is: 15wt% iron alum, 20wt% sugar Calcium, 5wt% calcium chloride, 20wt% silica fume, 15wt% water reducer, 25wt% sucrose. The preparation method of the compound admixture is as follows: mixing iron alum, sugar calcium, calcium chloride, silica fume, water reducing agent and sucrose according to the above-mentioned mass content ratio.

[0095] According to the method of Example 1, the performance of the lightweight partition wall panel prepared in Example 2 of the present invention was tested, and the test results are shown in Table 2.

[0096] Table 2 Per...

Embodiment 3

[0099] According to the method of Example 1, the light-weight partition board is prepared. The difference from Example 1 is that the mass ratio of the raw materials of the light-weight partition board is: 33wt% of titanium tailings, 41wt% of light-burned magnesium oxide, industrial Magnesium sulfate 20wt%, fly ash 3.5wt%, straw fiber 0.93wt%, compound admixture 1.5wt%, blowing agent 0.07wt%; Sugar calcium, 15wt% calcium chloride, 15wt% silica fume, 10wt% water reducer, 20wt% sucrose. The preparation method of the compound admixture is as follows: mixing iron alum, sugar calcium, calcium chloride, silica fume, water reducing agent and sucrose according to the above-mentioned mass content ratio.

[0100] According to the method of Example 1, the performance of the lightweight partition wall panel prepared in Example 3 of the present invention was tested, and the test results are shown in Table 3.

[0101] Table 3 The performance of the lightweight partition wall board prepared ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a partition board. The partition board comprises 25 to 40 wt% of extraction titanium tailings, 38 to 47 wt% of magnesium oxide, 18 to 24 wt% of magnesium sulfate, 0 to 4 wt% ofcoal ash, 0.4 to 1 wt% of straw fiber, 0.5 to 2 wt% of an additive, and 0.05 to 0.1 wt% of a foaming agent. The partition board is light, high-strength, fireproof and heat-insulating, and has the advantages that chloride ion in the extraction titanium tailings reacts with light calcined magnesia to produce stable cement strength phase (518 phase), and the content of water soluble chloride ion in the extraction titanium tailings is reduced, so that changing waste material into things of value is realized, the problems of land occupation and environmental pollution of the extraction titanium tailings are solved, and the partition board has good economic benefit and social benefit. The invention further provides a preparation method of the partition board.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a partition board and a preparation method thereof. Background technique [0002] In recent years, the country has proposed relevant policies for the construction market to encourage the development of prefabricated sustainable buildings. With the continuous improvement of relevant policy standards, my country's construction industry is transforming towards the modernization of green buildings and the construction industry, making lightweight partition panels The application prospect is more and more extensive. [0003] The blast furnace slag of Panzhihua Iron and Steel Co., Ltd. extracts TiO, a useful component in the slag, through high-temperature carbonization and low-temperature chlorination. 2 After that, a large amount of tailings are produced. This solid waste contains chloride ions and residual carbon, so it cannot be directly used as a concrete admixture. At p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/30C04B38/10C04B111/40C04B111/28
Inventor 李国栋童武兵万红伶丁见鹏杨强孙晓婷段大福王怀斌李冬梅杨浩李娇李师程林江华
Owner 攀钢冶金材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com