High-toughness PE pipeline material

A high-toughness, pipeline technology, applied in the field of PE pipeline material preparation

Inactive Publication Date: 2019-05-03
湖北恒标塑胶股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-toughness PE pipe material to solve the problems that the performance of the current PE pipe material needs to be further improved in terms of flexibility, impact resistance, weather resistance, and aging resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of high-toughness PE pipe material of the present embodiment is made up of following raw materials in parts by weight:

[0026] PE 60 PVC 12

[0027] Polysulfide 45 Polybutylacrylate 45

[0028] TPV 25 Silane coupling agent 12

[0029] Ethyl phosphite 1.5 Cardanol 12

[0030] Hydroxy silicone oil 8 Epoxy resin 12

[0031] POM 18 Melamine 12

[0032] Stabilizer 2 Lubricant 25

[0033] Turpentine 0.5 Toner 1;

[0034] During preparation, first add PE, cardanol, ethyl phosphite and PVC into a mixer, mix and react at 160-180 degrees Celsius for 15-20 minutes, extrude and granulate to obtain modified PE; then polysulfide rubber, silane Coupling agent, hydroxy silicone oil, add to the mixer, mix and react at 160-180 degrees Celsius for 15-20 minutes, extrude and granulate to obtain modified polysulfide rubber; then polybutylacrylate, melamine, epoxy resin, silane Add the coupling agent into the mixer and mix and react at 160-180 degrees Celsius for 20-25 minutes...

Embodiment 2

[0036] A kind of high-toughness PE pipe material of the present embodiment is made up of following raw materials in parts by weight:

[0037] PE 50 PVC 15

[0038] Polysulfide 40 Polybutylacrylate 50

[0039] TPV 20 Silane coupling agent 15

[0040] Ethyl phosphite 1 Cardanol 8

[0041] Hydroxy silicone oil 5 Epoxy resin 10

[0042] POM 15 Melamine 10

[0043] Stabilizer 1 Lubricant 20

[0044] Turpentine 0.1 Toner 0.1;

[0045] The preparation method is the same as in Example 1.

Embodiment 3

[0047] A kind of high-toughness PE pipe material of the present embodiment is made up of following raw materials in parts by weight:

[0048] PE 70 PVC 8

[0049] Polysulfide 40 Polybutylacrylate 50

[0050] TPV 30 Silane coupling agent 15

[0051] Ethyl phosphite 2 Cardanol 15

[0052] Hydroxy silicone oil 10 Epoxy resin 15

[0053] POM 20 Melamine 15

[0054] Stabilizer 3 Lubricant 30

[0055] Turpentine 1 Toner 2;

[0056] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of preparation of a PE pipeline material and provides a high-toughness PE pipeline material which is composed of, by weight, 50-70 parts of PE, 8-15 partsof PVC, 40-50 parts of polysulfide rubber, 40-50 parts of polybutyl acrylate, 20-30 parts of TPV, 8-15 parts of a silane coupling agent, 1-2 parts of ethyl phosphite, 8-15 parts of cardanol, 5-10 parts of hydroxy silicone oil, 10-15 parts of epoxy resin, 15-20 parts of polyoxymethylene, 10-15 parts of melamine, 1-3 parts of a stabilizer, 20-30 parts of lubricating oil, 0.1-1 part of turpentine, and 0.1-2 parts of toner. The PE pipeline material is prepared by modifying the PE, the polysulfide rubber and the polybutyl acrylate and then feeding the components into a mixing mill, then adding other raw materials, including the TPV and the modifier, and mixing all the materials. The PE pipeline material has excellent flexibility, impact strength, oxidization resistance, weather resistance and wearing resistance. The material is suitable for various pipelines.

Description

technical field [0001] The invention belongs to the technical field of PE pipe material preparation, in particular to a high-toughness PE pipe material. Background technique [0002] At present, the common pipe materials on the market are made of PE materials, such as building water supply, drainage, urban water supply, drainage, building heating, gas transmission, electrical and telecommunications protection casings, agricultural irrigation, industrial water delivery, etc. PE pipes. However, the general PE material needs to be further improved in terms of flexibility, impact resistance, weather resistance, aging resistance, etc., so as to be more suitable for pipeline materials in various occasions. Contents of the invention [0003] The purpose of the present invention is to provide a high-toughness PE pipe material to solve the problems that the performance of the current PE pipe material needs to be further improved in terms of flexibility, impact resistance, weather ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L33/08C08L27/06C08L81/04C08K13/02C08K5/00C08K5/3492C08K5/524C08K5/13
Inventor 徐逢来
Owner 湖北恒标塑胶股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com