Triblock polypropylene toughened and modified compatilizer as well as preparation method and application thereof

A toughening modification, polypropylene technology, applied in the field of new compatibilizers, can solve problems such as poor compatibility, and achieve the effect of improving performance and compatibility

Active Publication Date: 2019-01-25
CHNA ENERGY INVESTMENT CORP LTD +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition to EPDM rubber, materials such as SBS, SEBS, SIS, and EVA are also good tougheners for polypropylene resins. However, there are few reports on related dynamic vulcanized elastomers. The molecular compatibility of propylene is poor. CN1247682C reports a method for preparing elastomers by dynamic vulcanization of SIS, SBS or SEPS and PP. In this method, if the compatibility of elastomer molecules and polypropylene molecules is considered, adding Sexual additives will further improve material properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Triblock polypropylene toughened and modified compatilizer as well as preparation method and application thereof
  • Triblock polypropylene toughened and modified compatilizer as well as preparation method and application thereof
  • Triblock polypropylene toughened and modified compatilizer as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] (1) Preparation of maleic anhydride grafted polypropylene

[0065] 1000g of polypropylene 1102K, 29g of maleic anhydride, and 5g of dicumyl peroxide are added to a high-speed mixer and mixed evenly, then blended with a ZSK twin-screw extruder to melt and carry out grafting reaction, each section of the extruder The temperature is 175°C, 180°C, 185°C, 185°C, and 180°C in sequence; the product of the grafting reaction is dissolved in hot xylene, and methanol is added to the reaction product after cooling, and crude maleic anhydride grafted Then, the crude maleic anhydride grafted polypropylene was rinsed with ethanol and dried to obtain purified maleic anhydride grafted polypropylene; the grafting rate was 1.7% after testing.

[0066] (2) Preparation of maleic anhydride grafted SBS

[0067] Add 1000g of naphthenic oil KN4010 and 1000g of SBS elastomer into a beaker, stir evenly at room temperature, and let it stand for 24 hours to obtain oil-filled SBS elastomer;

[006...

Embodiment 2

[0072] (1) Preparation of maleic anhydride grafted polypropylene

[0073] 1000g of polypropylene 1102K, 39g of maleic anhydride and 4g of dicumyl hydroperoxide were added to a high-speed mixer and mixed uniformly, then blended with a ZSK twin-screw extruder for melting and grafting reaction, each extruder The temperature of the section is 175°C, 180°C, 185°C, 185°C, and 180°C in sequence; the product of the grafting reaction is dissolved in hot xylene, and methanol is added to the reaction product after cooling, and crude maleate is obtained after filtration. The acid anhydride grafted polypropylene was washed with ethanol and dried to obtain the purified maleic anhydride grafted polypropylene; the grafting rate was 2.2% after testing.

[0074] (2) Preparation of maleic anhydride grafted SBS

[0075] Add 900g of naphthenic oil KN4010 and 1100g of SBS elastomer into a beaker, stir evenly at room temperature, and let it stand for 18 hours to obtain oil-filled SBS elastomer;

...

Embodiment 3

[0080] (1) Preparation of maleic anhydride grafted polypropylene

[0081] Add 1100N 1000g of polypropylene, 29g of maleic anhydride, and 3g of dicumyl peroxide into a high-speed mixer and mix evenly, then blend with a ZSK twin-screw extruder for melting and grafting reaction, each section of the extruder The temperature is 175°C, 180°C, 185°C, 185°C, 180°C in sequence; the product of the grafting reaction is dissolved in hot xylene, after cooling, methanol is added to the reaction product, and crude maleic anhydride is obtained after filtration After grafting polypropylene, the crude maleic anhydride grafted polypropylene was rinsed with ethanol and dried to obtain purified maleic anhydride grafted polypropylene; the grafting rate was 2.3% after testing.

[0082] (2) Preparation of maleic anhydride grafted SEBS

[0083] Take white oil 10#1100g, add 900g of SEBS elastomer into the beaker, stir evenly at room temperature, let it stand for 30h, and obtain oil-filled SEBS elastom...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a triblock polypropylene toughened and modified compatilizer. The compatilizer is obtained by carrying out esterification reaction on the following raw materials in percentageby weight: 47.5-49.75% of carboxylic acid anhydride grafted polypropylene, 47.5-49.75% of carboxylic acid anhydride grafted and toughened elastomer and 0.5-5% of diamine derivative in a solvent, wherein the diamine derivative is an ethylenediamine or ethylenediamine derivative. The invention further discloses a preparation method and application of the riblock polypropylene toughened and modifiedcompatilizer. The toughened and modified compatilizer has the advantages that the compatibility between polypropylene resin and the corresponding elastomer is improved, and the performance of a polypropylene toughened elastomer material is improved.

Description

technical field [0001] The invention belongs to the technical field of toughened and modified compatibilizers, in particular to a novel compatibilizer for preparing polypropylene toughened and modified composite materials. Background technique [0002] Polypropylene resin has the advantages of good mechanical properties, low density, non-toxicity, corrosion resistance and easy processing and molding, and is widely used in building materials, home appliances, automobiles, pipes, daily necessities and other fields. However, in some fields that require special requirements, such as high toughness, high rigidity, electrical conductivity, etc., the performance of general-purpose polypropylene resin is difficult to meet the requirements, and the polypropylene resin needs to be modified accordingly. In the field of high-toughness products, such as automobile bumpers, it is necessary to add toughening agents to the extrusion of polypropylene base materials to improve toughness. In t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/02C08L23/12C08L87/00C08K5/14C08G81/02
CPCC08G81/021C08L53/02C08L53/025C08L23/12C08L87/005C08K5/14
Inventor 方伟罗春桃孟永智田广华申宏鹏赵春梅
Owner CHNA ENERGY INVESTMENT CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap