High-permeability penetrated oil layer for semi-rigid road base layer, and preparation method thereof

A road base, high-permeability technology, applied in building components, building insulation materials, buildings, etc., to achieve the effects of good permeability, product safety, and less volatiles

Active Publication Date: 2018-07-10
漯河市谊路达公路养护工程有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of high-permeability penetrating oil for semi-rigid pavement base and its preparation method in order to overcome the defects of existing penetrating oil materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-permeability penetrated oil layer for semi-rigid road base layer, and preparation method thereof
  • High-permeability penetrated oil layer for semi-rigid road base layer, and preparation method thereof
  • High-permeability penetrated oil layer for semi-rigid road base layer, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] High-permeability penetrating oil for semi-rigid pavement base, made of the following raw materials in parts by weight: 400-600 parts of asphalt, 80-120 parts of kerosene, 10-20 parts of emulsifier, 15-25 parts of hydrochloric acid, 300- 400 copies.

[0027] It is prepared from the following raw materials in parts by weight: 450-550 parts of asphalt, 90-110 parts of kerosene, 12-18 parts of emulsifier, 18-22 parts of hydrochloric acid and 340-380 parts of water.

[0028] It is made from the following raw materials in parts by weight: 500 parts of asphalt, 100 parts of kerosene, 15 parts of emulsifier, 20 parts of hydrochloric acid and 365 parts of water.

[0029] The asphalt is high-permeability emulsified asphalt.

[0030] The model of the emulsifier is MQK-1M.

[0031] As the above-mentioned preparation method for the high-permeability penetrating oil of semi-rigid pavement base, the concrete steps are as follows:

[0032] (1) Heat the asphalt to 120-140°C;

[003...

Embodiment 2

[0036] The high-permeability penetrating layer oil for semi-rigid pavement base is made of the following raw materials in parts by weight: 400kg of asphalt, 80kg of kerosene, 10kg of emulsifier, 15kg of hydrochloric acid, and 300kg of water.

[0037] The asphalt is a high-permeability emulsified asphalt.

[0038] The model of the emulsifier is MQK-1M.

[0039] As the above-mentioned preparation method for the high-permeability penetrating oil of semi-rigid pavement base, the concrete steps are as follows:

[0040] (1) Heat the asphalt to 120°C;

[0041] (2) After mixing kerosene, emulsifier, hydrochloric acid and water, heat to 50°C;

[0042] (3) Pass the heated raw materials in step (1) and step (2) into the colloid mill at the same time, grind them, and mix the raw materials evenly to obtain high-permeability penetrating layer oil.

Embodiment 3

[0044] The high-permeability penetrating layer oil used for semi-rigid pavement base is made of the following raw materials in parts by weight: 440kg of asphalt, 90kg of kerosene, 12kg of emulsifier, 17kg of hydrochloric acid, and 320kg of water.

[0045] The asphalt is a high-permeability emulsified asphalt.

[0046] The model of the emulsifier is MQK-1M.

[0047] As the above-mentioned preparation method for the high-permeability penetrating oil of semi-rigid pavement base, the concrete steps are as follows:

[0048] (1) Heat the asphalt to 124°C;

[0049] (2) After mixing kerosene, emulsifier, hydrochloric acid and water, heat to 54°C;

[0050] (3) Pass the heated raw materials in step (1) and step (2) into the colloid mill at the same time, grind them, and mix the raw materials evenly to obtain high-permeability penetrating layer oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetration depthaaaaaaaaaa
penetration depthaaaaaaaaaa
penetration depthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-permeability penetrated oil layer for a semi-rigid road base layer, wherein the high-permeability penetrated oil layer is prepared from the following raw materials by weight: 400-600 parts of asphalt, 80-120 parts of kerosene, 10-20 parts of an emulsifier, 15-25 parts of hydrochloric acid, and 300-400 parts of water. The specific steps comprise: (1) heating the asphalt to a temperature of 120-140 DEG C; (2) mixing the kerosene, the emulsifier, the hydrochloric acid and the water, and heating to a temperature of 50-70 DEG C; and (3) simultaneously introducing theheated raw materials obtained in the step (1) and the step (2) into a colloid mill, and grinding to uniformly mix the raw materials so as to obtain the high-permeability penetrated oil layer. In the prior art, the domestic emulsified asphalt penetrated oil layer has poor permeability, the easily-formed oil film can be adhered away by the wheel, rolled or worn out, and other problems exist. According to the present invention, the high-permeability penetrated oil layer can solve the problems in the prior art; and through the auxiliary agent screening, formula optimizing and other system researches, the high-permeability penetrated oil layer is researched and developed and has advantages of safety, environment protection and good application effect.

Description

technical field [0001] The invention belongs to the technical field of road construction materials, and in particular relates to a high-permeability penetrating layer oil used for semi-rigid pavement bases and a preparation method thereof. Background technique [0002] The interlayer bond between the cement-stabilized macadam base and the asphalt pavement has always been a weak link of this type of pavement, which in turn leads to water damage of the base and deterioration of the stress state of the asphalt pavement. In order to solve this problem, 9.1 of "Technical Specifications for Construction of Highway Asphalt Pavement JTG F40-2004" stipulates that all kinds of bases must be sprayed with penetrating oil, and the penetration depth is required to be not less than 5mm, so as to play the role of consolidation, stability, connection and waterproof . [0003] At present, the penetrating oil products widely used in the market mainly include coal tar pitch, kerosene diluted p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L91/00C08K3/16
CPCC08L95/005C08L91/00C08K3/16
Inventor 田东平王振宇张冬鹏高贵菊刘娜尹冰马志明李恒刘琳张凯杨胜李晓琼刘龙张剑英项明坡李锐宁雷孙庭跃朱朝军王纪龙郭文朋
Owner 漯河市谊路达公路养护工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com