White foam glass

A foam glass, white technology, applied in glass molding, glass manufacturing equipment, manufacturing tools and other directions, can solve problems such as unsightly cost, and achieve the effects of low raw material price, simple production process and low sintering temperature

Inactive Publication Date: 2017-11-24
HEBEI ZHUODA BUILDING MATERIALS RES INST CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aiming at the problems of unsightly appearance and high cost, the present invention proposes a white foam glass plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • White foam glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A white foam glass comprising an essential component and at least one decolorizing component: the essential component comprising: 74 mol % SiO 2 ; 5 mol% CaO; 18 mol% Al 2 o 3 ; 1 mol% SnCl 2 ; the at least one decolorizing component comprises: 2 mol % NiO.

[0020] Described white cellular glass obtains as follows:

[0021] 1) Preparation of premix: 100 parts of aluminosilicate glass powder with particle size above 500 mesh, 10 parts of calcium carbonate, opacifying agent SnCl 2 2 parts, 2 parts of decolorizing agent NiO are mixed, adding an appropriate amount of water, the ball-to-material ratio is 50:1, the rotation speed is 100-300rpm, and the ball mill is 30min, and the stated parts are parts by weight;

[0022] 2) Put the mixture into a foaming furnace and sinter according to the following process: from room temperature to 400°C at a heating rate of 10°C / min, keep warm for 60 minutes for preheating, raise to 800°C at 15°C / min, and hold for 30 minutes After 1...

Embodiment 2

[0025] A white foam glass comprising an essential component and at least one decolorizing component: the essential component comprising: 70 mol % SiO 2 ; 6 mol% CaO; 20 mol% Al 2 o 3 ; 2 mol% SnCl 2 ; the at least one decolorizing component comprises: 1 mol % NiO, 1 mol % Se.

[0026] Described white cellular glass obtains as follows:

[0027] 1) Preparation of premix: 100 parts of aluminosilicate glass powder with a particle size of 500 mesh or more, 8 parts of calcium carbonate, opacifying agent SnCl 2 4 parts, 2 parts of decolorizing agent (NiO and Se) are mixed, adding an appropriate amount of water, the ball-to-material ratio is 70:1, the rotation speed is 100-300rpm, and the ball mill is 30min. The parts are parts by weight;

[0028] 2) Put the mixture into a foaming furnace and sinter according to the following process: from room temperature to 400°C at a heating rate of 15°C / min, keep warm for 60 minutes for preheating, raise to 950°C at 20°C / min, and hold for 30 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to white foam glass. The glass comprises essential components and at least one decoloring component, wherein the essential components comprise about 70-76 mol% of SiO2, about 5-9 mol% of CaO, 18 mol% to about 22 mol% of Al2O3, and about 1-2 mol% of SnCl2, and the at least one decoloring component comprises (a) NiO which is greater than 0 mol% to about 5 mol%, and / or (b) Se which is greater than 0 mol% to about 4 mol%. The white foam glass has the characteristics of being high-whiteness in appearance, low in building cost, long in service life, good in effects of heat insulation and sound insulation, light in bulk unit weight and the like, and the density is 165 kg / m<3> or below.

Description

technical field [0001] The invention relates to a new type of building material, especially a kind of white foam glass. Background technique [0002] New building materials and wall insulation systems put forward higher requirements, requiring not only good thermal insulation performance, but also outstanding compression, tensile, and aging resistance; not only reliable protection performance, but also fundamentally To block fire hazards, it must also have the characteristics of waterproof, impermeable, and permanent service life; it must be green and environmentally friendly, and it must be non-toxic and harmless; it must avoid the problems of traditional external wall insulation systems that have complicated procedures, cannot be monitored, and have no guarantee of quality. But also the process is simple, convenient for construction, and the quality is guaranteed. Existing foam insulation boards on the market are foam insulation boards made of organic polymer materials su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C11/00C03C3/087C03C4/02C03C6/02C03C1/04C03C1/00C03B19/08C03B19/06
CPCC03B19/06C03B19/08C03C1/00C03C1/04C03C3/087C03C4/02C03C11/007
Inventor 杨卓舒纪勇纪轩
Owner HEBEI ZHUODA BUILDING MATERIALS RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap