Ceramic-based dental department bone powder and preparation method thereof

A technology based on dental and bone powder, applied in the field of ceramic-based dental bone powder and its preparation, can solve the problems of poor hydrophilicity, unfavorable cell adhesion and proliferation, and poor biocompatibility, so as to improve water absorption performance, improve bone repair effect, The effect of low production cost

Active Publication Date: 2018-06-05
BEIJING ALLGENS MEDICAL SCI & TECH
View PDF12 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of poor biocompatibility and hydrophilicity of the existing dental bone powder, which is not conducive to the adhesion and proliferation of cells on the bone powder material, the present invention provides a dental dental bone powder with good biocompatibility and excellent hydrophilic effect. Ceramic-based dental bone powder can improve the effect of bone repair, but also has a lower production cost and is convenient for clinical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic-based dental department bone powder and preparation method thereof
  • Ceramic-based dental department bone powder and preparation method thereof
  • Ceramic-based dental department bone powder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0079] In some embodiments, the preparation method of the porous hydroxyapatite includes:

[0080] (a) preparing hydroxyapatite suspension;

[0081] (b) adding the first PMMA particles and the second PMMA particles to the hydroxyapatite suspension to obtain a sintered base liquid;

[0082] (c) placing the sintering base liquid in a sintering device for sintering to obtain a sintered material;

[0083] (d) crushing and sieving the sintered material to obtain the porous hydroxyapatite.

[0084] Preferably, the step (a) is carried out as follows:

[0085] Mix 15-20g of hydroxyapatite in batches (for example, the hydroxyapatite can be divided into 3-10 parts, so that the hydroxyapatite can be added in 3-10 times) and 20-35mL of PBS solution are mixed, Then add 1.5-2.5 mL of polyvinyl alcohol solution with a concentration of 0.05-0.1 g / mL, stir evenly, and prepare the hydroxyapatite suspension. The PBS solution here is a commonly used phosphate buffered saline solution with a p...

Embodiment 1

[0116] A kind of ceramic base dental bone powder, its preparation component comprises:

[0117] Porous hydroxyapatite;

[0118] Type I collagen, the mass is 1% of the mass of porous hydroxyapatite;

[0119] Wherein, the preparation component of porous hydroxyapatite comprises hydroxyapatite, the first PMMA particle and the second PMMA particle, the mass ratio is 5:2.5:1.5, and the particle diameter of the first PMMA particle is 50 μ m, the second PMMA particle The particle size of the particles is 500 μm; and

[0120] Porous hydroxyapatite is prepared by sintering, and the sintering process is shown in Table 1

[0121] Table 1

[0122]

Embodiment 2

[0124] A kind of ceramic base dental bone powder, its preparation component comprises:

[0125] Porous hydroxyapatite;

[0126] Type I collagen, the mass is 10% of the mass of porous hydroxyapatite;

[0127]Wherein, the preparation component of porous hydroxyapatite comprises hydroxyapatite, the first PMMA particle and the second PMMA particle, the mass ratio is 5:3.5:2.5, and the particle diameter of the first PMMA particle is 100 μ m, the second PMMA particle The particles have a particle size of 1000 μm; and

[0128] Porous hydroxyapatite is prepared by sintering, and the sintering process is shown in Table 2:

[0129] Table 2

[0130]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a ceramic-based dental department bone powder and a preparation method thereof. The powder comprises preparation components, namely porous hydroxyapatite and type-I collagen,wherein the porous hydroxyapatite comprises preparation components, namely hydroxyapatite of a specific mass ratio, first PMMA (Polymethyl Methacrylate) granules and second PMMA granules; the particlesizes of the first PMMA granules are 50-100mu m; the particle sizes of the second PMMA granules are 500-1000mu m; the porous hydroxyapatite is made through sintering preparation; the sintering preparation comprises the following stages: at stage I, the heating velocity is 5-10 DEG C, the target temperature is 500-600 DEG C, and the constant temperature time is 20-30 minutes; at stage II, the heating velocity is 5-10 DEG C / minute, the target temperature is 1200-1500 DEG C, and the constant temperature time is 200-300 minutes; at stage III, heating is stopped, and the temperature is reduced naturally. The ceramic-based dental department bone powder is excellent in water absorption property and bone repairing effect and relatively low in production cost.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to a ceramic-based dental bone powder and a preparation method thereof. Background technique [0002] In dental surgery, there are many situations that may cause bone defect or bone deficiency in patients after surgery, such as bone defect after periodontal cyst extraction, and bone deficiency caused by alveolar ridge atrophy after tooth extraction. These conditions often limit the patient's postoperative bone healing and the effect of subsequent dental implants, so bone implants are required. The current gold method is mainly to use autologous bone for transplantation, but its application is limited due to its limited source and certain postoperative complications in the donor site. Allogeneic bone grafts have potential antigenicity and risk of disease transmission. Therefore, artificial bone repair materials have become the research direction of many scholars because of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/24A61L27/12A61L27/10A61L27/50A61L27/56
CPCA61L27/10A61L27/12A61L27/24A61L27/50A61L27/56A61L2430/12
Inventor 胡艳丽宋天喜崔云朱金亮何志敏仇志烨崔菡
Owner BEIJING ALLGENS MEDICAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com