Water-based highly-filled glaze for carpentry, preparation method of water-based highly-filled glaze and construction process

A water-based, wood-based technology, applied in the direction of coating, etc., can solve the problems of poor color retention, slow drying of Grace, poor adhesion, etc., achieve good thickening, reduce construction steps, and improve water resistance Effect

Inactive Publication Date: 2017-05-31
AODA KOALA PAINT HUIZHOU
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Some Graces on the market have slow drying, poor color fixation and color retention, and cannot be well combined with water-based primers or water-based topcoats, that is, poor adhesion, easy to delaminate, and easy to appear cross-color hair in subsequent coatings. flowers etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of water-based high-filling glass for woodware, which is composed of the following components in mass percentage: 7.7% water, 1% bentonite, 15% water-based co-solvent, 20% water-based resin, 0.3% water-based defoamer, wetting and dispersing agent 0.5%, powder 50%, pH regulator 0.2%, antiseptic bactericide 0.1%, antifungal agent 0.2%, water-based color paste toner 5%.

[0031] The preparation steps of the above-mentioned woodware water-based high-filling Grace:

[0032] A. Add water, defoamer, wetting and dispersing agent, water-based co-solvent, bentonite, and pH regulator into the dispersion tank in turn at 1200-1500 rpm, and stir for 5-10 minutes until uniform;

[0033] B. In step A, add water-based resin, powder, and water-based color paste toner in sequence, and stir and disperse for 10-15 minutes at 1800-2500 rpm until uniform;

[0034] C. Add antiseptic and fungicide in step B, antifungal agent 1200-1500 rpm, stir and disperse for 5 minutes until uniform....

Embodiment 2

[0036] A water-based high-filling glass for woodware, consisting of the following components in mass percentage: 10% water, 0.8% bentonite, 12.9% water-based co-solvent, 25% water-based resin, 0.3% water-based defoamer, wetting and dispersing agent 0.5%, powder 45%, pH adjuster 0.2%, antiseptic bactericide 0.1%, antifungal agent 0.2%, water-based color paste toner 5%.

[0037] The preparation steps of the above-mentioned woodware water-based high-filling Grace:

[0038] A. Add water, defoamer, wetting and dispersing agent, water-based co-solvent, bentonite, and pH regulator into the dispersion tank in turn at 1200-1500 rpm, and stir for 5-10 minutes until uniform;

[0039] B. In step A, add water-based resin, powder, and water-based color paste toner in sequence, and stir and disperse for 10-15 minutes at 1800-2500 rpm until uniform;

[0040] C. Add antiseptic and fungicide in step B, antifungal agent 1200-1500 rpm, stir and disperse for 5 minutes until uniform.

Embodiment 3

[0042] A water-based high-filling glass for woodware, consisting of the following components in mass percentage: 7.5% water, 1.2% bentonite, 10% water-based co-solvent, 15% water-based resin, 0.3% water-based defoamer, wetting and dispersing agent 0.5%, powder 60%, pH adjuster 0.2%, antiseptic bactericide 0.1%, antifungal agent 0.2%, water-based color paste toner 5%.

[0043] The preparation steps of the above-mentioned woodware water-based high-filling Grace:

[0044] A. Add water, defoamer, wetting and dispersing agent, water-based co-solvent, bentonite, and pH regulator into the dispersion tank in turn at 1200-1500 rpm, and stir for 5-10 minutes until uniform;

[0045] B. In step A, add water-based resin, powder, and water-based color paste toner in sequence, and stir and disperse for 10-15 minutes at 1800-2500 rpm until uniform;

[0046] C. Add antiseptic and fungicide in step B, antifungal agent 1200-1500 rpm, stir and disperse for 5 minutes until uniform.

[0047] Wra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of coatings, and relates to water-based highly-filled glaze for carpentry, a preparation method of the water-based highly-filled glaze and a construction process. The water-based highly-filled glaze for the carpentry comprises, in weight percentage, 15%-25% of water-base resin, 0.5%-2% of bentonite, 40%-60% of powder materials, 1%-10% of water, 1%-10% of water-based color paste color powder and 10.6%-22.5% of other functional additives. The glaze has good filling functions without affecting coloring and is good in anti-settling effect, various water-based primers can effectively adhere, and delaminating is avoided.

Description

technical field [0001] The invention belongs to the field of coatings, and relates to a water-based high-filling glass for woodware, a preparation method and a construction process thereof. Background technique [0002] Grace is a translucent to transparent pigment colorant, which is composed of resin dissolved in oily solvent. It dries slowly and can be wiped, brushed and layered to make the overall color soft, natural and layered. Most of them are used in NC paint. Grace can fill the color into the tube holes of the wood, and can adjust the light and dark shades of the color by wiping, increasing the layering of the coating color and the clarity of the wood grain. It is an indispensable coloring product for American painting. [0003] Some Graces on the market have slow drying, poor color fixation and color retention, and cannot be well combined with water-based primers or water-based topcoats, that is, poor adhesion, easy to delaminate, and easy to appear cross-color hai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D7/12
CPCC08K2201/014C08L2205/02C08L2205/035C09D125/14C09D7/61C09D7/62C09D7/65C08L83/04C08L3/02C08K13/06C08K3/346C08K3/34C08K3/36
Inventor 陈日云佘其渠
Owner AODA KOALA PAINT HUIZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com