High-purity molybdenum rhenium lanthanum ternary alloy guide rod and production process thereof

A ternary alloy and production process technology, applied in the field of alloy materials, can solve the problems of a wide range of strength, many cracks, low qualification rate, etc., and achieve the effects of small strength range, strict addition amount, and control of production costs.

Active Publication Date: 2019-03-26
江苏东浦钨钼制品有限责任公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the magnetron guide rods used in microwave ovens have the problems of many cracks, wide range of strength, short life, and low pass rate, so they need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-purity molybdenum rhenium lanthanum ternary alloy guide rod and production process thereof
  • High-purity molybdenum rhenium lanthanum ternary alloy guide rod and production process thereof
  • High-purity molybdenum rhenium lanthanum ternary alloy guide rod and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] Embodiment: The composition of the alloy material is less, and the change in content is small. The present invention is only described in detail through this example. It has been verified that the influence of composition change and temperature change on the performance of the guide rod can be ignored compared with the existing guide rod.

[0024] A high-purity molybdenum-rhenium-lanthanum ternary alloy guide rod. The alloy material for preparing the guide rod includes the following components in parts by weight: 1-2 parts of rhenium, 1-2 parts of lanthanum, and 90-100 parts of molybdenum.

[0025] The production process of the high-purity molybdenum-rhenium-lanthanum ternary alloy guide rod comprises the following steps:

[0026] (1) Preparation of molybdenum powder: Roast ammonium molybdate as a molybdenum source to obtain molybdenum trioxide, then perform a reduction reaction to reduce molybdenum trioxide to molybdenum dioxide, and then perform a second reduction reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-purity molybdenum rhenium lanthanum ternary alloy guide rod, and belongs to the field of an alloy material. The alloy material for preparing the guide rod comprises, byweight part, 1 to 2 parts of rhenium, 1 to 2 parts of lanthanum, and 90 to 100 parts of molybdenum. The purity of the molybdenum is higher than 99.99%. The molybdenum rhenium lanthanum alloy is subjected to ternary alloying, the material comprises , 1 to 2 parts of rhenium, 1 to 2 parts of lanthanum and the balance molybdenum, the alloy property is greatly improved, meanwhile, the adding amount ofheavy metal rhenium and rare earth lanthanum can be strictly controlled, the production cost of the alloy is reasonably controlled, the number of eddy current inspection crack points of the microwavefurnace magnetic control guide rod made of the alloy is greatly smaller than that of the similar product, the strength range is smaller than that of the similar product, the service life is prolonged, and the product yield is improved.

Description

technical field [0001] The invention relates to the field of alloy materials, in particular to a production process applied to a guide rod required by a microwave oven magnetron coil. Background technique [0002] Molybdenum-rhenium-lanthanum alloy can improve the plasticity of molybdenum, increase the strength of molybdenum and improve the high temperature creep performance. Generally, molybdenum-rhenium alloys are divided into low-rhenium (2%-5%) molybdenum alloys and high-rhenium (11%-50%) molybdenum alloys according to the rhenium content. CN106756157A discloses a method for preparing a molybdenum-rhenium-lanthanum alloy material, and in the molybdenum-rhenium-lanthanum alloy material, it is mentioned that rhenium is 1.0%-5.0%, lanthanum is 0.02%-2%, and the balance is molybdenum , the rhenium content also belongs to the low rhenium range. Low-rhenium-molybdenum alloys are considered to have little advantage in strengthening the molybdenum matrix. [0003] At present,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C27/04C22C1/04B21C37/04
Inventor 吴勇本郑远勋李一昕钱梅芳
Owner 江苏东浦钨钼制品有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com