Anticorrosive foam plastic composite material and production method thereof

A foamed plastic and composite material technology, applied in the field of composite plastics, can solve the problems of easy pollution, poor softness of composite materials, easy corrosion, etc., and achieve the effect of avoiding air pollution

Inactive Publication Date: 2017-11-07
卢路平
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the problems of poor softness, easy deformation, non-environmental protection, easy corrosion, and easy pollution of composite materials in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anticorrosive foam plastic composite material and production method thereof
  • Anticorrosive foam plastic composite material and production method thereof
  • Anticorrosive foam plastic composite material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3 and comparative example 1-4

[0031] According to the formulas of Examples 1-3 and Comparative Examples 1-2 listed in Table 1 below ("parts" in the table refer to weight fractions, the same below) polyether polyols and polyisocyanates are placed in a vacuum oven at 50°C Vacuum dry for 12 hours, remove moisture, put the wheat straw granules into a drying oven and dry at 80°C, when the moisture content of the wheat straw granules is 7% using a moisture content tester, stop drying, take out the wheat straw granules and put them in the oven. put into a pulverizer, pulverize to a particle size of 50 meshes, and obtain wheat straw powder; after incinerating the wheat straw into ashes, obtain wheat straw ash powder;

[0032] Pour the polyether polyol, montmorillonite, wheat straw powder and wheat straw ashes into a blender, and stir evenly, then add water, vibrate in an ultrasonic wave at 55°C for 2 hours, and obtain the first mixture;

[0033] Put the first mixture into a mixer, then add a catalyst and a foam st...

Embodiment 4-6

[0042] According to the formula of Examples 4-6 listed in the table below ("parts" in the table refer to weight fractions, the same below), put polyether polyol and polyisocyanate into a 60°C vacuum drying oven for 12h to remove moisture, The wheat straw granules are put into a drying oven and dried under the condition of 90° C., and when the moisture content of the wheat straw granules is measured by a moisture content tester to be 10%, the drying is stopped, and the wheat straw granules are taken out and put into a pulverizer, and pulverized to The particle size is 60 mesh, and the wheat straw powder is obtained, and the wheat straw ash powder is obtained after the wheat straw is incinerated into ashes;

[0043]Pour the polyether polyol, montmorillonite, wheat straw powder and wheat straw ashes into a blender, and stir evenly, then add water, vibrate in an ultrasonic wave at 60°C for 2.5 hours, and obtain the first mixture;

[0044] Put the first mixture into a mixer, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to an anticorrosive foam plastic composite material, which is formed by compounding a plurality of core-like structures, wherein the core part of the core-like structure is a nanometer metal, the middle part wrapping the core part is a foam plastic composite material, and the shell part wrapping the middle part is poly o-phenylenediamine. The invention further relates to a preparation method of the anticorrosive foam plastic composite material. According to the present invention, the nanometer metal is protected by the poly o-phenylenediamine, and the foam plastic composite material is used as the middle layer, such that the formed structure has advantages of compactness, firmness and light weight, the nanometer metal is effectively subjected to double protection with the poly o-phenylenediamine and the foam plastic composite material, and advantages of no pollution, strong firmness and corrosion resistance are provided.

Description

technical field [0001] The invention belongs to the technical field of composite plastics, and relates to an anti-corrosion foamed plastic composite material and a manufacturing method thereof. Background technique [0002] In recent years, with the development of navigation and river transportation, the requirements for the use of ships are higher. It is necessary to prevent the hull from being corroded by chemical substances in the water, such as salts, and to prevent the materials used from polluting the water. It is also necessary to consider whether the outer body of the hull is easy to age and damage, and the existing hull is generally easy to corrode. After one or two years of use, some rust spots will appear, and the hull is heavy and consumes a lot of energy. question. Not only that, due to the deteriorating electromagnetic wave environment in the ocean, in order to conduct electronic simulation and other tests, it is urgent to build a non-echo anechoic chamber tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L97/02C08L79/02C08L83/04C08K3/04C08K3/08C08K3/34C08J9/12B01J13/14
CPCC08L75/08B01J13/14C08J9/125C08J2203/10C08J2375/08C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2203/14C08L2205/035C08L2207/53C08L97/02C08L79/02C08L83/04C08K3/04C08K3/08C08K3/346
Inventor 卢路平
Owner 卢路平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com