Ultraviolet-resistant flame-retardant optical cable material and preparation method thereof

An anti-ultraviolet and optical cable technology, applied in the field of optical cable materials, can solve the problems of agglomeration of modified particles, affecting the comprehensive performance of polystyrene, etc., to reduce the degradation rate, increase the thermal decomposition temperature and the amount of carbon, and reduce the heat release value. Effect

Inactive Publication Date: 2016-09-21
安徽电信器材贸易工业有限责任公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, a large amount of addition leads to the agglomeration of modified particles in the matrix resin, which will affect the comprehensive performance of polystyrene

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] An anti-ultraviolet flame-retardant optical cable material, which is composed of the following raw materials in parts by weight:

[0023] 2 (2'hydroxyl'tert-octylphenyl) benzotriazole 0.6, polyvinyl chloride 100, polystyrene 20 sodium hypophosphite monohydrate 3, paraformaldehyde 2, 35% hydrochloric acid 0.2, chlorinated spirocyclic phosphoric acid Ester 4, aluminum chloride hexahydrate 5, triethylamine 0.1, graphite powder 10, polyvinyl butyral ester 4, magnesium oxide 0.1, dimethyl chlorophthalate 0.6, calcium palmitate 1, lauryl dimethyl Amine oxide 0.1, ethylene glycol monobutyl ether 0.3, aluminum dihydrogen phosphate 0.6.

[0024] A kind of preparation method of described anti-ultraviolet flame retardant optical cable material, comprises the following steps:

[0025] (1) Take the above-mentioned sodium hypophosphite monohydrate, add it to deionized water 50 times its weight, stir evenly, put it into a constant temperature water bath at 76°C, slowly add the above-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultraviolet-resistant flame-retardant optical cable material which is composed of the following raw materials in parts by weight: 0.6-1 part of 2-(2'-hydroxy-5'-tert-octylphenyl)benzotriazole, 100-130 parts of polyvinyl chloride, 20-27 parts of polystyrene, 3-4 parts of sodium hypophosphite monohydrate, 2-3 parts of polyformaldehyde, 0.2-0.3 part of 37-37% hydrochloric acid, 4-6 parts of chlorospirophosphate, 5-7 parts of aluminum chloride hexahydrate, 0.1-0.2 part of triethylamine, 10-12 parts of graphite powder, 4-6 parts of polyvinyl butyral resin, 0.1-0.3 part of magnesium oxide, 0.6-1 part of dimethyl chlorophthalate, 1-2 parts of calcium palmitate, 0.1-0.2 part of lauryldimethylamine oxide, 0.3-0.5 part of ethylene glycol monobutyl ether and 0.6-2 parts of aluminum dihydrogen phosphate. The ultraviolet-resistant flame-retardant optical cable material can perform the function of lowering the temperature of the combustion zone, and some phospho-oxygen free radicals and the like generated during pyrolysis can capture free radicals generated by polystyrene segment pyrolysis, thereby lowering the heat release value of the material.

Description

technical field [0001] The invention relates to the technical field of optical cable materials, in particular to an anti-ultraviolet and flame-retardant optical cable material and a preparation method thereof. Background technique [0002] In recent years, nanotechnology has attracted widespread attention in the field of flame retardancy. Studies have shown that nanomaterials only need a small amount of addition (generally less than 5%) to achieve a more obvious flame retardancy effect. Therefore, the preparation of flame-retardant nanocomposites is an important component in the field of flame-retardant technology, and is highly regarded by researchers. Layered inorganic nanomaterials are one of the most effective filler materials in flame-retardant nanocomposites. When layered inorganic nanomaterials are dispersed in the polymer matrix at the nanoscale, they can significantly improve the mechanical properties of nanocomposites. , thermal stability and flame retardant prope...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L25/06C08L29/14C08K13/04C08K7/00C08K5/5317C08K5/3475C08K3/04
CPCC08L27/06C08L2201/02C08L2201/08C08L2203/202C08L2205/03
Inventor 王卫东柳冰李光良
Owner 安徽电信器材贸易工业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com