Surface adjusting agent containing manganese phosphate

A technology of surface modifier and manganese phosphate, which is applied in the coating process of metal materials, etc., which can solve the problems of excessive particle size of manganese phosphate, inconvenient use of powder, and easy agglomeration

Active Publication Date: 2018-07-06
SHANGHAI YAOYAN CHEM CO LTD
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, these various manganese phosphate crystal nuclei used as surface modifiers have disadvantages, that is, the particle size of manganese phosphate is too large, and it is easy to agglomerate over time, and its shape is powder, which is inconvenient to use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surface adjusting agent containing manganese phosphate
  • Surface adjusting agent containing manganese phosphate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of the dispersion is as follows: there is no special limitation on the preparation method for dispersing the manganese phosphate in the aqueous medium to form the aqueous dispersion. A better method is to mix the manganese phosphate in the dispersion medium such as water or organic solvent, and then Prepared by wet pulverization in the presence of additives.

[0032]When preparing an aqueous dispersion of manganese phosphate, it is more appropriate in the process to mix manganese phosphate in an aqueous medium for wet pulverization when preparing the dispersion, or wet grinding in a dispersion medium other than the aqueous medium. After pulverization, solvent replacement was performed again to prepare a solution.

[0033] Usually, the blending amount of manganese phosphate in the dispersion is 0.5 to 50%. If it is less than 0.5%, the content of manganese phosphate is too small, and the effect of the surface conditioner obtained with this dispersio...

Embodiment 1

[0065] Calculated in parts by weight, the manganese phosphate-containing surface regulator includes 2 parts of manganese phosphate, 100 parts of solvent, 6 parts of dispersant, 1 part of neutralizer, and 0.8 part of thickener; the manganese phosphate-containing surface regulator Particle size D of manganese phosphate 90 At 1.40 μm, D 50At 0.45 μm; the solvent is water, the dispersant is carboxymethyl cellulose, modified carboxymethyl cellulose, polyethylene glycol, and the carboxymethyl cellulose and the modified carboxymethyl cellulose The weight ratio of element, described polyethylene glycol is 1:0.3:0.7; Described neutralizing agent is 2-amino-2-methyl-1-propanol; Described thickening agent is diatomaceous earth, xanthan Gum, the weight ratio of the diatomaceous earth to the xanthan gum is 1:3.6;

[0066] The preparation method of the surface regulator containing manganese phosphate is as follows:

[0067] Add 2 parts of manganese phosphate, 100 parts of solvent, 6 part...

Embodiment 2

[0072] Calculated in parts by weight, the manganese phosphate-containing surface regulator includes 2 parts of manganese phosphate, 100 parts of solvent, 6 parts of dispersant, 1 part of neutralizer, and 0.8 part of thickener; the manganese phosphate-containing surface regulator Particle size D of manganese phosphate 90 At 1.40 μm, D 50 At 0.45 μm; the solvent is water, the dispersant is carboxymethyl cellulose, modified carboxymethyl cellulose, polyethylene glycol, and the carboxymethyl cellulose and the modified carboxymethyl cellulose The weight ratio of element, described polyethylene glycol is 1:0.1:0.7; Described neutralizing agent is 2-amino-2-methyl-1-propanol; Described thickening agent is diatomaceous earth, xanthan Gum, the weight ratio of the diatomaceous earth to the xanthan gum is 1:3.6;

[0073] The preparation method of the manganese phosphate-containing surface regulator and the modified carboxymethyl cellulose are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a surface adjusting agent containing manganese phosphate. The surface adjusting agent containing the manganese phosphate comprises the following components of, by weight, 0.4-5parts of the manganese phosphate, 80-100 parts of a solvent, 2-10 parts of a dispersing agent, 0.5-3 parts of a neutralizer and 0.5-2 parts of a thickening agent; and the average particle size of themanganese phosphate in the surface adjusting agent containing the manganese phosphate is 2 microns or below, D90 is 1.5 microns or below, and the PH value is 3-9. According to the surface adjusting agent containing the manganese phosphate, the stability is excellent, brushing is not needed after chemical conversion treatment of the iron and steel wear-resistant manganese phosphate, and the excellent treatability is realized.

Description

technical field [0001] The invention relates to the technical field of surface regulators, in particular, the invention relates to a surface regulator containing manganese phosphate. Background technique [0002] The main moving parts inside the refrigerator compressor, such as the crankshaft, piston, and outer bearings, have to work reciprocatingly under numerous high-temperature motions. In addition to ensuring the machining accuracy, it is also necessary to degrease the surface of the parts, adjust the surface, and use manganese phosphate chemistry. Converted and brushed, it helps to enhance the abrasion resistance of the outer surface and enhances the oil absorption of refrigeration oil. [0003] The purpose of the surface conditioning treatment is to rapidly, uniformly, and densely form a film of manganese phosphate crystals on the steel surface in the manganese phosphate-based chemical conversion treatment that is the next step. Usually, the iron and steel material is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/78
CPCC23C22/78
Inventor 戴忆锋万满
Owner SHANGHAI YAOYAN CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com