A kind of supercritical CO Vinyl sulfone type reactive disperse dye and its preparation method and application

A reactive disperse dye, vinyl sulfone type technology, applied in the direction of reactive dyes, dyeing methods, organic dyes, etc., can solve problems such as difficult application of supercritical dyeing, achieve good industrialization prospects, good dyeing effect, and improve solubility

Active Publication Date: 2018-10-23
SHENYANG RES INST OF CHEM IND +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The dye still has good dispersibility at high temperature and is suitable for high-temperature dyeing in conventional water phase. It has good dyeing effect on chemical fibers such as polyester, but it is insoluble in supercritical carbon dioxide, so it is difficult to apply in supercritical dyeing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of supercritical CO Vinyl sulfone type reactive disperse dye and its preparation method and application
  • A kind of supercritical CO Vinyl sulfone type reactive disperse dye and its preparation method and application
  • A kind of supercritical CO Vinyl sulfone type reactive disperse dye and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Compound 1:

[0044]

[0045] (1) Weigh 2-methoxy-4-acetamidoaniline (18.1g, 0.1mol), add 300ml DMF, stir to dissolve, add Na 2 CO 3 (21.2g, 0.2mol), tetra-n-butylammonium bromide (3.22g, 0.001mol), the temperature was raised to 90°C, and allyl bromide (36.3g, 0.3mol) was slowly added dropwise, kept for 2h, and the reaction was detected by TLC After the reaction is complete, add 300ml of water, extract with dichloromethane (30ml×3), wash with water, dry the organic phase, and rotary evaporate to obtain 22.76g of brown-black solid with a yield of 87.54%.

[0046] (2) Weigh p-vinylsulfone aniline (10.98g, 0.06mol), add 40g of water, add 36% HCl (18.25g, 0.18mol), heat up to 50°C, stir and dissolve into a brown-black solution, cool to 0 - 5°C, weigh NaNO 2 (4.14g, 0.06mol) was made into a 30% solution, slowly added dropwise to the reaction solution, and reacted for 30min to obtain a yellow and clear diazonium solution.

[0047] (3) Weigh the product (16.38g, 0.063mol)...

Embodiment 2-6

[0049] Examples 2-6 were prepared according to the method of Example 1, as shown in Table 1.

[0050] Table 1

[0051]

Embodiment 7

[0053] Compound 7:

[0054]

[0055] (1) Weigh 2-ethoxy-4-propionamidoaniline (20.8g, 0.1mol), add 400ml DMF, stir to dissolve, add Na 2 CO 3 (30.9g, 0.3mol), add benzyltriethylammonium chloride (2.27g 0.01mol), heat up to 65°C, slowly add allyl bromide (48.4g, 0.4mol), keep warm for 2h, and detect with TLC The reaction proceeded, and after the reaction was complete, 300ml of water was added, extracted with acetone (30ml×3), washed with water, the organic phase was dried, and rotary evaporated to obtain 25.83g of a brown-black solid with a yield of 89.71%.

[0056] (2) Weigh 2,6-dibromo-4-vinylsulfonylaniline (10.83g, 0.03mol), dissolve it in 40g concentrated sulfuric acid, stir and dissolve into a dark red solution, slowly add 37% nitrosylsulfuric acid solution dropwise (9.52g, 0.03mol), and kept stirring for 30min to obtain a dark brown diazonium solution.

[0057] (3) Weigh the product (8.64g, 0.03mol) in step (1), add 30mlCH 3 COOH, add 30gCH 3 Add 300 g of ice wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of dye synthesis, and relates to a vinyl-sulfone type reactive disperse dye for supercritical CO2 and a preparation method thereof. The structure of the compound is shown in the formula (I) specified in the description, wherein each functional group in the formula is defined in the description. The compound has the good dyeing activity, can be used for supercritical CO2 dyeing, and has the good dyeing performance on both wool fiber and polyester fiber.

Description

technical field [0001] The invention belongs to the technical field of fine chemical dyes, specifically a supercritical CO 2 Vinylsulfone-type reactive disperse dyes and their preparation methods and applications. Background technique [0002] As a green dyeing method, supercritical carbon dioxide dyeing uses supercritical carbon dioxide instead of water medium, and selects appropriate dyes to disperse and dye in supercritical carbon dioxide. Compared with traditional water bath dyeing, it reduces the use of auxiliary agents and eliminates wastewater pollution. , shorten the dyeing procedure, and has good industrialization prospects. [0003] At present, the industry has developed some reactive disperse dyes for supercritical carbon dioxide dyeing. These reactive disperse dyes mainly use disperse dyes as the matrix to access active groups. The active groups include: cyanuric fluoride, cyanuric chloride, bromoacrylamide, vinyl sulfone etc. However, triazine active groups a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09B62/51D06P3/52D06P3/66D06P1/384C07C315/04C07C317/34
CPCC07C315/04C07C317/34C09B62/51D06P1/384D06P3/528D06P3/666Y02P20/54
Inventor 李学敏王瑛张晓超白雪松徐飒英
Owner SHENYANG RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com