Co-Ni bimetallic selenide/graphene composite electrode material
An electrode material and graphene technology, which is applied in the manufacture of hybrid capacitor electrodes and hybrid/electric double-layer capacitors, etc., can solve the problems of poor cycle stability, low specific capacitance, and low specific capacity, and improve the performance of supercapacitors. The effect of high specific capacitance and improved conductivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0025] A kind of preparation method of cobalt-nickel double metal selenide / graphene composite electrode material, concrete steps are:
[0026] (1) Weigh 10 mg of graphene oxide (GO, self-made) and add it to 50 mL of ethylene glycol, and disperse ultrasonically for 30 minutes to make GO uniformly dispersed in ethylene glycol;
[0027] (2) Weigh 0.3 g of polyvinylpyrrolidone (PVP), 125 mg of cobalt acetate tetrahydrate (Co(CH 3 COO) 2 4H 2 O) and 124 mg of nickel acetate tetrahydrate (Ni(CH 3 COO) 2 4H 2 O) Add it to the solution in step (1), dissolve it fully by ultrasonication, then transfer the above mixed solution to a round bottom flask and place it on an oil bath at 150°C for 5 hours in an oil bath. Finally, after it was naturally cooled to room temperature, it was centrifuged and washed 4 times with absolute ethanol, and the washed product was dried in an electric blast drying oven;
[0028] (3) Weigh 15 mg of the centrifuged-dried product in step (2), 100 mg of sod...
Embodiment 2
[0030] A kind of preparation method of cobalt-nickel double metal selenide / graphene composite electrode material, concrete steps are:
[0031] (1) Weigh 5 mg of graphene oxide (GO, self-made) and add it to 30 mL of ethylene glycol, and ultrasonically disperse for 30 minutes to make GO uniformly dispersed in ethylene glycol;
[0032] (2) Weigh 0.5 g of polyvinylpyrrolidone (PVP), 250 mg of cobalt acetate tetrahydrate (Co(CH 3 COO) 2 4H 2 O) and 250 mg of nickel acetate tetrahydrate (Ni(CH 3 COO) 2 4H 2 O) Add it to the solution in step (1), dissolve it fully by ultrasonication, then transfer the above mixture to a round bottom flask and place it on an oil bath at 250°C for 1 hour in an oil bath. Finally, after it was naturally cooled to room temperature, it was centrifuged and washed 5 times with absolute ethanol, and the washed product was placed in an electric blast drying oven to dry;
[0033] (3) Weigh 30 mg of the centrifuged-dried product in step (2), 250 mg of sodi...
Embodiment 3
[0035] A kind of preparation method of cobalt-nickel double metal selenide / graphene composite electrode material, concrete steps are:
[0036] (1) Weigh 20 mg of graphene oxide (GO, self-made) and add it to 100 mL of ethylene glycol, and ultrasonically disperse for 30 minutes to make GO uniformly dispersed in ethylene glycol;
[0037] (2) Weigh 0.1 g of polyvinylpyrrolidone (PVP), 60 mg of cobalt acetate tetrahydrate (Co(CH 3 COO) 2 4H 2 O) and 70 mg of nickel acetate tetrahydrate (Ni(CH 3 COO) 2 4H2 O) Add it to the solution in step (1), dissolve it fully by ultrasonication, then transfer the above mixture to a round bottom flask and place it on an oil bath at 200°C for 1 hour in an oil bath. Finally, after it was naturally cooled to room temperature, it was centrifuged and washed 5 times with absolute ethanol, and the washed product was placed in an electric blast drying oven to dry;
[0038] (3) Weigh 50 mg of the centrifuged-dried product in step (2), 300 mg of sodium...
PUM
Property | Measurement | Unit |
---|---|---|
Specific capacitance | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com