Ru porcelain celeste blue glaze and preparation method thereof

A porcelain celadon glaze and calcite technology, which is applied in the field of ceramics, can solve the problems of natural kiln turning into azure color and agate entering the glaze, so as to achieve the effect of pure and delicate glaze layer and soft luster

Inactive Publication Date: 2018-08-28
马聚魁
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of Ru porcelain sky blue glaze, in order to solve the glaze color of thousands of generations of the sky blue glaze in the prior art, and solve the problem that agate enters the glaze, and the natural kiln becomes azure; the purpose of the present invention It is also to provide a preparation method of Ru porcelain sky blue glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A cerulean glaze for Ru porcelain, comprising the following components in parts by weight: 11 parts of agate stone, 6 parts of purple gold soil, 35 parts of feldspar powder, 9 parts of quartz powder, 16-25 parts of calcite, 3 parts of bone ash, and 6 parts of wood ash , 10 parts of local glazed soil (taken from Henan Baofeng local glazed soil), and 11 parts of self-made medicine.

[0026] The preparation method of Ru porcelain sky blue glaze comprises the following steps:

[0027] 1) Agate stone and calcite are refined, washed and pulverized into particles or powder respectively;

[0028] 2) Mix purple gold soil, feldspar powder, quartz powder, bone ash, wood ash, local glazed soil, self-made this medicine and the stone materials treated in step 1) according to the proportion, and then add water for ball milling. The amount of water added is 0.85 of the glaze. times, the ball milling time is 20 hours, and the glaze slurry is obtained;

[0029] 3) Adjust the concentrat...

Embodiment 2

[0035] A cerulean glaze for Ru porcelain, comprising the following components in parts by weight: 18 parts of agate stone, 9 parts of purple gold soil, 45 parts of feldspar powder, 15 parts of quartz powder, 25 parts of calcite, 8 parts of bone ash, 15 parts of wood ash, local glaze 16 parts of soil (taken from the local glazed soil in Baofeng, Henan), and 18 parts of this medicine.

[0036] The preparation method of Ru porcelain sky blue glaze comprises the following steps:

[0037] 1) Agate stone and calcite are refined, washed and pulverized into particles or powder respectively;

[0038] 2) Mix purple gold soil, feldspar powder, quartz powder, bone ash, wood ash, local glazed soil, self-made medicine and the stones treated in step 1) according to the proportion, and then add water for ball milling. The amount of water added is 0.90 of the glaze. times, the ball milling time is 60 hours, and the glaze slurry is obtained;

[0039] 3) Adjusting the concentration of the glaz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ru porcelain celeste blue glaze and a preparation method thereof. The ru porcelain celeste blue glaze is prepared from the following components in parts by weight: 11 to 18 parts of agate, 6 to 9 parts of purple and gold soil, 35 to 45 parts of feldspar powder, 9 to 15 parts of quartz powder, 16 to 25 parts of calcspar, 3 to 8 parts of bone ash, 6 to 15 parts of wood ash,10 to 16 parts of local glaze soil and 11 to 18 parts of home-made drug. The ru porcelain celeste blue glaze has the unique characteristics of lasting glaze color, natural accidental coloring into azure due to the adoption of agate, plain, elegance, smoothness, fineness, change along with light, brightness without dazzling, jade property, emulsion and ice property, green and elegant color, richness in water color, pure and fine glaze layer, jadeite color, high luster, softness, full glaze burning, dense glaze surface and texture like fish scales, cicada wings, crab claws, ice cracks and sesame blossoms.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a Ru porcelain sky blue glaze and a preparation method thereof. Background technique [0002] Ru porcelain was listed as the first of the five famous porcelains (Ru, Guan, Jun, Ge, Ding) in the Song Dynasty of our country, and was designated as royal porcelain at that time. The clay of Ru porcelain is fine, the fetal bone is hard, the glaze color is moist, and the shape is simple and generous. The characteristics of "sesame flower" are called "like jade but not jade but better than jade" by the world. Ru porcelain began in the late Northern Song Dynasty and got its name because the kiln site was in Ruzhou (now Ruzhou and Baofeng, Henan). Due to historical reasons, Ru Kiln flourished for only 20 years. Due to the short firing time, there are less than 100 pieces of treasures handed down to this day, which are very precious. [0003] The traditional ceramic glaze is a kind of s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14
CPCC03C8/14
Inventor 马聚魁马得原马铭
Owner 马聚魁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com