Anti-oxidation flame-retardant sheath material for air-conditioner wire harness and preparation method of anti-oxidation flame-retardant sheath material
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A flame-retardant sheath and anti-oxidation technology, which is applied in the direction of plastic/resin/wax insulators, organic insulators, electrical components, etc., can solve the problems of inconvenience and power supply failure, and achieve outstanding performance
Inactive Publication Date: 2016-09-21
合肥得润电子器件有限公司
View PDF1 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Household wire harness is a part of household appliances, and it is also an important bridge between power supply and power supply. If there is no household wire harness, the power supply will not be able to communicate with each other, which will have a very inconvenient impact
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012] An anti-oxidation and flame-retardant sheath material for air-conditioning wire harnesses, which is made of the following raw materials by weight (kg): polyperfluoroethylene propylene 65, dibromocresyl glycidyl ether 16, vinyl chloride-acrylonitrile copolymer 25, phosphorus aluminum Stone 14, porous powder quartz 12, zinc phosphate 7, aluminum distearate 6, hexaphenoxycyclotriphosphazene 10, brominated polystyrene 18, tin antimony oxide 4, halloysite nanotube 13, antimony slag 12. Chlorinated paraffin 8. Sodium erythroconate 3. Tert-butylphenyl diphenyl phosphate 20.
[0013] A method for preparing an anti-oxidation and flame-retardant sheath material for an air-conditioning wire harness, comprising the following steps:
[0014] (1) Mix the phosphate phosphate and antimony slag evenly, pulverize, sieve, then add 15% hydrochloric acid solution equivalent to 5 times the weight of the powder, heat in a water bath to 65°C, oscillate ultrasonically for 20 minutes, centrifuge...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an anti-oxidation flame-retardant sheath material for an air-conditioner wire harness and a preparation method of the anti-oxidation flame-retardant sheath material. The anti-oxidation flame-retardant sheath material is prepared from the following raw materials in parts by weight: 55-70 parts of poly-perfluorinated ethylene-propylene, 14-18 parts of dibromomethyl-benzene glycidyl ether, 22-27 parts of a vinyl chloride-acrylonitrile copolymer, 12-16 parts of amblygonite, 10-15 parts of porous powder quartz, 5-9 parts of zinc phosphate, 4-8 parts of aluminum distearate, 8-12 parts of hexaphenoxy cyclotriphosphazene, 15-20 parts of brominated polystyrene, 3-6 parts of tin antimony oxide, 11-17 parts of indianite nanotubes, 10-15 parts of antimony ore slag, 6-10 parts of chlorinated paraffin, 2-5 parts of red algae sugar acid sodium and 16-22 parts of phosphoric acid tert-butyl benzene diplenyl ester. The air-conditioner wire harness sheath material prepared from raw materials such as poly-perfluorinated ethylene-propylene, the vinyl chloride-acrylonitrile copolymer, hexaphenoxy cyclotriphosphazene, brominated polystyrene, porous powder quartz, tin antimony oxide and the indianite nanotubes has integrated properties of flame retardancy, oxidation prevention, weather resistance, chemical corrosion resistance and the like, is outstanding in performance, and is applicable to market requirements.
Description
technical field [0001] The invention relates to an anti-oxidation and flame-retardant sheath material for an air-conditioning wire harness and a preparation method thereof, belonging to the field of polymer materials. Background technique [0002] Household wire harness is a part of household appliances, and it is also an important bridge between power supply and power supply. If there is no household wire harness, the power supply will not be able to communicate with each other, which will have a very inconvenient impact. Many household appliances in the family, such as refrigerators, washing machines, televisions, rice cookers, and water dispensers, will have home wiring harnesses. With the invention of electricity, a variety of household appliances also appeared, produced and widely used by people. As a very important part of electrical appliances, the scope of application of household wire harnesses has also been widely used with the generation of electrical appliances. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.