Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Recyclable PC-ABS plastic building template

A PC-ABS, ABS plastic technology, applied in the field of building formwork, can solve the problems of poor mechanical properties, inability to reuse, damage to building formwork, etc., achieve high bending strength, improve utilization rate, and avoid aging effects

Inactive Publication Date: 2019-04-26
上海凯雄新材料科技有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the mechanical properties of this invention are relatively poor, and it is easy to be damaged when used as a building formwork, so it cannot be reused.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recyclable PC-ABS plastic building template
  • Recyclable PC-ABS plastic building template
  • Recyclable PC-ABS plastic building template

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] The preparation method of carbon black modified ABS plastic comprises the steps:

[0055] (1) Preheat 45 parts of acrylonitrile, 56 parts of butadiene and 25 parts of styrene at a temperature of 70 for 2.5 hours;

[0056] (2) Mix 45 parts of acrylonitrile, 56 parts of butadiene, 36 parts of styrene, 25 parts of carbon black, and 16 parts of ethylene acrylic acid in step (1) and add them into an injection molding machine with an injection temperature of 210°C for injection molding , and then kneaded and granulated by a twin-screw extruder.

[0057] The preparation method of carbon black-benzophenone comprises the steps:

[0058] (1) 8 parts of benzophenone are dissolved in 14 parts of dehydrated alcohol to obtain benzophenone-dehydrated ethanol solution;

[0059] (2) 10 parts of carbon black were ultrasonically obtained in 20 parts of absolute ethanol for 50 min to obtain a carbon black-dehydrated alcohol dispersion;

[0060] (3) Mix the benzophenone-dehydrated ethano...

Embodiment 2

[0074] The preparation method of carbon black modified ABS plastic comprises the steps:

[0075] (1) Preheat 40 parts of acrylonitrile, 51 parts of butadiene and 31 parts of styrene at a temperature of 80° C. for 2 hours;

[0076] (2) Mix 40 parts of acrylonitrile, 51 parts of butadiene, 31 parts of styrene, 20 parts of carbon black, and 14 parts of ethylene acrylic acid in step (1) and add them into an injection molding machine with an injection temperature of 210°C for injection molding , and then kneaded and granulated by a twin-screw extruder.

[0077] The preparation method of carbon black-benzophenone comprises the steps:

[0078] (1) 6 parts of benzophenone are dissolved in 12 parts of dehydrated alcohol to obtain benzophenone-dehydrated ethanol solution;

[0079] (2) 8 parts of carbon black were ultrasonically obtained in 18 parts of absolute ethanol for 45 min to obtain a carbon black-dehydrated alcohol dispersion;

[0080] (3) Mix the benzophenone-dehydrated ethan...

Embodiment 3

[0094] The preparation method of carbon black modified ABS plastic comprises the steps:

[0095] (1) Preheat 38 parts of acrylonitrile, 50 parts of butadiene and 30 parts of styrene at a temperature of 70 for 1 hour;

[0096] (2) Mix 38 parts of acrylonitrile, 50 parts of butadiene, 30 parts of styrene, 18 parts of carbon black, and 13 parts of ethylene acrylic acid in step (1) and add them into an injection molding machine with an injection temperature of 200°C for injection molding , and then kneaded and granulated by a twin-screw extruder.

[0097] The preparation method of carbon black-benzophenone comprises the steps:

[0098] (1) 5 parts of benzophenone are dissolved in 13 parts of dehydrated alcohol to obtain benzophenone-dehydrated ethanol solution;

[0099] (2) 7 parts of carbon black were ultrasonically obtained in 18 parts of absolute ethanol for 40 min to obtain a carbon black-dehydrated alcohol dispersion;

[0100] (3) Mix the benzophenone-dehydrated ethanol so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a recyclable PC-ABS plastic building template, relates to the field of building templates and aims to solve the problem of poor reusability of existing building templates. Thebuilding template is technically characterized by being prepared from the following raw materials in parts by weight: 50-65 parts of polycarbonate, 45-70 parts of carbon black modified ABS plastic, 15-26 parts of alkali-free glass fiber, 8-15 parts of polydimethylsiloxane-maleic anhydride, 10-15 parts of carbon black-benzophenone, 10-16 parts of polyacrylamide-acetic acid and 10-18 parts of triphenyl phosphate. The template is reusable.

Description

technical field [0001] The invention relates to the field of building formwork, more specifically, it relates to a recyclable PC-ABS plastic building formwork. Background technique [0002] The building formwork is a temporary support structure, which is manufactured according to the design requirements, so that the concrete structure and components are formed according to the specified position and geometric size to maintain their correct positions, and bear the self-weight of the building formwork and the external load acting on it. Cast-in-place The building formwork structure used in the construction of concrete structures is mainly composed of three parts: panels, supporting structures and connectors. The panels are bearing slabs that directly contact the newly poured concrete; the supporting structures are temporary structures that support the panels, concrete and construction loads. Ensure that the building formwork structure is firmly combined without deformation or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L51/08C08L33/26C08K13/04C08K7/14C08K3/04C08K5/07C08K5/523
CPCC08L55/02C08L69/00C08L2201/08C08L2205/035C08L51/08C08L33/26C08K13/04C08K7/14C08K3/04C08K5/07C08K5/523
Inventor 王宏涛
Owner 上海凯雄新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com