Technology for producing mosaic glass body

A preparation process and technology of glass gobs, which are applied in glass manufacturing equipment, glass molding, manufacturing tools, etc., can solve the problems of single structural characteristics of mosaic glass blanks, low regularity of mosaic glass blanks, and limited pattern decoration diversity, etc. , to achieve the effect of facilitating size adjustment, saving labor costs, and bright pattern effect

Inactive Publication Date: 2018-03-23
佛山市唯格建材有限公司 +1
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the existing glass mosaic body preparation process, raw glass powder is usually used for ball milling and granulation, and the mosaic glass body is obtained by dry pressing. Melted at the firing temperature, the mosaic glass body finally obtained often has low regularity, unobvious edges, and is prone to rounded corners, which leads to the need for grinding and other processing, which greatly consumes large labor costs; and The structural characteristics of the obtained mosaic glass body are single, thus greatly limiting the diversity of its pattern decoration; in addition, in the prior art, waste glass powder is not used in the preparation process of the glass mosaic body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technology for producing mosaic glass body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1-a kind of preparation technology of mosaic glass body, comprises the steps:

[0022] (1) Mix 95% raw glass powder and 5% waste glass powder evenly according to mass percentage to obtain a mixture;

[0023] (2) adding water ball milling to the mixture obtained in step (1) to obtain a slurry, and performing granulation and sieving to obtain a mixed green body powder;

[0024] (3) Put the mixed green body powder into a mold, press to form, and perform low-temperature firing at a temperature of 750° C. to obtain a mosaic glass body with a thickness of 1.45 mm.

Embodiment 2

[0025] Embodiment 2-a kind of preparation technology of glass mosaic, comprises the steps:

[0026] (1) Mix 80% raw glass powder and 20% waste glass powder evenly according to mass percentage to obtain a mixture;

[0027] (2) adding water ball milling to the mixture obtained in step (1) to obtain a slurry, and performing granulation and sieving to obtain a mixed green body powder;

[0028] (3) After putting the mixed green body powder into the mould, the green glass powder is arranged above the mixed green body powder, and uniformly pressed and formed, wherein the thickness of the green body is 1.55 mm;

[0029] (4) Glazing: The surface of the pressed mosaic glass body is applied with a low-temperature glaze under a constant pressure of 0.3Mpa, and the thickness of the glaze is 0.05mm;

[0030] (5) Inkjet printing: Inkjet printing is carried out on the surface of the mosaic glass body with low-temperature glaze applied;

[0031] (6) The ink-jet printed mosaic glass body was ...

Embodiment 3

[0032] Embodiment 3-a kind of preparation technology of glass mosaic, comprises the steps:

[0033] (1) Mix 90% raw glass powder and 10% waste glass powder evenly according to the mass percentage to obtain a mixture;

[0034] (2) adding water ball milling to the mixture obtained in step (1) to obtain a slurry, and performing granulation and sieving to obtain a mixed green body powder;

[0035] (3) Put the mixed green body powder into the mould, press and form, wherein the thickness of the green body is 1.50mm;

[0036] (4) Glazing: the surface of the pressed mosaic glass body is applied with a low-temperature glaze under a constant pressure condition of 2.5Mpa, and the thickness of the glaze is 0.15mm;

[0037] (5) Inkjet printing: Inkjet printing is carried out on the surface of the mosaic glass body with low-temperature glaze applied;

[0038] (6) The ink-jet printed mosaic glass body was fired at a low temperature of 780° C. to obtain a glass mosaic 2 with an opaque struc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A technology for producing a mosaic glass body comprises the following steps: 1, uniformly mixing 80-95 mass% of raw glass powder with 5-20 mass% of waste glass powder to obtain a mixture; 2, adding water to the mixture obtained in step 1, performing ball milling to obtain a slurry, and granulating and sieving the slurry to obtain a mixed body powder; and 3, adding the mixed body powder into a die, performing compression molding, and carrying out low-temperature sintering to obtain the mosaic glass body. The technology for producing the mosaic glass body has the advantages of realization of the effective recycling of the waste glass powder, and reduction of the production cost; and the prepared mosaic glass body has the advantages of high regularity, good skeleton feeling, structured and uniform laying, high strength and good non-transparent effect.

Description

technical field [0001] The invention relates to the technical field of glass preparation and processing, in particular to a preparation process of a mosaic glass body. Background technique [0002] At present, in the existing glass mosaic body preparation process, raw glass powder is usually used for ball milling and granulation, and the mosaic glass body is obtained through dry pressing. Melted at the firing temperature, the finally obtained mosaic glass body often has low regularity, unobvious edges, and is prone to rounded corners, which leads to the need for grinding and other processing, which greatly consumes large labor costs; and The obtained mosaic glass body has a single structural feature, which greatly limits the diversity of its pattern decoration; in addition, in the prior art, waste glass powder is not used in the preparation process of the glass mosaic body. Contents of the invention [0003] The purpose of the present invention is to propose a preparation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/02C03B19/06C03C17/34
CPCC03B19/06C03C1/002C03C17/34
Inventor 姚文江刘勇王飞任东
Owner 佛山市唯格建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com