Single-layer fireproof tempered glass preparation method

A tempered glass, single-layer technology, applied in the direction of glass manufacturing equipment, glass tempering, manufacturing tools, etc., can solve the problems of high installation cost, easy to appear bubbles, poor weather resistance, etc., to achieve improved impact resistance, easy installation, high The effect of weather resistance

Inactive Publication Date: 2017-12-01
DONGGUAN TAISHENG GLASS CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition to the bubbles that are prone to appear during the production process, the perfusion fireproof glass will quickly turn milky white under the action of ultraviolet rays and flames, and lose the permeability of the glass.
This also determines the complex production process of composite fireproof glass; the weight is heavier, the installation cost is higher; the disadvantages of poor weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-layer fireproof tempered glass preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing single-layer fireproof tempered glass, comprising the following steps:

[0024] (1) Pretreatment: Prepare a mixed acid solution with a concentration of 18% nitric acid and a concentration of 10% hydrofluoric acid, wherein the volume ratio of nitric acid and hydrofluoric acid is 1:0.7; use the mixed acid solution to treat the glass surface Acid treatment, then wash and dry the acid-treated glass, preheat to 420°C, and keep it warm for 20 minutes;

[0025] (2) Send the pre-treated glass into a tempering furnace for tempering treatment, the tempering treatment temperature is 650°C, and the tempering treatment time is 1h;

[0026] (3) While tempering and heating the glass, spray the cesium potassium salt solution of a specific composition twice, and perform the second spraying 10 minutes after the first spraying, and the spraying amount of the cesium potassium salt solution is 3g / cm 2 , spray thickness is 3mm; cesium potassium salt solution is compos...

Embodiment 2

[0029] A method for preparing single-layer fireproof tempered glass, comprising the following steps:

[0030] (1) Pretreatment: Prepare a mixed acid solution with a concentration of 18% nitric acid and a concentration of 10% hydrofluoric acid, wherein the volume ratio of nitric acid and hydrofluoric acid is 1:1.4; use the mixed acid solution to treat the glass surface Acid treatment, then wash and dry the acid-treated glass, preheat to 460°C, and keep it warm for 30 minutes;

[0031] (2) Send the pre-treated glass into a tempering furnace for tempering treatment, the tempering treatment temperature is 730°C, and the tempering treatment time is 2h;

[0032] (3) While tempering and heating the glass, spray the cesium potassium salt solution of a specific composition twice, and perform the second spraying 15 minutes after the first spraying, and the spraying amount of the cesium potassium salt solution is 5g / cm 2 , spray thickness is 5mm; cesium potassium salt solution is compos...

Embodiment 3

[0035] A method for preparing single-layer fireproof tempered glass, comprising the following steps:

[0036] (1) Pretreatment: Prepare a mixed acid solution with a concentration of 18% nitric acid and a concentration of 10% hydrofluoric acid, wherein the volume ratio of nitric acid and hydrofluoric acid is 1:1; use the mixed acid solution to treat the glass surface Acid treatment, then wash and dry the acid-treated glass, preheat to 440°C, and keep it warm for 25 minutes;

[0037] (2) Send the pre-treated glass into a tempering furnace for tempering treatment, the tempering treatment temperature is 690°C, and the tempering treatment time is 1.5h;

[0038] (3) While tempering and heating the glass, spray the cesium potassium salt solution of a specific composition twice, and perform the second spraying 13 minutes after the first spraying, and the spraying amount of the cesium potassium salt solution is 4g / cm 2 , the spray thickness is 4mm; the cesium potassium salt solution i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a single-layer fireproof tempered glass preparation method, and relates to the technical field of building materials. The preparation method comprises the following steps: (1) performing acid treatment on the surface of glass by using a mixed acid solution of nitric acid and hydrofluoric acid, then washing the acid treated glass, and performing drying and preheating; (2) sending the pre-processed glass in the step (1) into a glass tempering furnace to perform glass tempering, wherein the glass tempering temperature is in a range of 650-730 DEG C and the glass tempering time is in a range of 1-2 hours; (3) when the glass is tempered with heating, spraying a cesium-potassium salt solution with a certain composition twice, wherein a second spraying is performed 10-15 min after a first spraying is finished; and (4) taking out the tempered glass and performing air cooling molding, and finally performing cooling to obtain the single-layer fireproof tempered glass. The single-layer fireproof tempered glass provided by the invention is simple in preparation process, convenient in installation, high in impact resistance and high in weatherability.

Description

field of invention [0001] The invention belongs to the technical field of building materials, and in particular relates to a preparation method of single-layer fireproof tempered glass. Background technique [0002] Fire-resistant glass is a special glass that has been processed and treated by a special process and can maintain its integrity and heat insulation in the specified fire-resistant test. The main role in fire prevention is to control the spread of fire or to isolate smoke. It is a measure-type fireproof material. Fireproof glass has the properties of light transmission, fire prevention (smoke, fire, and heat radiation), sound insulation, and impact resistance. It is suitable for architectural decoration of steel and wood fire doors, windows, upper lights, partition walls, lighting roofs, and smoke-blocking vertical walls. , see-through floors and other building components that require both transparency and fire protection. The original glass of fireproof glass c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B27/03
CPCC03B27/03
Inventor 李锦亮
Owner DONGGUAN TAISHENG GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com