Radar hood temperature-resistant coating material and preparation method thereof

A technology for coating materials and radomes, applied in coatings, fire-retardant coatings, etc., can solve the problems of short service life and narrow temperature resistance range, and achieve the effects of long service life, improved temperature resistance, and simple preparation method.

Inactive Publication Date: 2018-11-06
ANHUI NIKOLA ELECTRONICS TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems of narrow temperature-resistant range and short service life of coating materials used in radome in the prior art, and propose a heat-resistant coating material for radome and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A heat-resistant coating material for a radome, consisting of the following raw materials in parts by weight:

[0017] 38 parts of pure thermosetting liquid polyimide resin, 26 parts of linear low density polyethylene, 3.1 parts of hydroxyl-terminated polybutadiene, 4 parts of isobutyltriethoxysilane, 4 parts of expanded graphite, 3.2 parts of gas phase white carbon black , 3.2 parts of polyethylene wax, 1.5 parts of polyethylene glycol 4000, 1.5 parts of antioxidant.

[0018] The preparation method of the heat-resistant coating material for the above-mentioned radome comprises the following preparation steps:

[0019] (1) According to the formula ratio, weigh linear low density polyethylene and add it to isobutyltriethoxysilane and polyethylene wax, stir at a speed of 560r / min for 18min, then add expanded graphite and gas phase silica, and ultrasonically Evenly dispersed mixture A;

[0020] (2) According to the formula ratio, take thermosetting liquid polyimide pure ...

Embodiment 2

[0023] A heat-resistant coating material for a radome, consisting of the following raw materials in parts by weight:

[0024] 43 parts of pure thermosetting liquid polyimide resin, 28 parts of linear low density polyethylene, 3.2 parts of hydroxyl-terminated polybutadiene, 4.8 parts of isobutyltriethoxysilane, 4.6 parts of expanded graphite, 3.5 parts of gas phase white carbon black , polyethylene wax 3.6 parts, polyethylene glycol 2001.6 parts, antioxidant 1.8 parts.

[0025] The preparation method of the heat-resistant coating material for the above-mentioned radome comprises the following preparation steps:

[0026] (1) According to the formula ratio, weigh linear low-density polyethylene and add it to isobutyltriethoxysilane and polyethylene wax, stir at a speed of 580r / min for 20min, then add expanded graphite and gas phase silica, and ultrasonically Evenly dispersed mixture A;

[0027] (2) According to the formula ratio, take thermosetting liquid polyimide pure resin, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a radar hood temperature-resistant coating material and a preparation method thereof, and solves problems that in the prior art that a radar hood coating material generally can not bear high and low temperatures or is easy to crack under high and low temperatures, and is short in service life. The temperature-resistant coating material comprises the following raw materials: pure thermosetting liquid polyimide resin, linear low-density polyethylene, hydroxyl-terminated polybutadiene, isobutyltriethoxysilane, expanded graphite, gas-phase white carbon black, polyethylenewax, a dispersant, and an antioxidant. The coating material is prepared with a scientific and ratio-rigorous formula; the obtained temperature-resistant coating material has the advantages of being capable of resisting high and low temperatures, having low probability of cracking at high and low temperatures, and being capable of resisting temperature of 150-200 DEG C and long in service life; thepreparation method is simple, preparation conditions are mild, the industrial production is easy to realize, and the application is wide.

Description

technical field [0001] The invention relates to the technical field of military materials, in particular to a heat-resistant coating material for a radome and a preparation method thereof. Background technique [0002] Radar products are large electronic devices used in harsh environments, and the protection of their surfaces is particularly important. In the prior art, coatings are often used on the surface of radomes to improve their surface protection performance; however, in extreme environments, it is often required that the surface coatings of radomes have a wide range of temperature resistance to protect radars from environmental damage. The existing coating materials for radome generally have problems such as narrow temperature resistance range, brittle coating, and short service life. Based on the above statements, the present invention proposes a heat-resistant coating material for a radome and a preparation method thereof. Contents of the invention [0003] Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/08C09D123/08C09D7/61C09D7/63C09D7/65
CPCC08L2201/08C08L2205/035C09D5/18C09D7/61C09D7/63C09D7/65C09D7/70C09D179/08C08L23/0815C08L23/06C08L47/00C08K3/36C08K7/24C08K5/5419
Inventor 夏森陈大龙黄耀操瑞谢荣婷
Owner ANHUI NIKOLA ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com