A kind of non-oriented silicon steel for high power factor motor and its production method

A high power factor, oriented silicon steel technology, applied in the field of non-oriented silicon steel for high power factor motors and production, can solve unthinkable problems and achieve excellent magnetic properties

Active Publication Date: 2017-08-25
武汉钢铁有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] Judging from the above literature, there is no understanding that improving the power factor of the motor can improve the efficiency of the motor and the corresponding technical measures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of non-oriented silicon steel for high power factor motor and its production method
  • A kind of non-oriented silicon steel for high power factor motor and its production method
  • A kind of non-oriented silicon steel for high power factor motor and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0061] The present invention is described in detail below:

[0062] Table 1 is the composition value list of each embodiment of the present invention and comparative example;

[0063] Table 2 is the main process parameter list of each embodiment of the present invention and comparative example;

[0064] Table 3 is a list of performance detection and motor performance simulation of each embodiment of the present invention and comparative examples.

[0065] Each embodiment of the present invention carries out according to the following steps:

[0066] 1) Smelting and continuous casting into blanks by using pure steel mode;

[0067] 2) Heating the slab, controlling its heating rate to 6-10°C / min, soaking temperature at 1100-1160°C, soaking time at 30-60min;

[0068] 3) Carry out hot rolling, control the rough rolling temperature at 1000-1050°C; control the finish rolling entrance temperature at 950-1000°C, control the final rolling temperature at 750-850°C, and control the thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

Non-oriented silicon steel for a high-power-factor motor is prepared from, by weight, 0-0.0020% of C, 1.70-1.90% of Si, 0.10-0.20% of Mn, 0-0.05% of P, 0-0.0030% of S, 0.25-0.35% of Al, 0.05-0.50% of Cr and 0-0.0020% of N. A production method includes the steps that pure steel is smelted into ingots; the ingots are heated; hot rolling is conducted; coiling is conducted; normalizing is carried out; acid pickling is conducted; cold rolling is conducted; finished products are annealed at the N2+H2 atmosphere; cooling, coating and finishing are conducted through conventional methods. The thickness of the silicon steel is 0.50 mm, iron loss P1.5 / 50 is smaller than or equal to 3.3 W / kg, and B5000 is larger than or equal to 1.74 T. A motor simulation result shows that the silicon steel can be used for manufacturing the high-power-factor motor, relatively high motor efficiency is obtained, and components are simple.

Description

technical field [0001] The invention relates to a non-oriented silicon steel and a production method thereof, in particular to a non-oriented silicon steel for high power factor motors and a production method thereof. Background technique [0002] In recent years, environmental issues such as global warming and air pollution and energy shortages have attracted worldwide attention. In order to curb the continuous warming of the earth, it is necessary to improve energy efficiency and reduce emissions in terms of CO 2 major greenhouse gases. In my country, motors consume about 60-70% of the total domestic electricity, especially industrial motors consume more than 70% of electricity. Relevant reports show that the current market share of high-efficiency motors in my country only accounts for about 10% of the entire motor market. For this reason, improving the performance and efficiency of motors is a long-term and arduous task, which requires the non-oriented electrical stee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/18C22C38/02C22C38/04C22C38/06C21D8/12
CPCC21D8/1222C21D8/1233C21D8/1272C22C38/02C22C38/04C22C38/06C22C38/18
Inventor 冯大军石文敏杜光梁陈圣林杨光吕黎万政武欧阳页先曹亢
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com