Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of n-alkylacrylamide

A technology of alkyl acrylamide and acrylonitrile, which is applied in the preparation of carboxylic acid amide, organic compound, sulfuric acid ester, etc. It can solve the problems of high cost and low recycling rate of waste liquid, so as to reduce the treatment cost and speed up the production process. The effect of reaction speed and mild reaction conditions

Active Publication Date: 2020-09-15
BEIJING HENGJU CHEM GRP +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems of high cost and low recycling rate of waste liquid in the prior art, and provide a preparation method of N-alkylacrylamide, which only uses concentrated sulfuric acid as a catalyst and does not need to add organic acid As a co-catalyst, it can be directly recovered to obtain high-purity sulfuric acid, which can be reused after concentration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of n-alkylacrylamide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] This embodiment relates to the preparation method of N-alkylacrylamide described in the present invention, comprising the following steps:

[0040] 1) According to the ratio of n (acrylonitrile): n (α-olefin): n (concentrated sulfuric acid) = 1:0.95:1, add 130.7g of concentrated sulfuric acid with a concentration of 75% to the equipment equipped with a condenser, thermometer, and agitator In the reactor, the temperature of the system was lowered to 5°C with an ice-water bath, and 53 grams of acrylonitrile and 159.9 grams of 1-dodecene were slowly added dropwise in sequence. During the dropping process, the reaction temperature did not exceed 8°C. , the temperature of the system was raised to 40°C, and the stirring reaction was continued for 3.5h; the reaction was completed, and an intermediate was obtained;

[0041] 2) Add 17.1 grams of deionized water to the monomer, stir evenly, let stand, and separate layers to obtain an upper layer solution and a lower layer solutio...

Embodiment 2

[0044] This embodiment relates to the preparation method of N-alkylacrylamide described in the present invention, comprising the following steps:

[0045]1) According to the ratio of n (acrylonitrile): n (α-olefin): n (concentrated sulfuric acid) = 1:1:1.2, add 147g of concentrated sulfuric acid with a concentration of 80% into a container equipped with a condenser, a thermometer and a stirrer. In the reactor, the temperature of the system was lowered to 5°C in an ice-water bath, and 53 grams of acrylonitrile and 196 grams of 1-tetradecene were slowly added dropwise in sequence. During the dropwise addition, the reaction temperature did not exceed 8°C. After the dropwise addition, the system The temperature was raised to 40°C, and the stirring reaction was continued for 3.5 hours; the reaction was completed, and the monomer was obtained;

[0046] 2) Add 18 grams of deionized water to the intermediate, stir evenly, leave standstill, and separate layers to obtain an upper layer ...

Embodiment 3

[0049] This embodiment relates to the preparation method of N-alkylacrylamide described in the present invention, comprising the following steps:

[0050] 1) According to the ratio of n (acrylonitrile): n (α-olefin): n (concentrated sulfuric acid) = 1: 1.1: 1.2, add 138.2 g of concentrated sulfuric acid with a concentration of 85% into a condenser, thermometer, and agitator In the reactor, the temperature of the system was lowered to 5°C with an ice-water bath, and 53 grams of acrylonitrile and 246.4 grams of 1-hexadecene were slowly added dropwise in sequence. During the dropwise addition, the reaction temperature did not exceed 8°C. After the dropwise addition, The temperature of the system was raised to 50°C, and the stirring reaction was continued for 6 hours; after the reaction was completed, an intermediate was obtained;

[0051] 2) Add 18 grams of deionized water to the intermediate, stir evenly, leave standstill, and separate layers to obtain an upper layer solution an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of N-alkyl acrylamides. The preparation method comprises the following steps: 1) under the catalysis of concentrated sulfuric acid, acrylonitrile reacts with an alpha-olefin to form an intermediate, wherein in the reaction process, the molar ratio of acrylonitrile, alpha-olefin and sulfuric acid is controlled to be 1:[0.9-1.1]:[1-1.2]; 2) water is added to the intermediate to perform hydrolysis, so as to obtain an upper layer hydrolysis product and a lower layer sulfuric acid solution; and 3) the upper layer hydrolysis product is purified to give the N-alkyl acrylamides. According to the preparation method, no organic acid is added as a cocatalyst, the sulfuric acid can be directly separated from the reaction product to obtain high-purity sulfuric acid, and the high-purity sulfuric acid can be directly reused after being concentrated, thereby eliminating the consumption of an alkali in the reaction process, and greatly reducing treatment cost of waste acid and production cost; and the yield of the target product is greater than 90%, the purity is greater than 98%, the reaction process is mild and easy to control, the source of raw materials is wide, and the product post-processing is simple, therefore, the N-alkyl acrylamides are easy for industrial production.

Description

technical field [0001] The invention belongs to the field of synthesis of organic compounds, and in particular relates to a preparation method of N-alkylacrylamide. Background technique [0002] Hydrophobic association Water-soluble polymers have a unique structure. In aqueous solution, due to the hydrophobic effect, the hydrophobic groups of the polymers aggregate, causing macromolecular chains to produce intramolecular and intermolecular associations, so they have good viscosity-increasing properties. Shear resistance, salt resistance, etc., are widely used in the fields of enhanced oil recovery, fluidity control and paint thickening. [0003] There are four types of methods for the preparation of hydrophobic monomer N-alkylacrylamides that are hydrophobically associated with water-soluble polymers: (1) the reaction method of acryloyl chloride and alkylamine; (2) thermal decomposition of carboxylic acid or sulfonic acid amides (3) reaction method of olefin or alcohol and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C231/10C07C231/24C07C233/09
CPCC07C231/10C07C231/24C07C303/24C07C233/09C07C305/14
Inventor 莫衍志徐青林吴林健彭韵燕白宝成
Owner BEIJING HENGJU CHEM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com