Mie resonance anti-counterfeiting product based on hollow structure purple TiO2 and anti-counterfeiting method of Mie resonance anti-counterfeiting product
A hollow structure and product technology, applied in the preparation/purification of carbon, titanium oxide/hydroxide, instruments, etc., can solve the problems that users are not easy to identify, cannot distinguish authenticity, and anti-counterfeiting labels are easy to be counterfeited, so as to meet the requirements of anti-counterfeiting. requirements, easy to distinguish, to overcome the complex preparation and small-scale effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0034] A kind of purple TiO with monodisperse hollow structure 2 The preparation method of material comprises the following steps:
[0035] Step 1, a certain amount of tetraethyl orthosilicate is mixed with absolute ethanol and deionized water and stirred evenly, the volume ratio of ethanol to tetraethyl orthosilicate is 26:1, deionized water and tetraethyl orthosilicate The volume ratio is 5:1;
[0036] Step 2, add a certain amount of concentrated ammonia water (concentration 26-28wt%) to step 1, the volume ratio of concentrated ammonia water to tetraethyl orthosilicate is 0.7:1, and centrifuge, wash and separate after stirring for 4 hours;
[0037] Step 3, the SiO obtained in step 2 2 Dispersed in an appropriate amount of absolute ethanol for subsequent use, the volume ratio of the volume of absolute ethanol to tetraethyl orthosilicate described in step 1 is 23:1;
[0038] Step 4, to the SiO in step 3 2 Add a certain volume of acetonitrile and an appropriate amount of hy...
Embodiment 2
[0046] A kind of purple TiO with monodisperse hollow structure 2 The preparation method of material comprises the following steps:
[0047] Step 1, mix and stir a certain amount of tetraethyl orthosilicate with absolute ethanol and deionized water, the volume ratio of ethanol to tetraethyl orthosilicate is 20:1, deionized water and tetraethyl orthosilicate The volume ratio is 4:1;
[0048] Step 2, add a certain amount of concentrated ammonia water (concentration 26-28%) to step 1, the volume ratio of concentrated ammonia water to tetraethyl orthosilicate is 0.68:1, centrifuge and wash and separate after stirring for 4 hours;
[0049] Step 3, the SiO obtained in step 2 2 Dispersed in an appropriate amount of absolute ethanol for subsequent use, the volume ratio of the volume of absolute ethanol to tetraethyl orthosilicate described in step 1 is 23:1;
[0050] Step 4, to the SiO in step 3 2 Add a certain volume of acetonitrile and an appropriate amount of hydroxypropyl cellu...
Embodiment 3
[0058] A kind of purple TiO with monodisperse hollow structure 2 The preparation method of material comprises the following steps:
[0059] Step 1, mix and stir a certain amount of tetraethyl orthosilicate with absolute ethanol and deionized water, the volume ratio of ethanol to tetraethyl orthosilicate is 25:1, deionized water and tetraethyl orthosilicate The volume ratio is 6:1;
[0060] Step 2, add a certain amount of concentrated ammonia water (concentration 26-28%) to step 1, the volume ratio of concentrated ammonia water to tetraethyl orthosilicate is 0.64:1, and centrifuge and wash after stirring for 4 hours;
[0061] Step 3, the SiO obtained in step 2 2 Dispersed in an appropriate amount of absolute ethanol for subsequent use, the volume ratio of the volume of absolute ethanol to tetraethyl orthosilicate described in step 1 is 23:1;
[0062] Step 4, to the SiO in step 3 2 Add a certain volume of acetonitrile and an appropriate amount of hydroxypropyl cellulose to t...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com