A method for smelting ultra-advanced duplex stainless steel made of cd3mwn

A technology of duplex stainless steel and process method, which is applied in the metallurgy field of metal materials, and can solve the problems of not very strict requirements, large investment in equipment, high production cost, etc.

Active Publication Date: 2020-07-28
LUOYANG SUNRUI SPECIAL EQUIP
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] At present, the intermediate frequency induction furnace melting process, intermediate frequency induction furnace + AOD furnace double melting process, electric arc furnace + AOD furnace double melting process, intermediate frequency induction furnace melting process, intermediate frequency Induction furnace + VOD furnace dual smelting process and electric arc furnace + VOD furnace dual smelting process, etc., using these smelting processes, duplex stainless steel that meets the composition requirements can be smelted, but the quality of molten steel is uneven and the composition fluctuates greatly. , Corrosion resistance is quite different, and the production cost is different
[0011] Intermediate frequency induction furnace + AOD furnace dual smelting process, electric arc furnace + AOD furnace dual smelting process, intermediate frequency induction furnace + VOD furnace dual smelting process and electric arc furnace + VOD furnace dual smelting process, the requirements for furnace materials are not very strict. Alloy charge can be used, such as returned furnace charge, scrap steel, ferromanganese, ferrochrome, electrolytic nickel, ferromolybdenum, etc., but the equipment investment is large, and it must be equipped with a refining furnace, which is suitable for large-scale production; dust, smoke and noise pollution, not environmentally friendly; induction furnace smelting is relatively environmentally friendly, and the production characteristics are highly adaptable, but the requirements for alloy furnace materials are higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for smelting ultra-advanced duplex stainless steel made of cd3mwn
  • A method for smelting ultra-advanced duplex stainless steel made of cd3mwn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Luoyang Shuangrui Special Equipment Co., Ltd. adopts the present invention when casting duplex stainless steel pump body castings made of ASTM A890 / A890M CD3MWN, and the implementation process is as follows:

[0061] (1) Prepare the alloy charge required for smelting ASTM A890 / A890M CD3MWN duplex stainless steel, pure iron, metallic chromium, ferrochromium nitride, electrolytic nickel, molybdenum bar, tungsten bar, crystalline silicon, electrolytic manganese, CD3MWN material return charge, lanthanum Cerium alloy (alloy block size 26-32mm, La+Ce content 99.1%), boron iron (alloy block size 16-23mm, B content 22%) and silicon-barium alloy (alloy block size 12-28mm, Ba content 26.1%, Si content is 45.8%.) etc. and slagging materials bagged active lime and fluorite etc.

[0062] (2) Medium frequency induction furnace is used for melting, and the furnace lining is made of neutral material.

[0063] (3) Active lime accounting for 1.2% of the mass of molten steel is added to ...

Embodiment 2

[0084] Luoyang Shuangrui Special Equipment Co., Ltd. adopts the present invention when casting duplex stainless steel impeller castings made of ASTM A890 / A890M CD3MWN, and the implementation process is as follows:

[0085] (1) Prepare the alloy charge required for smelting ASTM A890 / A890M CD3MWN duplex stainless steel, pure iron, metallic chromium, ferrochromium nitride, electrolytic nickel, molybdenum bar, tungsten bar, crystalline silicon, electrolytic manganese, CD3MWN material return charge, lanthanum Cerium alloy (alloy block size 26-32mm, La+Ce content 99.1%), boron iron (alloy block size 16-23mm, B content 22%) and silicon-barium alloy (alloy block size 12-28mm, Ba content 26.1%, Si content is 45.8%.) etc. and slagging materials bagged active lime and fluorite etc.

[0086] (2) Medium frequency induction furnace is used for melting, and the furnace lining is made of neutral material.

[0087] (3) Active lime accounting for 1.1% of the mass of molten steel is added to t...

Embodiment 3

[0107] Luoyang Shuangrui Special Equipment Co., Ltd. adopts the present invention when casting duplex stainless steel impeller castings made of ASTM A890 / A890M CD3MWN, and the implementation process is as follows:

[0108] (1) Prepare the alloy charge required for smelting ASTM A890 / A890M CD3MWN duplex stainless steel, pure iron, metallic chromium, ferrochromium nitride, electrolytic nickel, molybdenum bar, tungsten bar, crystalline silicon, electrolytic manganese, CD3MWN material return charge, lanthanum Cerium alloy (alloy size 20-34mm, La+Ce content 99.2%), boron iron (alloy size 18-24mm, B content 23.5%) and silicon-barium alloy (alloy size 15-25mm, Ba content 25.8%, Si content is 47%.), etc. and slag-making materials bagged active lime and fluorite, etc.

[0109] (2) Medium frequency induction furnace is used for melting, and the furnace lining is made of neutral material.

[0110] (3) Active lime accounting for 1.5% of the mass of molten steel is added to the bottom of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

A method for smelting ultra-advanced duplex stainless steel made of CD3MWN, which is designed for the internal control composition during smelting of duplex stainless steel; wherein C≤0.030 wt%, Si≤0.90 wt%, Mn is 1.20-2.50 wt%, P≤0.020 wt%, S≤0.015 wt%, Cr 26.2-27.5 wt%, Ni 6.2-7.6 wt%, Mo 2.2-3.4 wt%, Cu≤0.80 wt%, W≤0.80 wt%, N 0.32-0.38 wt%, B is 0.0010-0.0100 wt%, Ba is 0.0002-0.0100 wt%, Ce+La is 0.005-0.030 wt%; %Cr+3.3(%Mo+0.5%W)+16%N≥45, precise control of trace The content of elements B, Ba, Ce, and La; increase the N content to more than 0.30%, and at the same time avoid nitrogen pores in the casting; minimize the content of harmful elements such as sulfur, oxygen, hydrogen and other elements, and improve the liquid steel. purity. The poured casting has high strength and excellent corrosion resistance. The ratio of ferrite phase and austenite phase in stainless steel is close to 50%. The service life of the casting is prolonged, the manufacturing cost is greatly reduced, and the goals of energy saving, consumption reduction, and environmental protection are realized.

Description

technical field [0001] The invention belongs to the field of metal material metallurgy, and in particular relates to a process method for smelting super-advanced duplex stainless steel made of CD3MWN using an intermediate frequency induction furnace. Background technique [0002] Duplex stainless steel is stainless steel in which the ferrite phase and austenite phase each account for about half of the structure. Duplex stainless steel combines the excellent toughness of austenitic stainless steel with the higher strength and chloride stress corrosion resistance of ferritic stainless steel. The combination of properties makes duplex stainless steel have the advantages of both types of stainless steel materials, and it is widely used all over the world, mainly in oil and gas, chemical industry, marine engineering, shipbuilding, papermaking, food and light industry, and construction. [0003] However, for more demanding application environments, such as marine and deep-sea fiel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/00C21C7/00C21C7/06C22C33/06C22C38/02C22C38/04C22C38/42C22C38/44C22C38/54C22C38/58
CPCC21C5/005C21C7/0006C21C7/06C22C33/06C22C38/001C22C38/002C22C38/005C22C38/02C22C38/04C22C38/42C22C38/44C22C38/54C22C38/58Y02P10/20
Inventor 陈亚涛靳新锋
Owner LUOYANG SUNRUI SPECIAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products