Nickel aluminum spinel catalyst and preparation method thereof

A nickel-aluminum spinel and catalyst technology, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problem of low-temperature preparation of nickel-aluminum spinel catalysts. See reports and other issues to achieve the effect of simple preparation process and low reduction temperature

Active Publication Date: 2018-10-12
TAIYUAN UNIV OF TECH
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no report on the low-temperature preparation of nickel-aluminum spinel catalysts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel aluminum spinel catalyst and preparation method thereof
  • Nickel aluminum spinel catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of preparation method of nickel-aluminum spinel catalyst, carry out hydrothermal reaction after mixing organic matter, aluminum source and nickel source, then collect hydrothermal reaction product and roast to obtain required nickel-aluminum spinel catalyst; The organic matter is For terephthalic acid, trimesic acid or methyl trimesate, the calcination temperature is 400-600°C.

[0023] The preparation method of the nickel-aluminum spinel catalyst is synthesized by a one-step method, and the operation is simple and convenient; and the nickel-aluminum spinel catalyst can be formed by roasting at a low temperature without high temperature conditions. In addition, it should be emphasized that the preparation method of a highly dispersed and easily reducible supported nickel-aluminum catalyst provided in Chinese patent CN106582655A is an amorphous nickel-aluminum catalyst. And the present invention is by adding nickel source in situ, that is, adding organic matter, a...

Embodiment 2

[0027] A nickel-aluminum spinel catalyst, which is prepared by the preparation method of the nickel-aluminum spinel catalyst provided in Example 1, has a specific nickel-aluminum spinel structure.

[0028] Some experimental groups are provided below

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of chemical materials, and provides a nickel aluminum spinel catalyst and a preparation method thereof. The preparation method is as follows: mixing an organic substance, an aluminum source and a nickel source for hydrothermal reaction, and collecting a hydrothermal reaction product for calcining to obtain the desired nickel aluminum spinel catalyst; the organic substance is terephthalic acid, trimesic acid or trimethyl 1,3,5-benzenetricarboxylate, the calcination temperature is 400 to 600 DEG C. The preparation method of the nickel aluminum spinelcatalyst can obtain a specific nickel aluminum spinel structure, and has the advantages of simple preparation process and low reduction temperature. The invention also provides the nickel aluminum spinel catalyst prepared by the preparation method of the nickel aluminum spinel catalyst.

Description

technical field [0001] The invention relates to the technical field of chemical materials, in particular to a nickel-aluminum spinel catalyst and a preparation method thereof. Background technique [0002] Catalysts are widely used in all walks of life, whether in the traditional chemical, pharmaceutical, biological fields, or in the improvement of economic benefits, the development and utilization of clean energy, and environmental protection and governance, catalysts play a very important role. In short, the preparation and application of catalysts are related to the survival and development of human beings. [0003] Supported catalysts play a pivotal role in the field of catalysis due to their high activity and selectivity, easy recovery and reuse, and good stability. Nickel metal has been widely concerned due to its high activity and low cost in reactions such as biomass catalytic gasification, ethanol steam reforming, methane carbon dioxide reforming, bio-oil hydrogena...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/755
CPCB01J23/005B01J23/755
Inventor 闫晓亮卢晶军李瑞丰胡通范立明王倩倩
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com