Antibacterial sock

A technology for socks and antibacterial masterbatch, applied in the field of textile products, can solve the problems of unsuitability for ordinary people, poor wear resistance, high cost of socks, and achieve excellent effectiveness and long-term effect, excellent wear resistance, and health care. Good results

Inactive Publication Date: 2017-08-08
晋大纳米科技(厦门)有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although some antibacterial socks have begun to appear at present, the comfort of the current antibacterial socks is poor, the cost of socks is high, and they are not suitable for ordinary people.
[0003] In addition, socks with antibacterial effect are easy to break when used, and have poor wear resistance. Antibacterial socks with a slightly longer service life are less skin-friendly, and the material is hard, which is not favored by consumers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial sock

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The concentration is 5% nano-silver solution, joins in diatomite, the ratio of the mass of solute in diatomite and nano-silver is 9:1 (mass ratio), dry after slowly absorbing, the primary product that obtains is carried out Granulate, control the granulation temperature to 62°C, and make antibacterial fiber masterbatch with a particle size of 1-20 μm. The obtained antibacterial masterbatch is blended with cotton fiber, polyester fiber and seaweed fiber, wherein the mass ratio of antibacterial masterbatch, cotton fiber and polyester fiber is 1:2:5, and seaweed fiber accounts for 2% of the total weight to obtain antibacterial socks 1.

Embodiment 2

[0024] The concentration is 8% nano-silver solution, joins in diatomite, the ratio of the mass of solute in diatomite and nano-silver is 19:1 (mass ratio), dry after slowly absorbing, the primary product that obtains is carried out Granulate, control the granulation temperature to 84°C, and make antibacterial fiber masterbatch with a particle size of 1-20 μm. The obtained antibacterial masterbatch is blended with cotton fiber, polyester fiber and seaweed fiber, wherein the mass ratio of antibacterial masterbatch, cotton fiber and polyester fiber is 1:5:8, and seaweed fiber accounts for 5% of the total weight to obtain antibacterial socks 2.

Embodiment 3

[0026] The concentration is 4% nano-silver solution, joins in diatomite, the ratio of the mass of solute in diatomite and nano-silver is 15:1 (mass ratio), dry after slowly absorbing, the primary product that obtains is carried out Granulation, control the granulation temperature to 73°C to make antibacterial fiber masterbatch with a particle size of 1-20 μm. The obtained antibacterial masterbatch is blended with cotton fiber, polyester fiber and seaweed fiber, wherein the mass ratio of antibacterial masterbatch, cotton fiber and polyester fiber is 1:3:6, and seaweed fiber accounts for 3.5% of the total weight to obtain antibacterial socks 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial sock and a preparation method thereof. The antibacterial sock comprises an antibacterial master batch and fibers, wherein the antibacterial master batch is composed of diatomite and nano-silver according to a mass ratio of 9:1 to 19:1. The antibacterial sock is prepared by the following steps: attaching silver ions to diatomite so as to prepare the antibacterial master batch; blending the antibacterial master batch and the fibers so as to obtain fiber yarns; spooling, warping and weaving the fiber yarns, forming a grey fabric, and performing after-treatment, so as to obtain the antibacterial sock. The process is simple, reliable and convenient to implement. The prepared antibacterial sock is wear-resistant, breathable and excellent in health effect, has antibacterial and deodorant effects and further has excellent antibacterial effectiveness and a long-term effect.

Description

technical field [0001] The invention relates to the field of textile products, in particular to antibacterial socks and a preparation method thereof. Background technique [0002] There are many socks with health care functions on the market, mainly to improve the color and material of socks, so that socks are more attractive in appearance, but there are relatively few studies on socks with antibacterial and deodorizing functions. Although some antibacterial socks have begun to appear at present, the comfort of the current antibacterial socks is poor, and the cost of socks is high, so they are not suitable for ordinary people. [0003] In addition, socks with antibacterial effects are easy to break when used, and have poor wear resistance. Antibacterial socks with a slightly longer service life are less skin-friendly and hard materials are not favored by consumers. Contents of the invention [0004] The problem to be solved by the present invention is to overcome the defi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41B11/00A41B17/00D06M23/02D06M101/06D06M101/32D06M101/04
CPCA41B11/00A41B17/00A41B2400/34D06M16/00D06M23/02D06M2101/04D06M2101/06D06M2101/32
Inventor 吴永鑫
Owner 晋大纳米科技(厦门)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com