Furfuryl alcohol polymer impregnated wood

A technology for impregnating wood and polymer, applied in the field of wood impregnated with furfuryl alcohol polymer, can solve the problems of environmental and human injury, low mechanical strength of wood, etc., and achieve the effect of high mechanical strength

Inactive Publication Date: 2018-04-03
宿州市徽睿木业有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in the prior art, toxic reagents are usually used for wood modification, which will cause harm to the environment and the human body, and the mechanical strength of the treated wood is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of wood impregnated with furfuryl alcohol polymer, comprises the following steps:

[0019] (1) Dipping: wood is put into the soaking solution, and the soaking solution submerges the wood completely, and the soaking solution is made of 50% (weight) water, 28% (weight) furfuryl alcohol, 9% (weight) nano calcium carbonate, 8% ( weight) sodium carbonate and 5% (weight) citraconic anhydride, the dipping temperature is 40°C, and the dipping time is 48h.

[0020] (2) Curing step: take out the wood from the dipping solution, and cure it at 150°C for 5 hours.

Embodiment 2

[0022] A kind of wood impregnated with furfuryl alcohol polymer, comprises the following steps:

[0023] (1) Impregnation: wood is put into the soaking solution, and the soaking solution submerges the wood completely, and the soaking solution is made of 60% (weight) water, 20% (weight) furfuryl alcohol, 8% (weight) nano calcium carbonate, 8% ( weight) sodium bicarbonate and 4% (weight) malic acid, the dipping temperature is 50°C, and the dipping time is 36h.

[0024] (2) Curing step: take out the wood from the dipping solution, and cure at 160°C for 4 hours.

Embodiment 3

[0026] A kind of wood impregnated with furfuryl alcohol polymer, comprises the following steps:

[0027] (1) Impregnation: wood is put into the soaking solution, and the soaking solution submerges the wood completely, and the soaking solution is made of 70% (weight) water, 15% (weight) furfuryl alcohol, 5% (weight) nano-calcium carbonate, 7% ( weight) sodium citrate and 3% (weight) palmitic acid, the dipping temperature is 40°C, and the dipping time is 48h.

[0028] (2) Curing step: take out the wood from the dipping solution, and cure it at 150°C for 5 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood impregnated with furfuryl alcohol polymer, which is obtained by impregnating wood with a polymerizable furfuryl alcohol monomer mixture, the mixture is composed of 50%-85% (weight) water, 10%-28% ( weight) furfuryl alcohol, 1%~9% (weight) nano-calcium carbonate, 2%~8% (weight) stabilizer and 0.5%~5% (weight) initiator composition, described stabilizer is selected from sodium carbonate, The group consisting of sodium bicarbonate, sodium citrate and sodium phosphate, the initiator is selected from the group consisting of citraconic anhydride, malic acid and palmitic acid.

Description

technical field [0001] The invention relates to the field of wood processing, in particular to wood impregnated with furfuryl alcohol polymer. Background technique [0002] Modified wood is produced by first impregnating a wood sample with an appropriate amount of a polymerizable liquid and, after impregnation, heating the wood sample so that the polymerizable compound is polymerized in the wood cell walls. [0003] The mechanism of wood impregnation is to impregnate low-molecular-weight resins into wood. Under certain conditions, the resins polymerize with each other, or form hydrogen bonds or chemical bonds with hydroxyl groups in wood, and generate insoluble polymers in the cell wall. The number of hydroxyl groups in the wood reduces the hydrophilicity of the wood, thereby resisting the adsorption of water by the cell wall; the resin polymer changes the swelling and expansion of the cell wall to resist the shrinkage of the cell wall; in addition, the density of the treate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/52B27K3/02
CPCB27K3/52B27K3/02
Inventor 李雪
Owner 宿州市徽睿木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com