Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Graphene 3D printing material and preparation method thereof

A 3D printing and graphene technology, applied in the field of 3D printing materials, can solve the problems of inconsistent phases of 3D printing products, affecting product uniformity and stability, and products are prone to cracks, etc., achieving excellent performance stability, easy control, and improved molding The effect of processability

Active Publication Date: 2019-01-11
深圳市明鑫高分子技术有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a graphene 3D printing material and a preparation method thereof, aiming at solving the problem that graphene and polyethylene terephthalate are prone to phase separation when used as a 3D printing material, resulting in a 3D printing product internal The phase state is inconsistent, which affects the uniformity and stability of the product, resulting in the problem that the obtained product is prone to cracks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene 3D printing material and preparation method thereof
  • Graphene 3D printing material and preparation method thereof
  • Graphene 3D printing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] In order to make the technical problems, technical solutions and beneficial effects to be solved by the present invention clearer, the present invention will be further described in detail below with reference to the embodiments. It should be understood that the specific embodiments described herein are only used to explain the present invention, but not to limit the present invention.

[0027] An embodiment of the present invention provides a graphene 3D printing material, comprising the following components in the following parts by weight:

[0028]

[0029] Described modified graphene is made of graphene oxide, ammoniacal liquor, polyethylene glycol diglycidyl ether, wherein, the mass ratio of described graphene oxide and described polyethylene glycol diglycidyl ether is 100:1- 5.

[0030] Specifically, in the embodiment of the present invention, the modified graphene, as the matrix material of the graphene 3D printing material, has excellent mechanical propertie...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a graphene 3D printing material. The graphene 3D printing material is prepared from, by weight, 20-60 parts of modified graphene, 30-50 parts of polyethylene glycol terephthalate, 2-8 parts of nano polytetrafluoroethylene, 1-5 parts of nano silica and 0.1-3 parts of an antioxidant, wherein the modified graphene is prepared from graphene oxide, ammonia water and polyethylene glycol diglycidyl ether, and the mass ratio of graphene oxide to polyethylene glycol diglycidyl ether is 100:(1-5).

Description

technical field [0001] The invention belongs to the technical field of 3D printing materials, and in particular relates to a graphene 3D printing material and a preparation method thereof. Background technique [0002] 3D printing (3DP) is a type of rapid prototyping technology, which is a technology that constructs objects by layer-by-layer printing based on digital model files and using adhesive materials such as powdered metal or plastic. Since 3D printing technology does not require molds, it can directly generate physical finished products according to the 3D CAD graphics designed by the computer, and obtain products with high precision and complexity. Therefore, 3D printing technology has become a rapidly developing emerging technology. [0003] Polyethylene terephthalate is the most important variety of thermoplastic polyester, commonly known as polyester resin. It has good physical and mechanical properties, long-term use temperature can reach 120 ° C, excellent el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L27/18C08K9/04C08K3/04C08K3/36B33Y70/00
CPCB33Y70/00C08L67/02C08L27/18C08K9/08C08K3/04C08K3/36
Inventor 惠先洋徐雪清许年芳
Owner 深圳市明鑫高分子技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com