Repair agent for travertine geology, repair liquid and application of repair liquid

A technology of repairing agent and repairing liquid, which is applied in marine engineering, construction, water conservancy engineering, etc., can solve the problem of difficult to guarantee the color, density and permeability coefficient of travertine, the original characteristics of travertine, and ecological Poor tolerance and other problems, to achieve the effect of promoting repair, high repair efficiency, and increased compatibility

Active Publication Date: 2017-05-31
SOUTHWEAT UNIV OF SCI & TECH
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The repair agent used for the maintenance or repair of travertine rock dams needs to focus on the maintenance of the original geological characteristics of travertine, but the maintenance or repair materials of conventional water conservancy project bank slopes such as reinforced concrete and travertine geological ecology Poor capacity, it is difficult to ensure that the color, density and permeability coefficient of travertine are consistent with the materials used for edge rock dam repair, resulting in the destruction of the original characteristics of travertine
For example, Chinese patent CN103526720 discloses a reinforced concrete prefabricated pile spur dam construction method, using reinforced concrete sheet piles as the spur dam foundation to replace the rockfill spur dam, which can maintain stability under the action of tidal surge and flood erosion, and can better withstand surge The impact of the tide, but the steel bars introduced to improve the stability of the reinforcement material will cause permanent damage to the original geomorphology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] By weight, the repair agent includes 75 parts of travertine powder, 5 parts of lime, and 5 parts of gypsum, wherein the particle size of travertine powder is 500 μm, the particle size of lime is 700 μm, and the particle size of gypsum is 500 μm. Stir each component with a power of 30kw for 20 minutes to obtain a repairing agent for travertine geology.

[0040] According to the mass ratio of repairing agent to water of 85:15, the repairing agent and water were mixed, pressed at a pressure of 10 MPa for 20 minutes, and then ventilated and dried for 3 days at 25°C to obtain brickwork. The compressive strength measured during the indoor test is 5MPa.

[0041] Take the travertine geological base block, cut it into a size of 4cm×4cm×16cm, cut the prepared brickwork to the same size, and compare the strength, the compressive strength of the travertine block is lower than 3MPa, and the compressive strength of the bricklaying is 5MPa.

[0042] The prepared brickwork was comple...

Embodiment 2

[0044] By weight, the repair agent includes 87 parts of travertine powder, 30 parts of lime, and 5 parts of gypsum, wherein the particle size of travertine powder is 500 μm, the particle size of lime is 700 μm, and the particle size of gypsum is 500 μm. Stir each component with a power of 30kw for 20 minutes to obtain a repairing agent for travertine geology.

[0045] According to the mass ratio of repairing agent to water of 85:15, the repairing agent and water were mixed, pressed at a pressure of 10 MPa for 20 minutes, and then ventilated and dried for 3 days at 25°C to obtain brickwork. The compressive strength measured during the indoor test is 9MPa.

[0046] Take the travertine geological base block, cut it into a size of 4cm×4cm×16cm, cut the prepared brickwork to the same size, and compare the strength, the compressive strength of the travertine block is lower than 3MPa, and the compressive strength of the bricklaying is 9MPa.

[0047] The prepared brickwork was compl...

Embodiment 3

[0049] By weight, the repair agent includes 75 parts of travertine powder, 5 parts of lime, and 5 parts of gypsum, wherein the particle size of travertine powder is 500 μm, the particle size of lime is 700 μm, and the particle size of gypsum is 500 μm. Stir each component with a power of 30kw for 20 minutes to obtain a repairing agent for travertine geology.

[0050] According to the mass ratio of repairing agent to water 85:15, the repairing agent and water were mixed and pressed at a pressure of 15 MPa for 20 minutes, and then ventilated and dried for 3 days at 25°C to obtain brickwork. The compressive strength measured during the indoor test is 13MPa.

[0051] Take the travertine geological base block, cut it into a size of 4cm×4cm×16cm, cut the prepared brickwork to the same size, and compare the strength, the compressive strength of the travertine block is lower than 3MPa, and the compressive strength of the bricklaying It is 13MPa.

[0052] The prepared brickwork was c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a repair agent for travertine geology. The repair agent is prepared from the following components in parts by weight: 65-87 parts of a travertine base material, 5-30 parts of lime and 1-5 parts of gypsum. According to the repair agent, the adopted travertine base material is good in compatibility with a repaired geological environment, so that in-situ repair of the travertine geology without damage and pollution is realized, and the repair efficiency and the strength after repairing are high. The repair agent can be used for repairing collapsed regions and large gaps of a stone dam at the edge of a ground surface colored pool in a travertine scenic spot, can also be used for repairing the travertine geology and is strong in pertinence. Shown by results of the embodiment of the invention, the provided repair agent for the travertine geology can realize in-situ repair of the travertine geology; and in the using process of the repair agent for the travertine geology, the compressive strength can reach 18 MPa.

Description

technical field [0001] The invention relates to the technical field of geological restoration, in particular to a repairing agent for travertine geology, a repairing liquid and the application of the repairing liquid. Background technique [0002] Travertine is a bicarbonate-rich surface water that, under suitable physical, chemical or biological conditions, is close to and / or exposed to the surface of the earth, forming a carbonate travertine deposit due to the escape of carbon dioxide in large quantities. These sediments change with the movement of the water flow and the change of the water circulation system, forming travertine landscapes, such as travertine side stone dam colored pools, travertine beach flows, travertine waterfalls and travertine collapse caves. As a special type of karst landform, while being continuously formed, it also faces the phenomenon of evolution and degradation of the landscape under the influence of normal erosion, among which the collapse or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B22/14E02B3/16
CPCC04B22/143C04B28/10C04B2201/50E02B3/16C04B14/28C04B22/002
Inventor 代群威党政董发勤李琼芳王岩
Owner SOUTHWEAT UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com