Waterborne brilliant UV-curable aluminium paint, preparation method and application method thereof

An aluminum powder paint, water-based technology, used in polyurea/polyurethane coatings, coatings, etc., can solve the problems of uneven surface, poor adhesion and low gloss of the workpiece, and achieve good aluminum powder arrangement effect, good adhesion, high gloss effect

Inactive Publication Date: 2018-07-27
CHUZHOU JINQIAO TEXAS NEW MATERIALS CO LTD
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a water-based bright light UV curing aluminum powder paint on the basis of the prior art, which can solve the unsmooth surface of the electroplated workpiece, low gloss, poor adhesion, non-abrasion resistance and other undesirable problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] The preparation method of water-based light UV curing aluminum powder paint provided by the invention may further comprise the steps:

[0046] (1) Preparation of aluminum paste: Add Toyo FZ-F-290 into container a, set the stirring speed at 600~800r / min, and stir for 5~10 min; then add water, propylene glycol methyl ether acetate, dispersant and di Methylethanolamine, continue to stir for 5 ~ 15min;

[0047] (2) Resin material mixing: add water-based UV urethane acrylate to container b, set the speed at 600~800r / min, stir for 5~10 minutes, then add the formula amount of water, wetting agent, leveling agent and dimethicone Glyethanolamine, continue to stir for 5-10 minutes; add photoinitiator, defoamer and thickener with half the formula amount, increase the speed to 1400-1600r / min, and continue to stir for 10-20 minutes;

[0048] (3) Mixing of aluminum paste and resin: reduce the speed of container b to 400~600r / min, add the aluminum paste prepared in container a to con...

Embodiment 1

[0054] The aluminum paste includes the following components and parts by mass: 54 parts of Toyo FZ-F-290, 7.0 parts of water, 18 parts of propylene glycol methyl ether acetate, 3 parts of dispersant, and 0.05 part of dimethylethanolamine.

[0055] A water-based light UV curing aluminum powder paint, it comprises the following components and parts by mass:

[0056] Waterborne UV polyurethane acrylate UCECOAT 7655 68 parts;

[0057] Wetting agent (TEGO Wet 270) 0.08 part;

[0058] Leveling agent (TEGO Rad 2100N) 0.02 parts;

[0059] Leveling agent (BYK333) 0.05 parts;

[0060] 1.5 parts of water;

[0061] 0.15 parts of dimethylethanolamine;

[0062] Photoinitiator (2-hydroxy-2-methyl-1-phenyl-1-propanone) 0.9 parts;

[0063] Defoamer (BYK088) 0.09 parts;

[0064] Thickener (Wanhua Chemical Vesmody U300) 1.4 parts;

[0065] Thickener (UH 450) 1.4 parts;

[0066] Aluminum paste 3 parts.

[0067] The preparation method of this aluminum powder paint comprises the following ...

Embodiment 2

[0072] The aluminum paste includes the following components and parts by mass: 58 parts of Toyo FZ-F-290, 13 parts of water, 26.8 parts of propylene glycol methyl ether acetate, 5.2 parts of dispersant, and 0.08 parts of dimethylethanolamine.

[0073] A water-based light UV curing aluminum powder paint, it comprises the following components and parts by mass:

[0074] Waterborne UV polyurethane acrylate UCECOAT 7655 74 parts;

[0075] Wetting agent (BYK346) 0.14 parts;

[0076] Leveling agent (TEGO Rad 2100N) 0.16 parts;

[0077] 2.8 parts of water;

[0078] 0.25 part of dimethylethanolamine;

[0079] Photoinitiator (2-hydroxy-2-methyl-1-phenyl-1-propanone) 1.8 parts;

[0080] Photoinitiator (ethyl 2,4,6-trimethylbenzoylphosphonate) 0.8 parts;

[0081] Defoamer (BYK088) 0.13 part;

[0082] Defoamer (BYK024) 0.08 parts;

[0083] Thickener (U450) 2.1 parts;

[0084] Thickener (UH 420) 2.1 parts;

[0085] Aluminum paste 10 parts.

[0086] The preparation method of this ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to waterborne brilliant UV-curable aluminium paint, a preparation method and an application method thereof, in order to solve the problems of unsmooth surface of electroplated workpieces, low luster, bad adhesive force, bad wear resistance, and the like, and belongs to the field of environmentally friendly aluminium paint. The aluminium paint mainly comprises the following components in parts by mass: 65-95 parts of waterborne UV-curable polyurethane acrylate, 0.05-0.5 parts of a wetting agent, 0.05-0.5 parts of a levelling agent, 2-10 parts of a thickening agent, 0.5-3.5parts of a photoinitiator, 0.05-0.5 parts of an antifoaming agent, 0.1-3.0 parts of dimethyl ethanolamine, 1-6 parts of water, and 2-14 parts of aluminium slurry. The aluminium paint can be used forcoating the surface of a household electrical appliance plastic part, and the paint film has the characteristics of good aluminium powder arrangement effects, high luster, high hardness and high wearresistance.

Description

technical field [0001] The invention belongs to the field of environment-friendly aluminum powder paint, and specifically relates to a water-based bright UV-curable aluminum powder paint; in addition, the invention also relates to a preparation method and a use method of the water-based bright UV-curable aluminum powder paint. Background technique [0002] Aluminum powder paint is a paint containing aluminum powder. Due to the good ductility of aluminum, a continuous aluminum film can be formed in the coating film, which can cover pinholes and reduce permeability. [0003] The traditional aluminum powder paint coating is generally based on solvent-based coatings. Usually, the paint material for the production of aluminum powder paint is composed of alkyd resin, solvent and aluminum powder paste, and alkyd resin is composed of polybasic acid, monobasic acid and polybasic acid. Alcohol and other raw materials are produced by esterification reaction in the resin reactor. The s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/61
CPCC09D175/14C08K2003/0812
Inventor 王景泉
Owner CHUZHOU JINQIAO TEXAS NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap