A kind of preparation method of metal coating on the surface of carbon fiber composite material

A composite material and surface metal technology, which is applied to the device, coating, epoxy resin coating and other directions of coating liquid on the surface, can solve the problems of the decrease of the strength of the carbon fiber composite material, damage to the surface of the substrate, and reduce the bonding strength, etc. The effect of improving bond strength, avoiding thermal damage, and increasing bond strength

Inactive Publication Date: 2021-03-26
BEIJING SATELLITE MFG FACTORY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, if figure 1 As shown, the current method of thermal arc spraying to prepare metal coating on the surface of carbon fiber composite will damage the surface of the substrate, resulting in a decrease in the strength of the carbon fiber composite, and there are defects such as pores and cracks between the coating and the coating, which reduces the bonding strength of the two.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of metal coating on the surface of carbon fiber composite material
  • A kind of preparation method of metal coating on the surface of carbon fiber composite material
  • A kind of preparation method of metal coating on the surface of carbon fiber composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] see figure 2 , the embodiment of the present invention provides a method for preparing a metal coating on the surface of a carbon fiber composite material, comprising the following steps:

[0034] Step 1. First, vacuum bake, polish and wipe the carbon fiber composite material to obtain the pretreated composite material;

[0035] Specifically, the carbon fiber composite material may be carbon fiber / epoxy 648 resin-based composite material, carbon fiber / cyanate resin-based composite material, carbon fiber / phenolic resin-based composite material, etc., which are not limited in the present invention;

[0036] Step 2, coating resin-metal-organic hybrid paint on the surface of the pretreated composite material to obtain an interface coating;

[0037] Specifically, the resin metal-organic hybrid paint is a paint obtained by organic hybridization of resin and metal; the resin can be epoxy resin, phenolic resin, polyester resin, etc., preferably the matrix resin of carbon fibe...

Embodiment 1

[0054] This embodiment provides a carbon fiber composite material with a metal coating, and its preparation method includes:

[0055] Step 1. Put the carbon fiber / epoxy 648 resin-based composite material into a vacuum oven for pretreatment, with a heating temperature of 100°C and a heating time of 12 hours.

[0056] Step 2. Polish the surface of the carbon fiber composite material pretreated in step 1 to a matte state with 600# sandpaper, and then gently wipe the surface with absolute ethanol for use.

[0057] Step 3. Prepare the aluminum powder-resin metal-organic hybrid paint material. The configuration process is as follows: dissolve 70g of epoxy resin in 70g of butyl acetate, and stir for 1 hour at the stirring speed of 350r / min to obtain component A; Dissolve 30g of aluminum powder in 60g of butyl acetate, and stir for 1 hour at a stirring paddle speed of 350r / min to prepare component B; mix components A and B, and stir for 3 hours at a stirring paddle speed of 350r / min ...

Embodiment 2

[0063] This embodiment provides a carbon fiber composite material with a metal coating, and its preparation method includes:

[0064] Step 1. Put the carbon fiber / cyanate resin-based composite material into a vacuum oven for pretreatment, with a heating temperature of 120°C and a heating time of 10 hours.

[0065] Step 2. Polish the surface of the carbon fiber composite material pretreated in step 1 to a matte state with 400# sandpaper, and then gently wipe the surface with absolute ethanol for use.

[0066] Step 3. Prepare aluminum powder-resin metal hybrid paint. The configuration process is as follows: Dissolve 50g of epoxy resin in 50g of butyl acetate, and stir for 1 hour at a stirring speed of 400r / min to obtain component A; Dissolve 50g of aluminum powder in 60g of butyl acetate, and stir for 1 hour at a stirring paddle speed of 400r / min to prepare component B; mix components A and B at a stirring paddle speed of 400r / min for 3 hours An interface coating paint is prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a metal coating on the surface of a carbon fiber composite material, and belongs to the technical field of surface treatment of materials. The preparation method includes the following steps that firstly, the carbon fiber composite material is subjected to vacuum baking, grinding and wiping to obtain a pretreated composite material; secondly, the surface of the pretreated composite material is coated with resin metal organic hybrid paint to obtain an interface coating; the surface of the obtained interface coating is sandblasted and then sprayed with deposited metal to obtain the carbon fiber composite material with the metal coating on the surface. By means of the preparation method, the surface of the prepared metal coating is uniform and dense, and the bonding strength between the metal coating and the carbon fiber composite material is high.

Description

technical field [0001] The invention belongs to the technical field of material surface treatment, and in particular relates to a method for preparing a metal coating on the surface of a carbon fiber composite material. Background technique [0002] Carbon fiber composites have a series of excellent properties such as high specific strength, high specific modulus, ablation resistance, corrosion resistance, small thermal expansion coefficient, flexibility and weaving, and are more and more widely used in the aerospace field. At this stage, a large number of products such as spacecraft structural cabin wall panels, central load-bearing cylinders, antennas, solar arrays, remote sensing camera lens barrels, and hoods have been made of carbon fiber materials. Affected by the lightweight design of spacecraft, more and more spacecraft structural products, such as fuel tanks, optical mirrors, lander supports, and large radar antenna brackets, have also begun to use composite materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/04C09D163/00C09D7/61C08L61/06C08L63/00C08L79/04C08K7/06B05D1/38B05D7/00
CPCB05D1/38B05D7/54C08J2361/06C08J2363/00C08J2379/04C08J2463/00C08K7/06C08K2003/0812C09D163/00C08J7/0427C08L63/00C08L61/06C08L79/04
Inventor 张杭张家强张立功崔庆新白晶莹贺光辉杨铁山
Owner BEIJING SATELLITE MFG FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com