Medical packaging material and preparation method thereof

A technology for packaging materials and raw materials, applied in the field of medical packaging materials and their preparation, can solve the problems of the packaging materials failing to meet the use requirements, deformation, and related mechanical properties reduction, and achieve high tensile strength, high temperature resistance, The effect of long service life

Inactive Publication Date: 2016-12-21
ANHUI JIAMU RUBBLE & PLASTIC IND
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Conventional medical packaging materials such as polyvinyl chloride and polyethylene will be deformed under long-term sterilization conditions, and the relevant mechanical properties of conventional medical packaging materials will also be reduced after deformation, so that the packaging materials cannot meet the requirements for use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A medical packaging material, which is made of the following raw materials in parts by weight: 16 parts of polycarbonate, 12 parts of polyurethane, 0.8 part of polyacetimide, 0.9 part of polydimethylsiloxane diquaternary amine, 0.6 parts of trichlorofluoromethane, 5 parts of dichlorodifluoromethane, 23 parts of polylactide, 4.8 parts of calcium carbonate, 0.6 parts of sodium dibutylnaphthalene sulfonate, 23 parts of polyethylene glycol, 10 parts of acrylic resin, ethylene- 8 parts of vinyl acetate copolymer, 2.5 parts of borax.

[0020] The preparation method of described medical packaging material, it comprises the following steps:

[0021] (1) Take each raw material component in proportion;

[0022] (2) Open the reactor, adjust the temperature of the reactor to 80-83°C, after the temperature is stable, add the raw material components in the step (1), and stir evenly at high temperature to obtain the film packaging material mixture;

[0023] (3) Carry out high-temper...

Embodiment 2

[0027] A medical packaging material, which is made of the following raw materials in parts by weight: 16 parts of polycarbonate, 12 parts of polyurethane, 0.8 part of polyacetimide, 1 part of polydimethylsiloxane diquaternary amine, 0.7 parts of trichlorofluoromethane, 6 parts of dichlorodifluoromethane, 20 parts of polylactide, 3.5 parts of calcium carbonate, 0.7 parts of sodium dibutylnaphthalene sulfonate, 24 parts of polyethylene glycol, 11 parts of acrylic resin, ethylene- 6 parts of vinyl acetate copolymer, 4 parts of borax.

[0028] The preparation method of described medical packaging material, it comprises the following steps:

[0029] (1) Take each raw material component in proportion;

[0030] (2) Open the reactor, adjust the temperature of the reactor to 80-83°C, after the temperature is stable, add the raw material components in the step (1), and stir evenly at high temperature to obtain the film packaging material mixture;

[0031] (3) Carry out high-temperatur...

Embodiment 3

[0035] A medical packaging material, which is made of the following raw materials in parts by weight: 20 parts of polycarbonate, 14 parts of polyurethane, 1 part of polyacetimide, 1 part of polydimethylsiloxane diquaternary amine, 0.7 parts of trichlorofluoromethane, 9 parts of dichlorodifluoromethane, 18 parts of polylactide, 3 parts of calcium carbonate, 0.8 parts of sodium dibutylnaphthalene sulfonate, 19 parts of polyethylene glycol, 9 parts of acrylic resin, ethylene- 6 parts of vinyl acetate copolymer, 3.5 parts of borax.

[0036] The preparation method of described medical packaging material, it comprises the following steps:

[0037] (1) Take each raw material component in proportion;

[0038] (2) Open the reactor, adjust the temperature of the reactor to 80-83°C, after the temperature is stable, add the raw material components in the step (1), and stir evenly at high temperature to obtain the film packaging material mixture;

[0039] (3) Carry out high-temperature e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a medical packaging material. The medical packaging material is prepared from, by weight, 12-23 parts of polycarbonate, 8-18 parts of polyurethane, 0.5-1.2 parts of polyethylenimine, 0.5-1.2 parts of polydimethylsiloxane diquaternary amine, 0.4-1 part of trichlorofluoromethane, 4-9 parts of dichlorodifluoromethane, 15-28 parts of polylactide, 1.5-6 parts of calcium carbonate, 0.5-1 part of sodium dibutyl naphthalene sulfonate, 15-30 parts of polyethylene glycol, 6-12 parts of acrylic resin, 4-9 parts of vinyl-vinyl acetate copolymer and 2.5-6 parts of borax. Compared with the prior art, the medical packaging material has strong resistance to high temperature and high tensile strength, does not easily deform after high temperature and high pressure sterilization treatment and is especially suitable for the medical field.

Description

technical field [0001] The invention relates to a packaging material, in particular to a medical packaging material and a preparation method thereof. Background technique [0002] Packaging materials are widely used in various fields of our society, such as medical packaging materials and food packaging materials, etc., in order to improve the hygiene status of the medical industry or food industry, it must allow the effective penetration of the selected sterilant, and be suitable for Relevant conditions for other sterilization methods. Conventional medical packaging materials such as polyvinyl chloride and polyethylene will be deformed under long-term sterilization conditions, and the relevant mechanical properties of conventional medical packaging materials will also be reduced after deformation, so that the packaging materials cannot meet the requirements for use . Contents of the invention [0003] The purpose of the present invention is to provide a medical packagin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L69/00C08L75/04C08L71/02C08L33/00C08L23/08C08K13/02C08K5/02C08K3/26C08K5/42C08K3/38
CPCC08L67/04C08L69/00C08L2201/08C08L2205/035C08L75/04C08L71/02C08L33/00C08L23/0853C08K13/02C08K5/02C08K2003/265C08K5/42C08K2003/387
Inventor 叶春会王泽平
Owner ANHUI JIAMU RUBBLE & PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com