Wood composite fiber and preparation method thereof

A composite fiber and wood technology, applied in the direction of fiber raw materials, fiber raw material processing, textiles and papermaking, etc., can solve the problems of unfriendly preparation process environment and single raw materials, and achieve the effect of environmental protection process, simple organizational structure and less ash content

Active Publication Date: 2019-01-15
CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the above patents, the raw materials are single, and the preparation process is not friendly to the environment!

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A wood composite fiber, the wood composite fiber is made of five components, the weight percentage of each component is: Pennisetum fiber 40%, cotton stem fiber 30%, waste paper fiber of grass pulp paper copy paper 20%, slash pine liquefied wood 5%, nano-silica dispersion 5%.

[0032] Wherein, the slash pine liquefied wood is obtained by vacuum-drying some slash pine sawdust, crushing, sieving, mixing with a wood liquefying agent, and then performing microwave liquefaction to obtain coniferous liquefied wood.

[0033] The nano-silicon dioxide dispersion liquid is a transparent liquid with a pH value of 6.1, a nano-silicon dioxide content of 20%, and a particle size of the nano-silicon dioxide of 10.

[0034] The preparation method of above-mentioned wood composite fiber, comprises the following steps:

[0035] Step 1: Preparation of Pennisetum fiber: Collect some Pennisetum fibers in the wilderness, dry them in the sun, remove impurities, chop them, soak them in 5% NaO...

Embodiment 2

[0043] A wood composite fiber, the wood composite fiber is made of five components, the weight percentage of each component is: Pennisetum fiber 50%, cotton stem fiber 20%, wood pulp paper copy paper waste paper fiber 16% %, gray cedar liquefied wood 10%, nano-silica dispersion 4%.

[0044] Preferably, the liquefied wood of Chinese fir is obtained by taking some sawdust of Chinese fir, crushing and sieving after vacuum drying, mixing with a wood liquefaction agent, and then performing microwave liquefaction to obtain coniferous liquefied wood.

[0045] Preferably, the nano-silicon dioxide dispersion liquid is a transparent liquid with a pH value of 9, a nano-silicon dioxide content of 30%, and a particle size of the nano-silicon dioxide of 20 nm.

[0046] The preparation method of described a kind of wood composite fiber, comprises the following steps:

[0047] Step 1: Preparation of Pennisetum fiber: Collect some Pennisetum fibers in the wilderness, dry them in the sun, remo...

Embodiment 3

[0055] The difference from Example 1 is that the percentage by weight of each component is: Pennisetum fiber 45%, cotton stem fiber 20%, wood pulp paper copy paper waste paper fiber 20%, conifer liquefied wood 10%, nanometer dioxide Silicon dispersion 5%.

[0056] Wherein, the coniferous tree is pinus slash pine or gray fir, and the liquefied wood of coniferous trees is, take some pinus slash pine or gray fir sawdust, after vacuum drying, crush and sieve, mix with wood liquefaction agent and then carry out microwave liquefaction , the obtained conifer liquefied wood.

[0057] Its preparation method refers to Example 1-2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wood composite fiber and a preparation method thereof. The preparation method is prepared from raw materials including 40-50% of Chinese pennisetum fibers, 20-30% of cotton stalk fibers, 10-20% of waste paper of offices, 5-10% of conifer liquefied timber and 4-5% of a nanometer silica dispersion liquid by weight. The preparation method of the wood composite fiber includessteps of preparation of the raw materials and packaging. The wood composite fiber includes little ash, is high in heat resistance and oil absorbency, low in cost, and ideal for roads or preparation of high-intensity boards, and technology of the wood composite fiber is environment-friendly.

Description

technical field [0001] The invention belongs to the field of new materials, and in particular relates to a wood composite fiber and a preparation method thereof. Background technique [0002] From the adoption of the "Framework Convention on Climate Change" at the 1st United Nations Conference on Environment and Development in Rio de Janeiro, Brazil in 1992, to the adoption of the "Paris Agreement" at the 21st Global Climate Conference in Paris, France, in 2015 to make arrangements for global action on climate change after 2020, and then By 2016, China and the United States ratified the Paris Agreement at the G20 Summit in Hangzhou, China. While "building an innovative, dynamic, interconnected, and inclusive world economy", it left endless thinking and heavy burdens for resource, environment, and material science and technology workers. On the one hand, the development and plunder of forests, oil and mineral resources by human beings has reached the point of madness; And se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21B1/02D21B1/04D21B1/06D21B1/08
CPCD21B1/021D21B1/04D21B1/06D21B1/08Y02W30/64
Inventor 吴庆定李佩袁建刘俊怀刘克非何玉琴
Owner CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap