Thermosetting mold release coating agent, a mold releasing film, and a mold release polyethylene terephthalate film

A technology of thermal curing and coating agent, which can be used in coatings, polyester coatings, polyether coatings, etc., and can solve the problems of film curling and large damage to polyester film.

Active Publication Date: 2017-06-20
ARAKAWA CHEM IND LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the case of using melamine resin, a high temperature of 150°C or higher is required to form a coating film, so the polyester film as the base material is greatly damaged.
In addition, when melamine resin forms a coating film or stores the film for a long time, there is a problem of film curling due to curing shrinkage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting mold release coating agent, a mold releasing film, and a mold release polyethylene terephthalate film
  • Thermosetting mold release coating agent, a mold releasing film, and a mold release polyethylene terephthalate film
  • Thermosetting mold release coating agent, a mold releasing film, and a mold release polyethylene terephthalate film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] 50 parts of Cymel 303LF (full ether type methylated melamine resin: manufactured by Ornex Japan Co., Ltd.), 50 parts of PRIPOL 2033 (number average molecular weight of hydrogenated dimer glycol 540: manufactured by Croda Japan Co., Ltd.), p-toluenesulfonic acid 4 parts were mixed, and methyl ethyl ketone was further added to prepare a coating agent with a solid content of 20%.

Embodiment 2

[0068] Mix 50 parts of Cymel 303LF, 50 parts of Praxel 205 (polyester polyol number average molecular weight 500, manufactured by Daicel Co., Ltd.), 4 parts of p-toluenesulfonic acid, and further add methyl ethyl ketone to prepare a coating with a solid content of 20%. Cloth agent.

Embodiment 3

[0070] 50 parts of Cymel 303LF, 50 parts of Clare Polyol C-1090 (polycarbonate polyol with a number average molecular weight of 1000, manufactured by Kurare Co., Ltd.) and 4 parts of p-toluenesulfonic acid were mixed, and methyl ethyl ketone was further added to prepare the solid content of 20% coating agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a heat-curable release coating composition which can form a cured film excellent in releasability and residual adhesion at a relatively low temperature while the film is formed by film formation. The thermosetting release coating agent contains a methylated melamine resin (A), a polyol (B) having a molecular weight of 100 to 3000, and an acid catalyst (C).

Description

technical field [0001] The invention mainly relates to a heat-curing release coating agent, a release film coated with the coating composition, and a polyethylene terephthalate release film. Background technique [0002] Biaxially stretched polyester films represented by polyethylene terephthalate films are widely used in various industrial fields because of their excellent properties such as transparency, dimensional stability, mechanical properties, and chemical resistance. In recent years, it has been widely used in various optical films, such as base films of prism sheets, light diffusion sheets, reflectors, touch screens, etc. of LCD components or anti-reflection base films or explosion-proof base films of display screens, PDP filter films, etc. Various uses. In addition, it is also used in large quantities as a release film, as an adhesive sheet, tape, touch screen protective film, and ceramic capacitor, and is also widely used in electronic material applications. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18C08L61/32C08L71/00C08L67/00C08L69/00C09D161/32C09D171/00C09D167/00C09D169/00
CPCC09D161/32C09D167/00C09D169/00C09D171/00C08J5/18C08L61/32C08L67/00C08L69/00C08L71/00C08L2203/16C09D161/28C08J7/04C08L61/28C09D7/20C09D7/63C09D7/65C08L83/00B32B27/36B32B27/42C08J2367/02C08J2461/28B32B2307/748
Inventor 伊藤良树金子光耶子东本徹
Owner ARAKAWA CHEM IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com