High-brightness finishing printing silica gel for silk screen printing and preparation method of high-brightness finishing printing silica gel

A technology of screen printing and glossy covering, applied in textiles, papermaking, fiber processing, etc., can solve the problems of impatience to rapid drying, long defoaming time, poor gloss effect of covering glue, etc., and achieve outstanding glossy effect. Fast defoaming effect

Active Publication Date: 2017-06-23
东莞市科多有机硅材料有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, due to the large amount of white carbon black in the general-purpose bright cover glue on the market, the cover glue has poor gloss effect during use, long defoaming time, is not resistant to rapid baking, pitting and air bubbles after baking, etc. unpleasant sight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1. This example provides a high-gloss cover printing silica gel for screen printing. Calculated by mass, its constituent materials include 10-15 parts of high-gloss cover printing silica A component and 1-3 parts High-gloss cover printing silicone B component;

[0033] The high-gloss cover printing silica gel A component is composed of the following raw materials: 100-120 parts of 20000cs side chain vinyl silicone oil, 10-15 parts of 500cs terminal vinyl silicone oil, 10-15 parts of MQ resin and 0.7-1.0 parts of 5000ppm platinum catalyst ;

[0034] The high-gloss cover printing silica gel B component consists of the following raw materials: 2-3 parts of hydrogen-containing silicone oil with a hydrogen content of 0.55, 6-8 parts of hydrogen-containing silicone oil with a hydrogen content of 0.75, and 1-2 parts of 1000cs terminal ethylene Base silicone oil and 0.03-0.05 parts of ethynyl cyclohexanol.

[0035] The 20000cs side chain vinyl silicone oil is composed of the...

Embodiment 2

[0045] Example 2. The technical solution of this example 2 is basically the same as that of example 1. The difference is that, calculated in parts by mass, its constituent materials include 10 parts of high-gloss cover printing silica gel A component and 1 part of high-gloss silicone Cover printing silicone B component;

[0046] The high-gloss cover printing silica gel A component is composed of the following raw materials: 100 parts of 20000cs side chain vinyl silicone oil, 10 parts of 500cs terminal vinyl silicone oil, 10 parts of MQ resin and 0.7 parts of 5000ppm platinum catalyst;

[0047] The high-gloss cover printing silica gel B component consists of the following raw materials: 2 parts hydrogen-containing silicone oil with a hydrogen content of 0.55, 6 parts hydrogen-containing silicone oil with a hydrogen content of 0.75, 1 part 1000cs vinyl silicone oil and 0.03 parts acetylene Cyclohexanol.

[0048] The 20000cs side chain vinyl silicone oil is composed of the following ra...

Embodiment 3

[0049] Example 3. The technical solution of this example 3 is basically the same as that of example 1. The difference is that in terms of parts by mass, its constituent materials include 15 parts of high-gloss cover printing silicone A component and 3 parts of high-gloss silicone Cover printing silicone B component;

[0050] The high-gloss cover printing silica gel A component is composed of the following raw materials: 120 parts of 20000cs side chain vinyl silicone oil, 15 parts of 500cs terminal vinyl silicone oil, 15 parts of MQ resin and 1.0 part of 5000ppm platinum catalyst;

[0051] The high-gloss cover printing silica gel B component is composed of the following raw materials: 3 parts hydrogen-containing silicone oil with a hydrogen content of 0.55, 8 parts hydrogen-containing silicone oil with a hydrogen content of 0.75, 2 parts 1000cs vinyl silicone oil and 0.05 parts acetylene Cyclohexanol.

[0052] The 20000cs side chain vinyl silicone oil is composed of the following raw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-brightness finishing printing silica gel for silk screen printing. The high-brightness finishing printing silica gel is prepared from the following raw materials in parts by mass: 10 to 15 parts of a high-brightness finishing printing silica gel component A and 1 to 3 parts of a high-brightness finishing printing silica gel component B. The invention further discloses a preparation method of the high-brightness finishing printing silica gel for the silk screen printing. According to the high-brightness finishing printing silica gel and the preparation method thereof, the defects of the general bright finishing gel are overcome; the high-brightness finishing gel with an outstanding brightness effect, high debubbling effect, urgent baking resistance, and zero hard spots and bubbles on a baked product is prepared; the finishing gel can be used for large-pattern printing finishing, to meet the requirement for the flowability, and also used for small-pattern finishing, to meet the requirement for avoiding smudging of a fillet.

Description

Technical field [0001] The invention relates to the field of silica gel screen printing, in particular to a high-gloss overlay printing silica gel for screen printing and a preparation method of the high-gloss overlay printing silica gel for screen printing. Background technique [0002] Screen printing silica gel is different from ink or glue with single material and single effect printing. It can be divided into bright round corner effect, bright right angle effect, matte round corner effect, matte right angle effect and flat right angle effect according to different surface effects. Among them, the bright rounded corner effect is loved by consumers because of its strong three-dimensional effect on the surface and a raindrop-like arc shape. [0003] However, the common gloss cover glue on the market contains a large amount of white carbon black, resulting in poor gloss effect, long defoaming time, intolerance to rapid baking, pitting and bubbles after baking, etc. unpleasant sig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643C08G77/20
CPCC08G77/20D06M15/643
Inventor 陶玉红陈志刚高庆胜
Owner 东莞市科多有机硅材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap