A formula of a glaze material showing purple-white ripples in furnace transmutation

A white and corrugated technology, applied in the field of Jun porcelain, can solve the problems of aesthetic fatigue and achieve the effect of bright and bright glaze color, high ornamental collection value and high production value

Inactive Publication Date: 2018-10-09
温书强
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in recent years, the Jun porcelain industry has developed rapidly, and people are tired of aesthetics. The existing Jun porcelain glaze colors on the market can no longer meet people's increasing appreciation level and artistic pursuit. A new type of glaze with uniform and beautiful slices to solve the existing problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: the glaze material formula that becomes purple-white corrugated, comprises following raw material: feldspar, calcite, iron ore, ox bone ash, fluorite, soda stone, this medicine, frit, zinc oxide, talcum powder, copper oxide ,Tin oxide.

[0011] The composition of the raw materials is as follows: 65 parts of feldspar, 35 parts of calcite, 17 parts of iron ore, 15 parts of bovine bone ash, 23 parts of fluorite, 8 parts of soda stone, 8 parts of this medicine, 7 parts of frit, oxidation 4 parts of zinc, 0.8 part of talcum powder, 0.2 part of copper oxide, and 0.2 part of tin dioxide.

[0012] The Jun glaze produced in this embodiment is bright and bright in color, high in gloss, novel and beautiful in texture, evenly sliced, has high artistic value and ornamental and collection value, has a high firing rate, and has high production value. production efficiency.

Embodiment 2

[0013] Embodiment 2: the glaze formula that becomes purple-white corrugated, comprises following raw material: feldspar, calcite, iron ore, ox bone ash, fluorite, soda stone, this medicine, frit, zinc oxide, talcum powder, copper oxide ,Tin oxide.

[0014] The composition of the raw materials is as follows: 60 parts of feldspar, 30 parts of calcite, 15 parts of iron ore, 7 parts of bovine bone ash, 8 parts of fluorite, 7 parts of soda stone, 5 parts of this medicine, 5 parts of frit, oxidation 3 parts of zinc, 0.5 part of talcum powder, 0.1 part of copper oxide, and 0.1 part of tin dioxide.

[0015] The Jun glaze produced in this embodiment is bright and bright in color, high in gloss, novel and beautiful in texture, evenly sliced, has high artistic value and ornamental and collection value, has a high firing rate, and has high production value. production efficiency.

Embodiment 3

[0016] Embodiment 3: the glaze material formula that becomes purple-white corrugated, comprises following raw material: feldspar, calcite, iron ore, ox bone ash, fluorite, soda stone, this medicine, frit, zinc oxide, talcum powder, copper oxide ,Tin oxide.

[0017] The composition of the raw materials is: 70 parts of feldspar, 40 parts of calcite, 20 parts of iron ore, 20 parts of bovine bone ash, 15 parts of fluorite, 15 parts of soda stone, 10 parts of this medicine, 9 parts of frit, oxidation 5 parts of zinc, 1 part of talcum powder, 0.3 parts of copper oxide, and 0.3 parts of tin dioxide.

[0018] The Jun glaze produced in this embodiment is bright and bright in color, high in gloss, novel and beautiful in texture, evenly sliced, has high artistic value and ornamental and collection value, has a high firing rate, and has high production value. production efficiency.

[0019] Above-mentioned embodiment is prepared by following process:

[0020] The first step is to take ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a formula of a glaze material showing purple-white ripples in furnace transmutation. Raw materials of the glaze material include feldspar, calcite, iron ore, cattle bone ash,fluorite, kaolinite clay rock, glaze stone, frit, zinc oxide, talc powder, copper oxide and stannic oxide, and particularly include, by weight, 60-70 parts of the feldspar, 30-40 parts of the calcite,15-20 parts of the iron ore, 7-20 parts of the cattle bone ash, 8-15 parts of the fluorite, 7-15 parts of the kaolinite clay rock, 5-10 parts of the glaze stone, 5-9 parts of the frit, 3-5 parts of the zinc oxide, 0.5-1 part of the talc powder, 0.1-0.3 part of the copper oxide and 0.1-0.3 part of the stannic oxide. The glaze material has bright and gorgeous color, novel and beautiful patterns, uniform cracks, high artistic value and ornamental and collection value, a high firing yield, and high production value, and the production efficiency is increased.

Description

technical field [0001] The invention belongs to the technical field of Jun porcelain, and in particular relates to a glaze formula with purple-white ripples in a kiln. Background technique [0002] Porcelain is an important cultural carrier after bronze ware, and so is Jun porcelain. Jun porcelain began at the end of the Eastern Han Dynasty. So far, it has gone through Tang Jun flower glaze, Song Jun, Jin Yuan Jun porcelain, the decline of Ming Dynasty, the revival of late Qing Dynasty, and the emergence of hundreds of flowers after liberation. Among the famous kilns, only the modern Jun porcelain has surpassed the splendor of the Song Dynasty in a certain sense. In different periods, through the interpretation of Jun porcelain culture, craftsmen have continuously innovated Jun porcelain, and the glaze colors and glaze types of Jun porcelain have also been increasingly enriched. Jun porcelain is simple and dignified in shape, regular in shape, and well-proportioned in thick...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B41/86
CPCC03C8/14C03C2204/04C03C2205/02C04B41/5022C04B41/86C04B41/4539C04B41/0072C04B41/52
Inventor 温书强
Owner 温书强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com