Preparation method of high water retention antibacterial graphite oxide mask base cloth

A graphene and base fabric technology, applied in the fields of textiles and cosmetics, can solve problems such as adverse effects on skin tissue, skin irritation damage, skin irritation, etc., and achieve good facial beauty and skin care effects, good moisturizing properties, and increasing moisturizing properties. Effect

Inactive Publication Date: 2018-03-30
IANGSU COLLEGE OF ENG & TECH
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the antiseptic and antibacterial agent added can inhibit the proliferation of skin cells and cause adverse effects on the skin tissue that is in contact. This may cause the mask to have a certain degree of irritation to the skin, bacteria, and even damage the skin when it is used. Stimulation damage, even allergies, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A preparation method of a graphene oxide high water-retaining antibacterial mask base cloth, the base cloth is composed of a nutrient layer fiber net and a hydrophobic skeleton layer fiber net, and the nutrient layer fiber net is made of graphene oxide nylon fiber and The biomass fibers are uniformly blended and prepared through a spunlace non-woven process; the hydrophobic skeleton layer fiber web is prepared from graphene oxide nylon fibers through a spunlace non-woven process.

[0016] The graphene oxide nylon fiber accounts for 20% of the total weight of the nutrient layer fiber web, and the biomass fiber accounts for 80% of the total weight of the nutrient layer fiber web.

[0017] The graphene oxide nylon fiber is made of graphene oxide as a raw material, and the weight percentage of graphene in the graphene oxide nylon fiber is 0.5%.

[0018] The specification of the graphene oxide nylon fiber is 7.22tex(65D) / 36F.

[0019] The biomass fiber is one or more of vis...

Embodiment 2

[0022] A preparation method of a graphene oxide high water-retaining antibacterial mask base cloth, the base cloth is composed of a nutrient layer fiber net and a hydrophobic skeleton layer fiber net, and the nutrient layer fiber net is made of graphene oxide nylon fiber and The biomass fibers are uniformly blended and prepared through a spunlace non-woven process; the hydrophobic skeleton layer fiber web is prepared from graphene oxide nylon fibers through a spunlace non-woven process.

[0023] The graphene oxide nylon fiber accounts for 10% of the total weight of the nutrient layer fiber web, and the biomass fiber accounts for 90% of the total weight of the nutrient layer fiber web.

[0024] The graphene oxide nylon fiber is made of graphene oxide as a raw material, and the weight percentage of graphene in the graphene oxide nylon fiber is 0.9%.

[0025] The specification of the graphene oxide nylon fiber is 8.33tex (75D) / 36F.

[0026] The biomass fiber is one or more of vi...

Embodiment 3

[0029] A preparation method of a graphene oxide high water-retaining antibacterial mask base cloth, the base cloth is composed of a nutrient layer fiber net and a hydrophobic skeleton layer fiber net, and the nutrient layer fiber net is made of graphene oxide nylon fiber and The biomass fibers are uniformly blended and prepared through a spunlace non-woven process; the hydrophobic skeleton layer fiber web is prepared from graphene oxide nylon fibers through a spunlace non-woven process.

[0030] The graphene oxide nylon fiber accounts for 14% of the total weight of the nutrient layer fiber web, and the biomass fiber accounts for 87% of the total weight of the nutrient layer fiber web.

[0031] The graphene oxide nylon fiber uses graphene oxide as a raw material, and the weight percentage of graphene in the graphene oxide nylon fiber is 0.7%.

[0032] The specification of the graphene oxide nylon fiber is 7.86tex (69D) / 36F.

[0033] The biomass fiber is one or more of viscose,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of high water retention antibacterial graphite oxide mask base cloth. The base cloth is formed by combining a nutritive layer fiber net and a hydrophobic framework layer fiber net, wherein the nutritive layer fiber net is prepared by evenly blending graphite oxide nylon fibers and biomass fibers via a spunlace non-woven fabric technology; and the hydrophobic framework layer fiber net is prepared from the graphite oxide nylon fibers via the spunlace non-woven fabric technology. The high water retention antibacterial graphite oxide mask base cloth isgood in skin friendliness, antibacterial property and moisture retention, simple in structure, high in production efficiency, low in cost and safer to use. The mask base cloth is not required to adopta preservative, meets green, ecological, environment-friendly and healthy requirements and can obtain a better facial beautifying and skin care effect.

Description

technical field [0001] The invention relates to the field of textiles and cosmetic products, in particular to a preparation method of a graphene oxide high water-retention antibacterial mask base cloth. Background technique [0002] Masks are becoming more and more popular among consumers. Stick-on masks are mainly made of mask base cloth and nutritional essence. The conventional mask base fabric is usually made of polyester staple fibers and viscose staple fibers, which are opened and mixed, then cross-laid and formed, and then spunlaced. In order to control the proliferation of bacteria on the mask for a long time, the nutritional essence must be artificially added with antiseptic and antibacterial agents. However, the added antiseptic and antibacterial agent inhibits the proliferation of skin cells and has adverse effects on the contacted skin tissue. This may cause the mask to have a certain degree of irritation to the skin when it is used, and bacteria can be generated...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/02A61Q19/00D04H1/4382D06B15/00
CPCA61Q19/00A61K8/0212D06B15/00A61K2800/10A61K2800/524D04H1/43835
Inventor 陈志华张炜栋
Owner IANGSU COLLEGE OF ENG & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com