High-performance fluorosilicone modified finish-coat paint

A technology of fluorosilicon modification and finishing paint, which is applied in the direction of biocide-containing paint, antifouling/underwater paint, coating, etc. Whitening and other problems, to achieve good dispersion, strong adhesion, improve the effect of adhesion

Inactive Publication Date: 2017-12-26
苏州振振好新型建材科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing fluorosilicone finish paint, there are still not enough performances such as weather resistance, color retention, water resistance, and stain resistance additives; after painting, the coating film is prone to cracking, whitening, discoloration and other pathological phenomena

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance fluorosilicone modified finish-coat paint
  • High-performance fluorosilicone modified finish-coat paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A high-performance fluorosilicon-modified finish paint, the preparation method of the fluorosilicon-modified acrylate is the preparation of isooctyl methacrylate, acrylic acid, tetrafluoropropyl methacrylate, polyoxyethylene octylphenol ether OP -10. Mix sodium dodecylbenzenesulfonate and deionized water evenly, add dicumyl peroxide, heat up to 80°C, keep warm for 8 minutes, then add disodium ethoxylated alcohol sulfosuccinate and acrylamide formaldehyde Sodium propane sulfonate was mixed evenly, cooled to 30°C, then added ammonia water to adjust the pH of the system to 7, filtered and cooled to room temperature to obtain material A; add material A and γ-(methacryloyloxy)propyltrimethoxysilane Add N,N dimethylethanolamine to deionized water to adjust the pH of the system to 8, raise the temperature to 60°C, stir for 40 minutes, and discharge to obtain fluorosilicon-modified acrylate.

[0032] The epoxy silane modified silica sol includes the following components by weig...

Embodiment 2

[0040]A high-performance fluorosilicon-modified finish paint, the preparation method of the fluorosilicon-modified acrylate is the preparation of isooctyl methacrylate, acrylic acid, tetrafluoropropyl methacrylate, polyoxyethylene octylphenol ether OP -10. Mix sodium dodecylbenzenesulfonate and deionized water evenly, add dicumyl peroxide, heat up to 90°C, keep warm for 12 minutes, then add disodium ethoxylated alcohol sulfosuccinate and acrylamide formaldehyde Sodium propane sulfonate was mixed evenly, cooled to 40°C, then added ammonia water to adjust the pH of the system to 8, filtered and cooled to room temperature to obtain material A; add material A and γ-(methacryloyloxy)propyltrimethoxysilane Add N,N dimethylethanolamine to deionized water to adjust the pH of the system to 10, raise the temperature to 70°C, stir for 80 minutes, and discharge to obtain fluorosilicon-modified acrylate.

[0041] The epoxy silane modified silica sol includes the following components by wei...

Embodiment 3

[0049] A high-performance fluorosilicon-modified finish paint, the preparation method of the fluorosilicon-modified acrylate is the preparation of isooctyl methacrylate, acrylic acid, tetrafluoropropyl methacrylate, polyoxyethylene octylphenol ether OP -10. Mix sodium dodecylbenzenesulfonate and deionized water evenly, add dicumyl peroxide, heat up to 85°C, keep warm for 10 minutes, then add disodium ethoxylated alcohol sulfosuccinate and acrylamide formaldehyde Sodium propane sulfonate was mixed evenly, cooled to 35°C, then added ammonia water to adjust the pH of the system to 7.5, filtered and cooled to room temperature to obtain material A; add material A and γ-(methacryloyloxy)propyltrimethoxysilane Add N,N dimethylethanolamine to deionized water to adjust the pH of the system to 9, raise the temperature to 65°C, stir for 60 minutes, and discharge to obtain fluorosilicon-modified acrylate.

[0050] The epoxy silane modified silica sol includes the following components by w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-performance fluorosilicone modified finish-coat paint. Fluorosilicone modified acrylate is taken as a main raw material, the film-forming property is excellent, the adhesive force is high and the hydrophobic property is excellent; the epoxy silane modified silica sol is adopted for improving the surface property of the film coating, the dispersity is excellent and the surface performance of the film is uniform; the graphene oxide is added, so that the adhesive force, flexibility, shock resistance, water tolerance, salt resistance and hardness of the finish-coat paint can be greatly promoted; an anti-microbial mildew preventive is selected from a Chinese herbal medicine extracting solution, is safe, environment-friendly and nontoxic and has excellent sterilizing property; a stain-resistant additive is beneficial to the promotion of stain resistance of the finish-coat paint; the finish-coat paint provided by the invention has the advantages of adhesive force reaching up to level 2, static contact angle of 110-120 degrees between a film and water, high flexibility, excellent shock resistance, high hydrophobicity, water resistance, salt resistance, stain resistance, no volatile organic compound, safety, environmental protection, anti-microbial and mold-proof effects and long service life.

Description

technical field [0001] The invention relates to the technical field of a fluorine-silicon modified finish paint, in particular to a high-performance fluorine-silicon modified finish paint. Background technique [0002] Building exterior wall coatings can beautify the environment and the living room, but due to the poor weather resistance and stain resistance additives of traditional coatings, the coating will change color and stain after a short period of time. As urban environmental pollution is intensifying, dust pollution and gas pollution are particularly serious. [0003] Real stone paint, textured paint and water-based colorful paint are now popular and widely used, but each has its own defects. Real stone paint has poor stain resistance, textured paint and water-based colorful paint have poor water and weather resistance. In order to solve this problem, construction A finish coat is required at the end. [0004] Fluorosilicone finishes are mainly used to protect the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/14C09D5/16C09D7/12
CPCC09D4/06C09D5/14C09D5/1687
Inventor 沈远振邢洪瑞龚雪良
Owner 苏州振振好新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com