Novel green fluorescent powder with Tb<3> doped tungstate

A technology of green fluorescent powder and tungstate, applied in the direction of luminescent materials, chemical instruments and methods, etc.

Inactive Publication Date: 2018-02-13
UNIV OF JINAN
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous update of photoluminescent materials and the development of LED technology, the traditional LED light source can no longer meet the growing needs of people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel green fluorescent powder with Tb&lt;3&gt; doped tungstate
  • Novel green fluorescent powder with Tb&lt;3&gt; doped tungstate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] (1) The rare earth oxide (Gd 2 o 3 and Tb 4 o 7 ) dissolved in hot nitric acid to prepare 0.5mol / L rare earth nitrate solution, measure 0.2mol rare earth nitrate solution (0.18mol of gadolinium nitrate and 0.02mol of terbium nitrate) into 50ml of deionized water, stir to mix Uniform;

[0017] (2) Weigh 0.3mol Na according to RE:W=2:3 2 WO 4 2H 2 O white particles were dissolved in 20ml deionized water, stirred to make the mixture evenly;

[0018] (3) Drop the uniformly stirred solution in step (1) into the solution obtained in step (2) with a pear-shaped separating funnel, and continue stirring for 30 minutes after the titration to obtain a mixed solution;

[0019] (4) Add sodium hydroxide solution dropwise to the mixed liquid in step (3) to adjust to Ph=7, then move it into the reaction kettle, put it in an electric oven at 120°C for hydrothermal reaction for 24 hours, and wait for the reaction kettle to cool down to room temperature. Take out the reaction kett...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses novel green fluorescent powder with Tb<3> doped tungstate. The novel green fluorescent powder is chemically composed of (Gd0.9Tb 0.1) 2 (WO4) 3. The synthesis method of the fluorescent powder includes that lanthanide nitrate and a sodium tungstate solution are mixed according to chemometry to serve as parent salt solution which is moved to a reaction kettle after complete mixing, the parent salt solution is then put in an air dry oven for reaction for a certain time under high temperature and high pressure, and white precipitates are obtained; white precursor powder isobtained via centrifuging, cleaning and drying on the basis of the white precipitates, and finally, the novel green fluorescent powder with Gd2 (WO4) 3: Tb<3+> is obtained via calcination. The prepared fluorescent powder is good in green emission, energy transfer effect exists among Gd<3+>->Tb<3+>, light intensity of Tb<3+> can be enhanced remarkably, and the novel green fluorescent powder is expected to be a lighting display material of the new generation.

Description

technical field [0001] The invention belongs to the field of rare earth luminescent materials, in particular to a Tb 3+ A new type of green phosphor doped with tungstate. Background technique [0002] With the continuous update of photoluminescent materials and the development of LED technology, the traditional LED light source can no longer meet the growing needs of people. [0003] Tungstate is a typical self-activating material, which can emit high-efficiency fluorescence under the excitation of ultraviolet (UV), X-ray and other light sources, and Gd 3+ It can be used as a host material and a good sensitizer; therefore, it is of great significance to explore the dual sensitization effect of host materials on activator ions on the basis of traditional phosphors. Contents of the invention [0004] The present invention aims to propose a Tb 3+ A new type of green phosphor doped with tungstate. [0005] A kind of Tb proposed by the present invention 3+ Nanoscale gadoli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K11/78
CPCC09K11/7776
Inventor 王文志李金凯刘宗明
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com