Urea-formaldehyde resin adhesive for artificial boards and preparation method thereof

A urea-formaldehyde resin and preparation process technology, applied in the direction of adhesives, aldehyde/ketone condensation polymer adhesives, adhesive types, etc. Problems such as the content of hydrophilic groups in the resin, to achieve better performance, improve heat resistance and water resistance, and reduce the effect of hydrophilic groups

Inactive Publication Date: 2018-03-02
柳州市林道科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using the above-mentioned component ratio, the degree of polycondensation of methylol melamine and methylol urea under acidic conditions in the preparation process is low, and the content of hydrophilic groups in the resin cannot be reduced to the greatest extent. The prepared urea-formaldehyde resin adhesive Heat resistance and water resistance are weak

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Urea-formaldehyde resin adhesive for artificial boards and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A preparation process of urea-formaldehyde resin waterproof and boiling-resistant adhesive for wood-based panels, comprising the following steps:

[0019] (1) Weigh the following components respectively: formaldehyde: 1450kg, urea: 1145kg, melamine 131-400kg, high-efficiency waterproofing agent: 35kg, PVA: 3.5kg, sodium hydroxide: 29-30kg and formic acid: 4.5kg, And the weighed urea is divided into four parts to be fed: the first part of urea is 700kg, the second part of urea is 175kg, the third part of urea is 150kg, the fourth part of urea is 120kg, and the formic acid is adjusted into 20% formic acid aqueous solution.

[0020] (2) Add formaldehyde and the first portion of urea to the reaction kettle, open the steam valve to raise the temperature to 40-70°C, add 40-100kg of melamine, then add 3-6kg of sodium hydroxide to adjust the pH value to 7.5-9.0, add After PVA heats up to 85-95°C, close the steam valve and keep warm for 30-70 minutes. In the early stage, urea a...

Embodiment 2

[0030] Weigh each component by weight as follows:

[0031] Formaldehyde: 1351kg, urea: 900kg, melamine 131-400kg, high-efficiency waterproofing agent: 10kg, PVA: 3kg, sodium hydroxide: 29-30kg and formic acid: 4kg, and divide the weighed urea into four parts, the first part of urea For 600kg, the second part of urea 100kg, the third part of urea 100kg, the fourth part of urea 100kg; all the other steps can make the wood-based panel urea-formaldehyde resin adhesive of the present invention equally according to the same process of embodiment one.

Embodiment 3

[0033] Weigh each component by weight as follows:

[0034] Formaldehyde: 1650kg, urea: 1500kg, melamine 131-400kg, high-efficiency waterproofing agent: 60kg, PVA: 4kg, sodium hydroxide: 29-30kg and formic acid 5kg, and the urea weighed is divided into four parts, of which the first urea is 900kg, the second part of urea 250kg, the third part of urea 200kg, the fourth part of urea 150kg; all the other steps can make the wood-based panel urea-formaldehyde resin adhesive of the present invention equally according to the same process of embodiment one.

[0035] Through the ratio of the above components (formaldehyde: 1351-1650kg, urea: 900-1500kg, melamine 131-400kg, high-efficiency waterproofing agent: 10-60kg, PVA: 3-4kg, sodium hydroxide: 29-30kg and formic acid 4 -5kg), the quality indicators of the wood-based panel urea-formaldehyde resin waterproof and boiling-resistant adhesive prepared by the adhesive are as follows:

[0036] Water solubility: 0.61

[0037] Curing time (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Curing timeaaaaaaaaaa
Viscosityaaaaaaaaaa
Curing timeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a urea-formaldehyde resin adhesive for artificial boards and a preparation method thereof. The urea-formaldehyde resin adhesive is prepared from, by weight, 1351-1650 kg of formaldehyde, 900-1500 kg of urea, 131-400 kg of melamine, 10-60 kg of a high-effective water-proofing agent, 3-4 kg of PVA, 29-30 parts of NaOH and 4-5 kg of formic acid. In the formula, the condensation polymerization synthesis degree between hydroxymethyl melamine and hydroxymethyl urea is high under an acidic condition during preparation, so that quantity of hydrophilic groups in the resin is greatly reduced, and heat resistance and water resistance of the hydrophilic group are improved. The urea-formaldehyde resin adhesive has further reinforced non-melting and non-dissolving three-dimensional structure, so that the adhesive is better in performances.

Description

technical field [0001] The invention relates to the production field of adhesives, in particular to a urea-formaldehyde resin adhesive for wood-based panels and a preparation process thereof. Background technique [0002] Formaldehyde, urea, melamine, high-efficiency compounding agent, sodium hydroxide and formic acid are used to prepare urea-formaldehyde resin adhesive for wood-based panels. The ratio of each component is different, which directly affects the acidic conditions of methylol melamine and methylol urea in the preparation process. The degree of polycondensation synthesis under the lower degree, and the degree of polycondensation synthesis determines the content of hydrophilic groups in the resin, the less the hydrophilic groups, the infusible and insoluble body structure of the prepared urea-formaldehyde resin adhesive will be enhanced, and the heat resistance and water resistance will be improved. the better. [0003] The Chinese invention patent with the pate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J161/30C08G12/38
CPCC09J161/30C08G12/38
Inventor 李同双覃显斌张克
Owner 柳州市林道科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com