Colloidal crystal paint and application of colloidal crystal paint to preparation of mouse pad

A technology of colloidal crystals and mouse pads, applied in coatings, data processing input/output processes, instruments, etc., can solve the problems of limited photoelectric mouse and low efficiency, and achieve improved moving speed, simple process equipment, and high productivity high effect

Active Publication Date: 2018-08-07
QINGDAO UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the performance of the mouse pads on the market is generally relatively mature, the movement of the photoelectric mouse is positioned by the light emitted from the bottom of the mouse and then reflected by the mouse pad back to the light sensor inside the photoelectric mouse for positioning. The efficiency of the mouse pad to the reflected light of the photoelectric mouse is not high, so it limits the practical application of the photoelectric mouse

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colloidal crystal paint and application of colloidal crystal paint to preparation of mouse pad
  • Colloidal crystal paint and application of colloidal crystal paint to preparation of mouse pad
  • Colloidal crystal paint and application of colloidal crystal paint to preparation of mouse pad

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The colloidal crystal coating described in this embodiment includes 0.5 g of monodisperse copolymer microspheres with a particle diameter of 220 nm, and 0.01 g of water-soluble carbon black.

[0029] The monodisperse copolymer microspheres described in this example are polymerized from styrene, methyl methacrylate and acrylic acid monomer components, which can be prepared according to methods known in the prior art. Monodisperse copolymer microspheres are prepared as follows:

[0030] Add 100ml of distilled water to a 250ml three-necked flask, then dissolve 17.5mg of emulsifier SDBS and 0.50g of buffer ammonium bicarbonate in the above distilled water, and in addition, 1.00g of MMA, 1.00g of AA and 19.00g of After St is mixed evenly, it is added to the above-mentioned three-necked flask, mechanically stirred, 450r / min, and heated in an oil bath. When the temperature rises to 70°C, continue to keep stirring at a constant temperature for 30min, and then add an aqueous sol...

Embodiment 2

[0038] The colloidal crystal coating described in this embodiment includes 0.5 g of monodisperse copolymer microspheres with a particle diameter of 260 nm, and 0.01 g of water-soluble carbon black.

[0039] The monodisperse copolymer microspheres described in this example are polymerized from styrene, methyl methacrylate and acrylic acid monomer components, which can be prepared according to methods known in the prior art. Copolymer microspheres are prepared as follows:

[0040] Add 100ml of distilled water to a 250ml three-necked flask, then dissolve 17.5mg of emulsifier SDBS and 0.50g of buffer ammonium bicarbonate in the above distilled water, and in addition, 1.00g of MMA, 1.00g of AA and 19.00g of After St is mixed evenly, it is added to the above-mentioned three-necked flask, mechanically stirred, 450r / min, and heated in an oil bath. When the temperature rises to 70°C, continue to keep stirring at a constant temperature for 30min, and then add an aqueous solution of init...

Embodiment 3

[0048] The colloidal crystal coating described in this embodiment includes 0.4 g of monodisperse copolymer microspheres with a particle diameter of 220 nm, and 0.01 g of water-soluble carbon black.

[0049] The preparation method of the monodisperse copolymer microspheres described in this example is the same as that in Example 1.

[0050] The preparation method of the colloidal crystal coating described in the present embodiment comprises the steps:

[0051] S1. Cleaning of copolymer microspheres:

[0052] Evenly disperse 0.4g of monodisperse copolymer microspheres with a particle size of 220nm in 40ml of distilled water, pour into a centrifuge tube and wash with distilled water and ethanol three times each until the supernatant is clear;

[0053] S2, doping the cleaned copolymer microspheres with carbon black:

[0054] Disperse the cleaned copolymer microspheres into 40ml of distilled water, add 0.01g of water-soluble carbon black, pour the mixed solution into a centrifuge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of colloidal crystal materials and specifically relates to colloidal crystal paint. According to the colloidal crystal paint, water-soluble carbon black isutilized to enhance reflected light intensity of colloidal crystal. The invention further discloses application of the colloidal crystal paint to prepation of the mouse pad. The colloidal crystal paint disclosed by the invention is prepared by mixing copolymer microballoon emulsion with the water-soluble carbon black. The water-soluble carbon black is favorable for enhancing the reflected light intensity of colloidal crystal, so that the colloidal crystal paint is suitable for preparing photoelectric mouse pads. The photoelectric mouse pad is covered by the colloidal crystal paint disclosed by the invention to form a light reflecting layer; according to a mouse movement speed test, a movement speed of a photoelectric mouse on the mouse pad coated with the colloidal crystal paint is higherthan that of the photoelectric mound on a mouse pad not coated with the colloidal crystal paint. Therefore, the colloidal crystal paint disclosed by the invention is favorable for improving the reflected light intensity of the mouse pad and can improve the mouse movement speed.

Description

technical field [0001] The invention belongs to the technical field of colloidal crystal materials, and in particular relates to a colloidal crystal coating. The colloidal crystal coating utilizes water-soluble carbon black to enhance the reflected light intensity of colloidal crystals, and further discloses its application for preparing mouse pads. Background technique [0002] Colloidal crystals are a class of substances with three-dimensional ordered structures formed by monodisperse micron or submicron inorganic or organic particles. In the three-dimensional ordered structure of colloidal crystals, the repeating period is on the order of micrometers and submicrometers, and visible light (400-700nm) can undergo Bragg diffraction in it, making it present different colors. In the past few decades, the study of the optical properties of colloidal crystals has received high attention. [0003] At present, the application fields of colloidal crystals are very extensive, and r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D7/61G06F3/039C08F212/08C08F220/14C08F220/06
CPCC08F212/08C09D7/61C09D125/14G06F3/0395C08F220/14C08F220/06C08K3/04
Inventor 丛海林于冰李照卿张小艳
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka