Phosphate laser neodymium glass

A phosphate and neodymium glass technology, applied in the field of laser neodymium glass, can solve problems such as difficulty in meeting the requirements of high-power laser devices, and achieve the effects of small photoelastic coefficient, high fluorescence lifetime, and moderate stimulated emission cross-section

Active Publication Date: 2018-12-25
CDGM GLASS LLC
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The photoelastic coefficient of phosphate laser neodymium glass is generally 1.8×10 -12 / Pa above, it is difficult to meet the requirements of high-power laser devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphate laser neodymium glass
  • Phosphate laser neodymium glass
  • Phosphate laser neodymium glass

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0063] The preparation method of phosphate laser neodymium glass of the present invention comprises the following steps:

[0064] ① Select the glass formula and weigh each raw material;

[0065] ② Fully mix the raw materials evenly to form a mixture;

[0066] ③The temperature of the silicon carbide melting furnace is raised to 1100-1150°C, and the mixture is evenly added to the ceramic material tank in the silicon carbide melting furnace at 20-25Kg / h;

[0067] ④Introduce O into the ceramic material tank 2 +CC1 4 Mixed gas, the air flow is 1-2L / min;

[0068] ⑤ After stopping the ventilation, inject the molten glass into the platinum crucible, and clarify the molten glass at 1200-1250°C for 3-4 hours;

[0069] ⑥ Mechanically stir the molten glass at 1050-1100°C for 2-4 hours;

[0070] ⑦ Pour the prepared glass liquid into a graphite mold for finalization, annealing and cooling.

[0071] Next, the performance and testing method of the phosphate laser neodymium glass of the ...

Embodiment

[0116] Embodiments 1-20 of the present invention are shown in Table 1-2. The composition (mol percent) and photoelastic coefficient B (10 -12 / Pa), stimulated emission cross section σ(10 -20 cm 2 ), fluorescence lifetime τ (μs), acid resistance stability (D A ) and air bubbles. It should be noted that the following examples are merely examples for better understanding of the present invention, and do not limit the present invention in any way.

[0117] Table 1

[0118]

[0119] Table 2

[0120]

[0121] The glass of the above-mentioned embodiment 9 is processed into a 1cm thick sample, and its absorption spectrum is tested with a spectrophotometer to obtain the required absorption spectrum curve for its stimulated emission cross-section test calculation, such as Figure 5 shown.

[0122] The glass of the above-mentioned embodiment 9 is processed into a sample with a thickness of 1mm, and its fluorescence spectrum is measured with a fluorescence spectrometer to obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fluorescence lifetimeaaaaaaaaaa
Login to View More

Abstract

The invention provides phosphate laser neodymium glass small in photoelastic coefficient. The phosphate laser neodymium glass comprises, by mole percentage, 30-60% of P2O5, 10-45% of MO, 0.5-8% of Al2O3, 1-10% of B2O3, 1-10% of SiO2, 1-15% of PbO, 0.1-5% of Nd2O3 and 0-15% of R2O, wherein R2O is one or more of K2O, Na2O and Li2O; MO is one or more of BaO, MgO, ZnO, CaO and SrO. The phosphate laserneodymium glass has the advantages that the laser glass is allowed to be small in photoelastic coefficient through a reasonable component proportion, the photoelastic coefficient B of the glass is below 1.55*10<-12> / Pa, and the glass is long in fluorescent lifetime, moderate in stimulated emission section, applicable to high-power laser devices and the like.

Description

technical field [0001] The invention relates to a laser glass, in particular to a laser neodymium glass with a small photoelastic coefficient. Background technique [0002] In a laser device based on a rod-shaped laser neodymium glass amplifier, the excitation light source such as a xenon lamp is usually placed in the direction of the cylinder of the laser neodymium glass rod, and the pump light is injected into the interior of the neodymium glass rod through the cylinder to promote the inversion of the number of neodymium ion particles. Thus realizing laser amplification, such as figure 1 shown. Since the neodymium glass has a large absorption coefficient for the pump light, the energy of the pump light from the outer layer to the center of the circle decreases gradually after the outer layer absorbs the light, that is, the pump light energy of the outer layer of the circular section of the neodymium glass rod The energy is significantly higher than that of the pump light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/074C03C3/072
CPCC03C3/072C03C3/074
Inventor 莫大洪于天来苏学剑
Owner CDGM GLASS LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com