Highly-transparent fiber glass-surface paper and its preparation method

A glass surface paper and fiber technology, which is applied in the direction of non-fiber pulp addition, fiber raw material treatment, paper, etc., can solve the problems of reducing light transmission performance, rough surface, poor flatness, etc., and achieves wide application range, simple preparation method, The effect of improving light transmission and surface smoothness

Inactive Publication Date: 2017-10-20
CHINA TOBACCO YUNNAN IND
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The sulfuric acid paper prepared by this method is solid, dense and translucent, but its surface is very rough and has poor flatness, and the smoothness is generally less than 90 seconds
When sulfuric acid paper is used for packaging printing, there are defects such as poor color reproduction, inability to adapt to fine dot printing, and insufficient barcode recognition clarity, which greatly limits its application in the printing field; at the same time, due to the loose fiber structure on the surface of sulfuric acid paper , also greatly reduces its light transmission performance, and cannot make its packaging products have the transparency they should

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly-transparent fiber glass-surface paper and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high light-transmitting fiberglass surface paper, comprising sulfuric acid paper, coated with primer, secondary coating and protective layer in sequence on both sides of the sulfuric acid paper, the primer layer is made of carbon dioxide copolymer polyol 80 parts, 18 parts of diisocyanate, 22 parts of chain-extending cross-linking agent and 14 parts of hydrophilic chain-extending agent; 7 parts, 16 parts of ethyl acetate, 0.3 parts of white mineral oil and 10 parts of dyes; the protective layer is made of 27 parts of hydroxyethyl cellulose ether, 2 parts of sodium lauryl sulfate, 4 parts of polyacrylamide and Prepared from 6 parts of triethanolamine.

[0022] A preparation method of high light-transmitting fiber glass surface paper, comprising the following steps:

[0023] 1) Select surface density as 160g / m 2 , a sulfuric acid paper with a thickness of 0.04mm is used as the base layer, and is set aside;

[0024] 2) Put 80 parts of carbon dioxide copolymer polyol, ...

Embodiment 2

[0032] A high light-transmitting fiberglass surface paper, comprising sulfuric acid paper, coated with primer, secondary coating and protective layer in sequence on both sides of the sulfuric acid paper, the primer layer is made of carbon dioxide copolymer polyol 80 parts, 18 parts of diisocyanate, 22 parts of chain-extending cross-linking agent and 14 parts of hydrophilic chain-extending agent; 7 parts, 16 parts of ethyl acetate, 0.3 parts of white mineral oil and 10 parts of dyes; the protective layer is made of 27 parts of hydroxyethyl cellulose ether, 2 parts of sodium lauryl sulfate, 4 parts of polyacrylamide and Prepared from 6 parts of triethanolamine.

[0033] A preparation method of high light-transmitting fiber glass surface paper, comprising the following steps:

[0034] 1) Select surface density as 160g / m 2 , a sulfuric acid paper with a thickness of 0.04mm is used as the base layer, and is set aside;

[0035] 2) Put 80 parts of carbon dioxide copolymer polyol, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high light-transmitting fiber glass surface paper, which comprises sulfuric acid paper, and the two sides of the sulfuric acid paper are coated with an undercoat layer, a secondary coat layer and a protective layer in sequence, and the undercoat layer is copolymerized by carbon dioxide 80 parts of polyols, 18 parts of diisocyanates, 22 parts of chain-extending cross-linking agents and 14 parts of hydrophilic chain-extending agents; 7 parts of sustained-release microcapsules, 16 parts of ethyl acetate, 0.3 parts of white mineral oil and 10 parts of dye; the protective layer is made of 27 parts of hydroxyethyl cellulose ether, 2 parts of sodium lauryl sulfate, polypropylene Made from 4 parts of amide and 6 parts of triethanolamine; this kind of high-transmittance fiber glass paper can significantly improve the light transmission and surface smoothness of the fiber, and the surface smoothness of the paper after double-sided treatment is greater than 210 seconds, and at the same time The preparation method of the process is simple and the application range is wide.

Description

technical field [0001] The invention belongs to the technical field of packaging materials, and in particular relates to a high light transmission fiber glass paper with strong light transmission and high surface smoothness and a preparation method thereof. Background technique [0002] At present, sulfuric acid paper (also known as tracing paper) is the only paper with light-transmitting properties on the market, which is mainly used in tracing, transfer printing and limited printing. Sulfuric acid paper is made of fine plant fibers interwoven with each other. After free beating, no sizing, no filler, and papermaking process in a wet state, it is soaked in concentrated sulfuric acid with a concentration of 72% for 2 to 3 seconds. Film-type paper formed after washing, glycerin treatment, and drying. The sulfuric acid paper prepared by this method is solid, dense and translucent, but its surface is very rough and has poor flatness, and the smoothness is generally less than 9...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/10D21H19/84D21H19/82D21H19/14D21H19/24D21H21/14D21H21/54D21H21/28D21H19/34D21H19/20D21H19/16
CPCD21H27/10D21H19/14D21H19/16D21H19/20D21H19/24D21H19/34D21H19/82D21H19/84D21H21/14D21H21/28D21H21/54
Inventor 余振华余耀张莹詹建波李赓谢姣郑晗余婷婷
Owner CHINA TOBACCO YUNNAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap