Double-side attaching aluminum foil paper for cigarette

A double-sided technology of aluminum foil paper, which is applied in the field of aluminum foil paper, can solve the problems of insufficient bonding, insufficient sealing, and poor adsorption of aluminum foil paper, and achieve good moisture-proof effect, improve production efficiency, and increase the bonding surface. Effect

Inactive Publication Date: 2018-08-14
CHUZHOU CIGARETTE MATERIALS FACTORY
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aluminum foil paper for cigarettes is one of the important packaging materials for cigarettes. The single-sided composite aluminum foil paper widely used at present, because of its thin texture and insufficient sealing performance, it is easy to make the filter element at the cigarette and the cigarette butt get wet, shorten the storage time, and cause waste and waste. loss, and when the filter element is damp, the adsorption effect becomes poor, and harmful substances are inhaled into the lungs, causing bodily harm; in addition, the existing aluminum foil paper is not firmly bonded, and it is easy to cause peeling between the layers of aluminum foil paper when it is heated and damp, which affects product quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-side attaching aluminum foil paper for cigarette
  • Double-side attaching aluminum foil paper for cigarette

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Preparation of ethyl maleate-silicone rubber copolymer emulsion

[0027] Add 100g of silicone rubber solution into the reaction tube, sequentially add 20g monomer ethyl maleate, 1g initiator benzoyl peroxide and 1g crosslinking agent 2-isopropylimidazole, stir well and swell at 25°C for 2h , then add 3g of reducing agent butylated hydroxyanisole under the protection of nitrogen, heat to 80-90°C and stir for copolymerization reaction for 5h, after the reaction is completed, add 0.2g of 0.01M sodium dihydrogen phosphate aqueous solution and stir for 2h to make the reaction liquid coagulate into latex , to obtain ethyl maleate-silicone rubber copolymer emulsion;

[0028] (2) Preparation of viscose:

[0029] Put the reaction tank into a water bath ultrasonic instrument, add 6g of water, 68g of ethyl maleate-silicone rubber copolymer emulsion, 10g of polyvinyl alcohol and 5g of methylol in sequence at a frequency of 20KHz-30KHz and a water bath temperature of 45-50°C S...

Embodiment 2

[0037] (1) Preparation of ethyl maleate-silicone rubber copolymer emulsion

[0038] Add 100g of silicone rubber solution into the reaction tube, sequentially add 20g monomer ethyl maleate, 5g initiator benzoyl peroxide and 5g crosslinking agent 2-isopropylimidazole, stir well and swell at 25°C for 2h , then add 3g of reducing agent butyl hydroxyanisole under the protection of nitrogen, heat to 90°C and stir for copolymerization reaction for 5h, after the reaction is completed, add 0.5g of 0.01M sodium dihydrogen phosphate aqueous solution and stir for 2h to make the reaction liquid condense into latex liquid, that is Obtain ethyl maleate-silicone rubber copolymer emulsion;

[0039] (2) Preparation of viscose:

[0040] Put the reaction tank into a water-bath ultrasonic instrument, add 8g of water, 50g of ethyl maleate-silicone rubber copolymer emulsion, 15g of polyvinyl alcohol and 10g of sodium hydroxymethylcellulose in sequence at a frequency of 30KHz and a water bath temper...

Embodiment 3

[0043] (1) Preparation of ethyl maleate-silicone rubber copolymer emulsion

[0044] Add 100g of silicone rubber solution into the reaction tube, add 20g of monomer ethyl maleate, 2g of initiator benzoyl peroxide and 3.5g of crosslinking agent 2-isopropylimidazole in sequence, stir evenly and swell at 25°C 2h, then add 3g of reducing agent butyl hydroxyanisole under the protection of nitrogen, heat to 80°C and stir for 5h of copolymerization reaction, after the reaction is completed, add 0.3g of 0.01M sodium dihydrogen phosphate aqueous solution and stir for 2h to make the reaction liquid coagulate into latex liquid, Promptly obtain ethyl maleate-silicone rubber copolymer emulsion;

[0045] (2) Preparation of viscose:

[0046]Put the reaction tank into a water-bath ultrasonic instrument, add 5g of water, 76g of ethyl maleate-silicone rubber copolymer emulsion, 7.5g of polyvinyl alcohol and 5g of hydroxymethyl cellulose in sequence at a frequency of 20KHz and a water bath tempe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses double-side attaching aluminum foil paper for a cigarette. The double-side attaching aluminum foil paper comprises an aluminum foil paper layer and a bonding layer, wherein butterfly grooves are uniformly formed in one side of the aluminum foil paper layer. A production process of the double-side attaching aluminum foil paper for cigarettes comprises the following steps ofS1, uniformly pressing one side of the double-side smooth aluminum foil paper into groove surfaces comprising butterfly grooves by a rolling pressing machine to obtain the aluminum foil paper layer; S2, uniformly coating an adhesive layer onto the groove surface of the aluminum foil paper layer to obtain a single-side aluminum foil paper; respectively putting the single-side aluminum foil paper onto placing frames arranged at the two sides; using a heat insulation conveying machine for simultaneously conveying the single-side aluminum foil paper at the left side and the right side to a position between attaching roller groups; performing pasting for bonding the adhesive layers of the two pieces of single-side aluminum foil paper to form the adhesive layer; S3, continuously feeding the pasted aluminum foil paper into shaping roller groups to be pressed and shaped; performing air cooling and edge cutting to obtain a finished product. The prepared double-side pasting aluminum foil paper for the cigarette has a good dampproof effect, and can be stored for a long time in various environments.

Description

technical field [0001] The invention belongs to the technical field of aluminum foil paper, and in particular relates to double-sided laminated aluminum foil paper for cigarettes. Background technique [0002] With the development of society and economy, the packaging of commodities is also constantly updated. Packaging materials based on paper and plastic films have been gradually replaced by exquisite and beautiful aluminum foil paper. The use of aluminum foil paper is increasing. Production brings new business opportunities. [0003] Aluminum foil paper for cigarettes is one of the important packaging materials for cigarettes. The single-sided composite aluminum foil paper widely used at present, because of its thin texture and insufficient sealing performance, it is easy to make the filter element at the cigarette and the cigarette butt get wet, shorten the storage time, and cause waste and waste. loss, and when the filter element is damp, the adsorption effect becomes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B29/00B32B29/06B32B7/12
CPCB32B29/005B32B7/12B32B29/06
Inventor 杜威陶香君邢连成
Owner CHUZHOU CIGARETTE MATERIALS FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products