Adhesive and production process thereof
A technology of adhesives and rubber softeners, applied in the direction of adhesives, natural rubber adhesives, adhesive types, etc., can solve the problems of limited lifting capacity, weak bonding, and high price of accessories, and achieve outstanding load-bearing capacity and sticky The glue is firm and reliable, and the effect of easy removal
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0044] (1) Cut 5 parts of natural smoked sheet rubber and 3 parts of styrene-butadiene rubber into small pieces in a rubber cutter, plasticize and knead them into thin slices through a rubber mixer, and coat them in a solvent kettle.
[0045] (2) Apply 10 parts of SIS rubber and 7 parts of SBS rubber in turn, and add solvent, and stir at a speed of 100-120r / min for 4-6 hours;
[0046] (3) After the rubber elastomer is softened and dissolved, add 30 parts of terpene phenolic resin, 0.5 part of zinc dibutyl carbamate, 0.5 part of 2,6-di-tert-butyl p-cresol, 3 parts of white oil and 0.1 part of 2 , 4-dihydroxybenzophenone, mixed with rubber elastomer at a speed of 60-100r / min for 3-5 hours, after being completely dissolved and mixed evenly, filter it into a rubber bucket with a 60-mesh filter for use.
Embodiment 2
[0048] (1) 12 parts of natural smoked sheet rubber and 3 parts of styrene-butadiene rubber are cut into small pieces in a rubber cutting machine, plasticized and kneaded by a rubber mixer to make thin slices, and coated in a solvent kettle,
[0049] (2) Apply 16 parts of SIS rubber and 8 parts of SBS rubber in sequence, and add solvent, and stir at a speed of 100-120r / min for 4-6 hours;
[0050] (3) After the rubber elastomer is softened and dissolved, add 33 parts of C5 petroleum resin, 1.2 parts of zinc dibutyl carbamate, 1 part of 2,6-di-tert-butyl p-cresol, 2.3 parts of liquid nitrile rubber and 0.65 parts 2-(2ˊ-hydroxy-5ˊ-methylphenyl)benzotriazole, mixed with rubber elastomer at a speed of 60-100r / min for 3-5 hours, after completely dissolved and mixed evenly, filter with 60 mesh Net filter into the glue barrel for use.
Embodiment 3
[0052] (1) 30 parts of natural smoked sheet rubber and 8 parts of styrene-butadiene rubber are cut into small pieces in a rubber cutting machine, plasticized and kneaded by a rubber mixer to make thin slices, and coated in a solvent kettle,
[0053] (2) Apply 30 parts of SIS rubber and 12 parts of SBS rubber in turn, and add solvent, and stir at a speed of 100-120r / min for 4-6 hours;
[0054] (3) After the rubber elastomer is softened and dissolved, add 50 parts of synthetic C5 / C9 petroleum resin, 3 parts of zinc dibutyl carbamate, 1.5 parts of 2,6-di-tert-butyl p-cresol, 3.5 parts of liquid polyisobutylene and 1 part of (1,2,2,6,6-pentamethylpiperidinyl) phosphite, mixed with the rubber elastomer at a speed of 60-100r / min for 3-5 hours, after being completely dissolved and mixed evenly, use Filter through a 60-mesh filter into a plastic bucket for use.
PUM
Property | Measurement | Unit |
---|---|---|
Tensile strength | aaaaa | aaaaa |
Release force | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com