Remelting method for electroslag ingot for cold roller

A technology of electroslag remelting and electroslag ingot, which is applied in the field of iron and steel metallurgy to improve hardenability and wear resistance and avoid production cracks

Active Publication Date: 2018-12-07
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, how to prepare high-quality electroslag ingots for cold rolling rolls by electroslag remelting, so as to prepare qualified cold rolling rolls for subsequent processes, there is currently no effective solution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This embodiment is to use the method of the present invention to produce Φ1100mm electroslag ingots, and the specific steps are as follows:

[0045] a. The raw materials are initially smelted in an electric arc furnace. After the smelting is completed, the molten steel is placed in a ladle refining furnace to refine the molten steel, and adjusted according to the composition requirements, and then vacuum degassed. After the molten steel is refined, it is molded into Φ730mm corrugated Ingot electrode rod;

[0046] b. Remove the risers of the casted 2 Φ730mm corrugated ingot electrode rods and weld the dummy electrodes, then check the surface quality of the electrode rods, clean up impurities such as iron oxide scale, and then put the electrode rods into the bottom of the car for heat treatment The furnace is heated and baked, the heating temperature is 840±10°C, the heating rate is ≤60°C / h, and the holding time is 12 hours;

[0047] c. Benxi steel or similar steel types...

Embodiment 2

[0054] This embodiment is to use the method of the present invention to produce Φ1100mm electroslag ingots, and the specific steps are as follows:

[0055] a. The raw materials are initially smelted in an electric arc furnace. After the smelting is completed, the molten steel is placed in a ladle refining furnace to refine the molten steel, and adjusted according to the composition requirements, and then vacuum degassed. After the molten steel is refined, it is molded into Φ730mm corrugated Ingot electrode rod;

[0056] b. Remove the risers of the casted 2 Φ730mm corrugated ingot electrode rods and weld the dummy electrodes, then check the surface quality of the electrode rods, clean up impurities such as iron oxide scale, and then put the electrode rods into the bottom of the car for heat treatment The furnace is heated and baked, the heating temperature is 850±10°C, the heating rate is ≤60°C / h, and the holding time is 15 hours;

[0057] c. Benxi steel or similar steel types...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a remelting method of an electroslag ingot for a cold roller, and belongs to the technical field of ferrous metallurgy. The technical problem to be solved is how to prepare thehigh-quality electroslag ingot for the cold roller through electroslag remelting. The invention provides the remelting method of the electroslag ingot for the cold roller. The remelting method comprises the steps of electrode rod baking, slag system selection, baking, melting protection slag, electroslag remelting process, and annealing process and the like. According to the method, chemical components of the electrode rod are improved, the proper slag system is selected, the electrode rod and slag material are baked, the electroslag remelting and the annealing process are adjusted, so that the electricslag ingot for the cold roller with good internal and external quality is prepared, defects such as ripples or slag runners are avoided, quality requirement of first-stage blank is met through high and low time inspection, and favorable conditions are provided for subsequent working procedure to guarantee product quality.

Description

technical field [0001] The invention belongs to the technical field of iron and steel metallurgy, and in particular relates to a method for remelting electroslag ingots for cold rolling rolls. Background technique [0002] The roll is one of the parts with the most complicated working conditions in the rolling mill, and it is also a high-tech product with the highest quality requirements, special materials, and complex manufacturing processes among roll products. With the rapid development of modern economic construction, the operating efficiency of large-scale cold rolling mills and the quality requirements of plates are constantly improving, and the required material strength requirements are getting higher and higher. Good performance and other aspects of development. The development of rolls at home and abroad mainly increases the content of Cr in cold rolls, from the initial 2% Cr to the 5% Cr cold rolls commonly used in the market, and continuously optimizes alloys su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C7/00C21C7/06C21C7/10C21D1/30C21D3/06C21D6/00C21D9/00C22B9/18C22C38/02C22C38/04C22C38/06C22C38/44C22C38/46
CPCC21C7/0006C21C7/06C21C7/10C21D1/30C21D3/06C21D6/004C21D6/005C21D6/008C21D9/0068C22B9/18C22C38/001C22C38/002C22C38/005C22C38/02C22C38/04C22C38/06C22C38/44C22C38/46Y02P10/20
Inventor 林发驹李宗周蔡武张建
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com