Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ceramic product capable of activating tea polyphenol and preparation method of ceramic product

A technology of ceramic products and tea polyphenols, which is applied in the field of ceramic products, can solve the problems of inability to transfer biological energy, achieve the effects of enhancing immunity, reducing injuries, and meeting market demand

Inactive Publication Date: 2017-12-05
GUANGDONG KANGSHITAI NEW MATERIAL TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, ceramic products cannot meet the needs of transmitting bioenergy to people for a long time, improving their overall health, and activating tea polyphenols. Ceramic products that can activate tea polyphenols are vacant in the ceramic industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A method for preparing the ceramic product capable of activating tea polyphenols, comprising the following steps:

[0013] A. Raw material equipment; calculated in parts by weight, the components of ceramic products include: 30 parts of Dongxing sand, 33 parts of pure white sand, 10 parts of Fuming sand, 5 parts of super white ball soil, 7 parts of Huidong Yuanni, 7 parts of quartz powder 5 parts of calcined talc, 4 parts of bentonite, 8 parts of pumice, 15 parts of pumice, 8 parts of magnetite, 8 parts of cold water stone, 8 parts of basalt, and 8 parts of ocher are mixed and equipped to obtain mixture A1; B, ball mill ; Add the mixture A1 and water (2:1 by weight) into the ball mill for mixing and grinding to form slurry B1; C, spray granulation; spray the slurry B1 in a spray drying tower to dry it , granulating to form powder C1; D, stamping and forming; adding the powder C1 to the punching machine for distribution and stamping forming to obtain the ceramic tile bod...

Embodiment 2

[0015] A method for preparing the ceramic product capable of activating tea polyphenols, comprising the following steps:

[0016] A. Raw materials: 38 parts of Dongxing sand, 45 parts of pure white sand, 15 parts of Fuming sand, 10 parts of super white ball clay, 10 parts of Huidong Yuanni, 10 parts of quartz powder, 10 parts of calcined talc, 8 parts of bentonite, pumice 12 parts, 25 parts of stamens, 10 parts of magnetite, 12 parts of cold water stone, 12 parts of basalt, and 12 parts of ochre are mixed and equipped to obtain mixture A1; B, ball milling; the mixture A1 and water (by weight ratio 2: 1) Put it into a ball mill for mixing and grinding to form slurry B1; C, spray granulation; spray the slurry B1 in a spray drying tower to dry it, granulate it, and form powder C1; D, stamping Forming: adding the powder C1 into a punching machine for distribution and stamping forming to obtain a ceramic tile body D1; E. Calcining: putting the ceramic tile body D1 into a kiln for c...

Embodiment 3

[0018] A method for preparing the ceramic product capable of activating tea polyphenols, comprising the following steps:

[0019] A. Raw materials: 35 parts of Dongxing sand, 35 parts of pure white sand, 12 parts of Fuming sand, 8 parts of super white ball soil, 9 parts of Huidong Yuanni, 8 parts of quartz powder, 8 parts of burnt talc, 5 parts of bentonite, pumice 10 parts, 20 parts of stamens, 9 parts of magnetite, 10 parts of cold water stone, 10 parts of basalt, and 10 parts of ochre are mixed and equipped to obtain mixture A1; B, ball milling; the mixture A1 and water (by weight ratio 2: 1) Put it into a ball mill for mixing and grinding to form slurry B1; C, spray granulation; spray the slurry B1 in a spray drying tower to dry it, granulate it, and form powder C1; D, stamping Forming: adding the powder C1 into a punching machine for distribution and stamping forming to obtain a ceramic tile body D1; E. Calcining: putting the ceramic tile body D1 into a kiln for calcinati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a ceramic product capable of activating tea polyphenol and a preparation method of the ceramic product. The ceramic product comprises the following components in parts by weight: 30-38 parts of Dongxing sand, 33-45 parts of pure white sand, 10-15 parts of Fuming sand, 7-10 parts of Huidong raw mud, 7-10 parts of quartz powder, 5-10 parts of calcined talc, 8-12 parts of pumice, 15-25 parts of ophicalcite, 8-10 parts of magnetite, 8-12 parts of gypsum rubrum, 8-12 parts of basalt and 8-12 parts of ruddle. The ceramic product provided by the invention has a function of activating tea polyphenol, and has a wide market prospect.

Description

technical field [0001] The invention relates to the technical field of ceramic products, in particular to a ceramic product capable of activating tea polyphenols and a preparation method thereof. Background technique [0002] At present, ceramic products cannot meet the needs of delivering bioenergy to people for a long time, improving their overall health, and activating tea polyphenols. Ceramic products that can activate tea polyphenols are vacant in the ceramic industry. Contents of the invention [0003] The object of the present invention is to address the deficiencies in the prior art and propose a ceramic product capable of activating tea polyphenols and a preparation method thereof, the ceramic product having the function of activating tea polyphenols. [0004] For reaching this purpose, the present invention adopts following technical scheme: [0005] A ceramic product capable of activating tea polyphenols. Calculated in parts by weight, the components of the cer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/00C04B35/622C04B33/13C04B33/24C04B33/16
CPCC04B35/00C04B33/131C04B33/16C04B33/24C04B35/622C04B2235/3272C04B2235/3418C04B2235/3427C04B2235/3445C04B2235/442C04B2235/448C04B2235/96
Inventor 程燕文周永富
Owner GUANGDONG KANGSHITAI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com