Carmine furnace Jun firing process

A technology of carmine and craftsmanship, which is applied in the field of glazes, can solve the problems of short firing time, general kiln transformation effect, and fast heating, etc., and achieve the effect of improving smoothness, good kiln transformation effect, and the glaze surface is as moist as jade

Inactive Publication Date: 2018-03-16
朱海玉
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In today's environmental protection situation, the firing of liquefied gas kiln has become the mainstream of Shenhou Jun porcelain, but the disadvantage of liquefaction is that the temperature rises too fast. The fire can be ceased within an hour, which results in a short firing time and a general kiln transformation effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of firing process of carmine furnace Jun, comprising the following steps

[0027] (1) Preparation of embryo material and glaze

[0028] The raw material is composed of the following raw materials in parts by weight: 60 parts of flint slope soil, 20 parts of Luowang soil, 10 parts of quartz sandstone, and 3 parts of bauxite;

[0029] The glaze is composed of the following raw materials in parts by weight: 30 parts of feldspar, 1 part of rare earth powder, 20 parts of quartz, 2 parts of rudolite, 0.3 part of glauconite, 3 parts of plant ash, 0.1 part of zinc oxide, frit 5 copies;

[0030] (2) Blank making; the blank obtained in step (1) is drawn to form a blank, and when the drawn blank is dry to a certain extent, the blank is trimmed, and finally the designed blank is obtained;

[0031] (3) biscuit firing; putting the green body obtained in step (2) into a kiln to obtain the green body;

[0032] (4) Glazing; evenly attaching the glaze prepared in step (1) to th...

Embodiment 2

[0035] A kind of firing process of carmine furnace Jun, comprising the following steps

[0036] (1) Preparation of embryo material and glaze

[0037] The raw material is composed of the following raw materials in parts by weight: 70 parts of flint slope soil, 30 parts of Luowang soil, 15 parts of quartz sandstone, and 8 parts of bauxite;

[0038] The glaze is composed of the following raw materials in parts by weight: 60 parts of yellow feldspar, 2 parts of rare earth powder, 30 parts of quartz, 3.5 parts of rudolite, 0.4 part of glauconite, 4 parts of plant ash, 0.2 part of zinc oxide, 7 parts of frit share;

[0039] (2) Blank making; the blank obtained in step (1) is drawn to form a blank, and when the drawn blank is dry to a certain extent, the blank is trimmed, and finally the designed blank is obtained;

[0040] (3) biscuit firing; putting the green body obtained in step (2) into a kiln to obtain the green body;

[0041] (4) Glazing; evenly attaching the glaze prepared...

Embodiment 3

[0044] A kind of firing process of carmine furnace Jun, comprising the following steps

[0045] (1) Preparation of embryo material and glaze

[0046] The raw material is composed of the following raw materials in parts by weight: 80 parts of flint slope soil, 40 parts of Luowang soil, 20 parts of quartz sandstone, and 13 parts of bauxite;

[0047] The glaze is composed of the following raw materials in parts by weight: 90 parts of yellow feldspar, 3 parts of rare earth powder, 40 parts of quartz, 5 parts of rudolite, 0.5 part of glauconite, 5 parts of plant ash, 0.3 part of zinc oxide, 9 parts of frit share;

[0048] (2) Blank making; the blank obtained in step (1) is drawn to form a blank, and when the drawn blank is dry to a certain extent, the blank is trimmed, and finally the designed blank is obtained;

[0049] (3) biscuit firing; putting the green body obtained in step (2) into a kiln to obtain the green body;

[0050] (4) Glazing; evenly attaching the glaze prepared ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a firing process of a carmine furnace; a firing process of a carmine furnace, comprising the following steps: (1) preparing blanks and glazes; (2) making blanks; (3) biscuit firing; 4) Glazing; (5) Glaze firing; the present invention adopts liquefied gas kiln firing, the pressure is lowered to 0.03 before ignition, which is beneficial to the drying of the embryo body, and then the pressure is raised to 0.12 when the temperature rises. 1250°C and heat preservation for 2 to 3 hours, which is conducive to the sealing of the glaze surface, improving the smoothness of the product, making the kiln transformation effect better, and the glaze surface more moist like jade.

Description

technical field [0001] The invention relates to the field of glazes, in particular to a firing process of carmine red furnace jun. Background technique [0002] The development history of ceramics is an important part of the history of Chinese civilization. As one of the four ancient civilizations, China has made outstanding contributions to the progress and development of human society. Among them, the invention and development of ceramics has unique significance. Different dynasties and dynasties in Chinese history have different artistic styles and different technical characteristics. "china" in English means both China and ceramics, which clearly shows that China is the "hometown of ceramics". As early as more than a thousand years before the Europeans mastered the porcelain manufacturing technology, the Han people had already produced very exquisite ceramics. China is one of the first countries in the world to use pottery, and Chinese porcelain is highly respected by ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B41/86C03C8/14C04B33/34
CPCC04B33/13C03C8/14C04B33/34C04B41/5022C04B41/86C04B41/0072
Inventor 朱海玉
Owner 朱海玉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap