A kind of crystal bead embryo of lake water orchid color and preparation method thereof

A crystal bead and color technology, applied in glass pressing, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of uneven color, low production efficiency, poor coloring, etc., and achieve good production efficiency, good gloss, and performance stable effect

Active Publication Date: 2018-06-26
浙江鑫伟兴水晶有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Lake orchid color crystal bead embryos are semi-finished products used to manufacture black crystal products. In the existing technology of lake orchid color crystal bead embryos, crucibles are often used to make them. There are poor coloring properties, uneven colors, patterns, and unstable product quality. Production Low efficiency, not suitable for continuous mass production. In addition, it contains aluminum, and the use of coal is easy to cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of preparation method of the crystal bead embryo of lake water orchid color, comprises the following steps:

[0017] 1) Take 50 parts of fire throwing powder, 60 parts of quartz sand, 75 parts of soda ash, 65 parts of cullet, 2 parts of sodium chloride, 12 parts of sodium nitrate, 5 parts of calcium carbonate, 2 parts of caustic soda, 1.2 parts of sodium chlorate, 5.5 parts of borax decahydrate, 0.95 parts of copper oxide and 0.05 parts of chromium oxide green, mix well;

[0018] 2) Putting it into a granulator for granulation, the particle size is 0.5-2.5cm;

[0019] 3) Put it into the crystal pool by the feeder, keep the liquid level stable during melting, and control the temperature at 1350-1400 °C;

[0020] 4) After 12 hours in the crystal pool, enter the clarification tank for 2 hours, molded after cooling in the feeder, and the temperature is controlled at 800-1000 °C;

[0021] 5) After being polished and shaped by the fire throwing furnace, it enters the...

Embodiment 2

[0024] A kind of preparation method of the crystal bead embryo of lake water orchid color, comprises the following steps:

[0025] 1) Take 150 parts of fire throwing powder, 170 parts of quartz sand, 170 parts of soda ash, 150 parts of broken glass, 10 parts of sodium chloride, 25 parts of sodium nitrate, 15 parts of calcium carbonate, 12 parts of caustic soda, 7 parts of sodium chlorate, 16 parts of borax decahydrate, 4 parts of copper oxide and 3 parts of chromium oxide green, mix well;

[0026] 2) put into granulator and carry out granulation, particle size is 2.5cm;

[0027] 3) Throw it into the crystal pool by the feeder, keep the liquid level stable during melting, and control the temperature at 1400°C;

[0028] 4) After 12 hours in the crystal pool, enter the clarification tank for 2 hours, molded after cooling in the feeding channel, and the temperature is controlled at 1000 °C;

[0029] 5) After being polished and shaped by the fire throwing furnace, it enters the s...

Embodiment 3

[0032] A kind of preparation method of the crystal bead embryo of lake water orchid color, comprises the following steps:

[0033] 1) Take 100 parts of fire throwing powder, 115 parts of quartz sand, 110 parts of soda ash, 95 parts of cullet, 5 parts of sodium chloride, 20 parts of sodium nitrate, 10 parts of calcium carbonate, 7 parts of caustic soda, 4 parts of sodium chlorate, 10 parts of borax decahydrate, 2 parts of copper oxide and 2 parts of chromium oxide green, mix well;

[0034] 2) put into granulator and carry out granulation, particle size is 1.5cm;

[0035] 3) Put it into the crystal pool by the feeder, keep the liquid level stable during melting, and control the temperature at 1375°C;

[0036] 4) After 12 hours in the crystal pool, enter the clarification tank for 2 hours, molded after cooling in the feeding channel, and the temperature is controlled at 900 °C;

[0037] 5) After being polished and shaped by the fire throwing furnace, it enters the stainless ste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a lake blue-color crystal bead blank. The lake blue-color crystal bead blank is prepared from 50-150 parts by weight of fire polishing powder, 60-170 parts by weight of quartz sand, 50-170 parts by weight of sodium carbonate, 60-150 parts by weight of broken glass, 1.3-10 parts by weight of sodium chloride, 10-25 parts by weight of sodium nitrate, 5-15 parts by weight of calcium carbonate, 2-12 parts by weight of caustic soda flake, 1-7 parts by weight of sodium chlorate, 5-16 parts by weight of borax decahydrate, 0.9-4 parts by weight of copper oxide and 0.01-3 parts by weight of chromium oxide green. The lake blue-color crystal bead blank has good stainability, stable quality and high production benefits, is suitable for mass production and does not cause environmental pollution.

Description

technical field [0001] The invention specifically relates to a crystal bead embryo with a lake blue color and a preparation method thereof. Background technique [0002] Lake orchid color crystal bead embryos are semi-finished products used to manufacture black crystal products. In the existing technology of lake orchid color crystal bead embryos, crucibles are often used to make them. There are poor coloring properties, uneven colors, patterns, and unstable product quality. Production The benefit is low, and it is not suitable for continuous mass production. In addition, it contains aluminum, and the use of coal is easy to cause environmental pollution. Contents of the invention [0003] The object of the present invention is to address the shortcomings of the prior art, to provide a crystal bead embryo with a lake orchid color that is good in colorability, stable in quality, high in production efficiency, suitable for mass production, and does not cause environmental pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C6/04C03C4/02C03B11/00
CPCC03B11/00C03C1/002C03C4/02
Inventor 杨鑫法
Owner 浙江鑫伟兴水晶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap